Method for producing iron hot-pressed carbon-containing pellets through direction reduction on metallized iron powder

A technology for metallizing iron powder and carbon pellets, applied in the field of iron and steel metallurgy, can solve the problems of poor high-temperature metallurgy performance, reduced output, increased energy consumption, etc. Effect

Active Publication Date: 2015-03-04
JIUQUAN IRON & STEEL GRP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the defects of low strength of carbon-containing pellets and poor high-temperature metallurgical properties in the prior art, which lead to reduced output and increased energy consumption of metallurgical equipment such as blast furnaces, and to provide a production method using direct reduction metallized iron powder. The method of iron hot-pressing carbon-containing pellets meets the needs of metallurgical equipment such as blast furnaces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1. Selection of metallized iron powder

[0020] In the production of iron hot-pressed carbon-containing pellets, the metallization rate of direct reduced iron powder is 90%, and the particle size is -200 mesh 60%.

[0021] 2. Selection of coal type

[0022] The coal type is caking coal with a caking index greater than 1.5. The colloid thermal stability of the coal is 140°C, the fixed carbon content in the coal is above 65%, and the particle size range is 0.2mm.

[0023] 3. Mixing of materials

[0024] Metallized iron powder and coal powder with moisture content less than 3% are mixed according to 75:25, and the prepared materials should be stirred evenly.

[0025] 4. Preheating of mixed materials

[0026] The mixed material is fed into the heating equipment, and under the action of high temperature in the furnace, the temperature of the mixed material is raised to 450°C.

[0027] 5. Insulation of mixed materials

[0028] After the mixed material is kept at a temper...

Embodiment 2

[0035] 1. Selection of metallized iron powder

[0036] In the production of iron hot-pressed carbon-containing pellets, the metallization rate of direct reduced iron powder is 90%, and the particle size is -200 mesh 65%.

[0037] 2. Selection of coal types

[0038] The coal type is caking coal with a caking index greater than 1.5. The colloidal thermal stability of the coal is 140°C, the fixed carbon content in the coal is above 65%, and the particle size range is 0.25mm.

[0039] 3. Mixing of materials

[0040] Metallized iron powder and coal powder with a moisture content of less than 3% are mixed according to the ratio of 70:30, and then water glass with a total weight of 0.8% of metallized iron powder and coal powder is added, and the prepared materials should be stirred evenly.

[0041] 4. Preheating of mixed materials

[0042] The mixed material is fed into the heating equipment, and under the action of high temperature in the furnace, the temperature of the mixed mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for producing iron hot-pressed carbon-containing pellets through direct reduction on metallized iron powder. The method for producing the iron hot-pressed carbon-containing pellets through the direct reduction on the metallized iron powder comprises the following steps: adding direct reduction iron powder with metallization ratio about 90% into equipment, such as a blast furnace to be utilized, manufacturing the metallized iron powder into pellets with a certain metallurgical performance before use, according to the caking property of coal and the characteristic related to temperature of the coal, mixing the metallized iron powder with coal dust in a certain proportion and then carrying out hot pressing at the temperature about 450 DEG C, so that the coal and metalized iron powder particles are fully contacted and caked, and a heat treatment technique at the temperature about 700 DEG C is adopted for improving strength of the iron hot-pressed carbon-containing pellets, so that the produced iron hot-pressed carbon-containing pellets have good compressive strength and metallurgical performance.

Description

technical field [0001] The invention belongs to the field of iron and steel metallurgy, and relates to a production method of carbon-containing pellets, in particular to a method for producing iron hot-pressed carbon-containing pellets by direct reduction of metallized iron powder, which is widely used in blast furnaces, electric furnaces, and cupolas and other equipment. Background technique [0002] In the production of equipment such as blast furnaces, the basic requirement for raw materials is that they should have a certain compressive strength. At present, the production of iron hot-pressed carbon-containing pellets in China mainly uses high-grade iron ore concentrate as raw material, and its main production methods include cold-solidified carbon-containing pellets and hot-pressed carbon-containing pellets. (1) Cold-consolidated pellets are mainly used in direct reduction or smelting reduction processes. It is made of iron concentrate with a certain proportion of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/16
Inventor 王明华权芳民雷鹏飞展仁礼鲁逢霖张志刚马胜军胡明
Owner JIUQUAN IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com