A kind of powder metallurgy bearing steel and preparation method thereof

A technology of powder metallurgy and bearing steel, applied in the field of powder metallurgy bearing steel and its preparation, to achieve the effect of compact structure, simple production steps and good microstructure

Active Publication Date: 2016-08-17
GUANGXI SHENGLONG METALLURGICAL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the method of improving rolling fatigue life with low oxidation has almost reached its limit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention will be described in detail below through specific examples.

[0016] A powder metallurgy bearing steel made from the following raw materials in parts by weight (kg): graphite 0.2, silicon 0.1, manganese 3.1, chromium 6.7, copper 0.7, ditungsten boride 0.3, SnO 2 0.1 、V 2 o 5 0.4, Te0.1, ZrO 2 0.3, microcrystalline wax 3.2, iron powder 87, additive 1;

[0017] The additive is made of the following raw materials in parts by weight (kg): iron powder 3, kaolin 2, nano-carbon 2, zirconium fluoride 1, alum 2, sodium alginate 3, sodium tripolyphosphate 1, corundum powder 3, Copper sulfate 1, calcium stearate 1, vinyl triethoxysilane 3; the preparation method is to mix iron powder, kaolin, zirconium fluoride, alum, sodium alginate, sodium tripolyphosphate, corundum powder, copper sulfate, Grind it into 200-300 mesh powder, then add vinyltriethoxysilane and mix evenly, press it into a billet at 10-15Mpa, then send it to 920-950℃ for calcination for 3-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a powder metallurgy bearing steel, which is characterized in that it is made of the following raw materials in parts by weight: graphite 0.2-0.3, silicon 0.1-0.2, manganese 3.1-3.3, chromium 6.7-6.9, copper 0.7-0.9, boron Ditungsten 0.3‑0.4, SnO 2 0.1‑0.2, V 2 o 5 0.4‑0.45, Te 0.1‑0.2, ZrO 2 0.3‑0.4, microcrystalline wax 3.2‑3.4, iron powder 87‑89, auxiliary agent 1‑2; graphite is added to the raw materials of the present invention, which increases the wear resistance and lubricity of bearing steel, and the manufactured bearing steel has a dense structure and microscopic The structure is good, the pores are few, and the structure rigidity, hardness, fatigue resistance and tensile strength are excellent; the invention has little environmental pollution, simple production steps and improved production efficiency.

Description

technical field [0001] The invention relates to the field of powder metallurgy, in particular to a powder metallurgy bearing steel and a preparation method thereof. Background technique [0002] Powder metallurgy is an industrial technology for producing metal powder or using metal powder (or a mixture of metal powder and non-metal powder) as raw material, forming and sintering to produce metal materials, composite materials and various types of products. At present, powder metallurgy technology has been widely used in transportation, machinery, electronics, aerospace, weapons, biology, new energy, information and nuclear industries, and has become one of the most dynamic branches of new material science. Powder metallurgy technology has a series of advantages such as significant energy saving, material saving, excellent performance, high product precision and good stability, and is very suitable for mass production. In addition, some materials and complex parts that cannot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/38C22C33/02B22F1/00
Inventor 黄浩
Owner GUANGXI SHENGLONG METALLURGICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com