Preparation method of novel titanium-nickel medical implantation material

An implant material, titanium-nickel technology, which is applied in the field of preparation of new titanium-nickel medical implant materials, can solve the problems of affecting surface properties, easy formation of voids on the surface of micro-arc oxidation film, etc., to achieve good wear resistance and thermal shock resistance, reduce Cavity generation, good insulation effect

Inactive Publication Date: 2014-10-08
TAIYUAN UNIV OF TECH
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface of the micro-arc oxidation film is also easy to form voids, which affects its surface properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of novel titanium-nickel medical implantation material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation method of a new type of titanium-nickel medical implant material. Firstly, plasma alloying technology is used to infiltrate titanium on the surface of titanium-nickel alloy workpiece to form a deposition layer, and then TiO is formed on the surface of the deposition layer by micro-arc oxidation. 2 and Al 2 o 3 mixed oxide coating;

[0028] Specifically include the following steps:

[0029]1) Take the titanium-nickel alloy substrate, cut it into Φ20mm×4mm as the workpiece, and remove the oxide film on the surface of the workpiece by mechanical and chemical mixing methods. The specific process is: use metallographic sandpaper to roughly grind the surface of the workpiece, and then sandblast the surface of the workpiece Grinding, then ultrasonic cleaning the surface of the workpiece, and finally drying;

[0030] 2) In the plasma surface alloying metal infiltration furnace, the source electrode selects a pure titanium target with a purity of 99.99%, and the...

Embodiment 2

[0041] A preparation method of a new type of titanium-nickel medical implant material. Firstly, plasma alloying technology is used to infiltrate titanium on the surface of titanium-nickel alloy workpiece to form a deposition layer, and then TiO is formed on the surface of the deposition layer by micro-arc oxidation. 2 and Al 2 o 3 mixed oxide coating;

[0042] Specifically include the following steps:

[0043] 1) Take the titanium-nickel alloy substrate, cut it into Φ20mm×4mm as the workpiece, and remove the oxide film on the surface of the workpiece by mechanical and chemical mixing methods. The specific process is: use metallographic sandpaper to roughly grind the surface of the workpiece, and then sandblast the surface of the workpiece Grinding, then ultrasonic cleaning the surface of the workpiece, and finally drying;

[0044] 2) In the plasma surface alloying metal infiltration furnace, the source electrode selects a pure titanium target with a purity of 99.99%, and th...

Embodiment 3

[0055] A preparation method of a new type of titanium-nickel medical implant material. Firstly, plasma alloying technology is used to infiltrate titanium on the surface of titanium-nickel alloy workpiece to form a deposition layer, and then TiO is formed on the surface of the deposition layer by micro-arc oxidation. 2 and Al 2 o 3 mixed oxide coating;

[0056] Specifically include the following steps:

[0057] 1) Take the titanium-nickel alloy substrate, cut it into Φ20mm×4mm as the workpiece, and remove the oxide film on the surface of the workpiece by mechanical and chemical mixing methods. The specific process is: use metallographic sandpaper to roughly grind the surface of the workpiece, and then sandblast the surface of the workpiece Grinding, then ultrasonic cleaning the surface of the workpiece, and finally drying;

[0058] 2) In the plasma surface alloying metal infiltration furnace, the source electrode selects a pure titanium target with a purity of 99.99%, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a novel titanium-nickel medical implantation material, particularly a composite treatment method for preparing a titanium dioxide / aluminum oxide mixture by depositing titanium on a titanium-nickel surface and performing micro-arc oxidation. The method comprises the following steps: firstly, by using a titanium-nickel alloy base as a workpiece, eliminating the oxide film on the workpiece surface by a mechanical-chemical mixed method; secondly, depositing titanium on the workpiece surface by a plasma surface alloying technique; thirdly, carrying out micro-arc oxidation on the workpiece in a micro-arc oxidation device; and finally, carrying out ultrasonic cleaning on the workpiece, and drying to obtain the finished product. The material can effectively isolate the precipitation of the nickel element in the titanium-nickel alloy, and the ceramic film layer of the titanium base surface subjected to micro-arc oxidation has the advantages of fewer surface voids, high hardness, high corrosion resistance, favorable insulativity and high binding force with the base metal. The method has the characteristics of favorable technical repetitiveness, controllable quality and the like, is simple to operate, can be widely used for surface modification treatment of titanium-nickel alloys, and effectively improves the application range and level.

Description

technical field [0001] The invention relates to the technical field of surface modification of rare metal materials, in particular to a compound treatment method for depositing titanium on the surface of titanium and nickel and performing micro-arc oxidation to prepare titanium dioxide and aluminum oxide mixed ceramic films, specifically a new type of titanium-nickel medical treatment. Preparation method of implant material. Background technique [0002] Titanium-nickel alloys are widely used in biomedical fields due to their good biocompatibility, high specific strength, corrosion resistance, and superelasticity. It is mainly used to manufacture blood vessels, esophageal stents, dental and orthopedic devices, etc. However, there are two major factors restricting its wide application so far: first, its hardness is low, as an implant, it needs to serve for a long time, and excessive wear and tear will cause human lesions; second, the precipitation of nickel ions caused by co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C28/00C23C10/08C25D11/26
Inventor 王振霞张红前贺志勇杨耀军刘小萍单小林杨红玉
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com