Corrosion-resistant terafluoroethylene-propylene rubber/chlorosulfonated polyethylene rubber sealing gasket and preparation method thereof

A technology of chlorosulfonated polyethylene and tetrapropylene fluorine rubber, which is applied in the field of gaskets and their preparation, can solve the problems of corrosion resistance, unsuitable service life equipment requirements, etc., and achieve low expansion, high compressive strength, and sealing performance excellent effect

Inactive Publication Date: 2013-11-27
WUHU YINHONG HYDRAULIC COMPONENTS
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing sealing materials for hydraulic systems are incompatible with the requirements of equipment in terms of corrosion resistance and service life to varying degrees, which are far from meeting the actual needs. Therefore, it is urgent to develop a corrosion-resistant rubber sealing material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion-resistant terafluoroethylene-propylene rubber/chlorosulfonated polyethylene rubber sealing gasket and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] A corrosion-resistant tetrapropylene fluororubber / chlorosulfonated polyethylene rubber gasket, made of the following weight (kg) raw materials: tetrapropylene fluororubber (TP-2) 80, chlorosulfonated polyethylene rubber (CSM2305) 30 , polyether ether ketone 15, carbon black N330 20, nano tin dioxide 5, calcined clay 12, modified nano ceramics 10-15, mica powder 5-10, dicumyl peroxide 2, 2,5-dimethyl Base-2,5-di-tert-butylperoxyhexane 1.5, triallyl isocyanurate 8, accelerator CZ 2, accelerator ZDC 1, lead stearate 1.5, zinc oxide 2, magnesium oxide 1.5. Antiaging agent TPPD2, antiaging agent ODA 2 .

[0013] The modified nano-ceramic is made from raw materials with the following weight (kg):

[0014] Nano-aluminum nitride 20, nano-titanium carbide 10, nano-zirconium boride 8, glass powder 2, fatty alcohol polyoxyethylene ether sodium sulfate 3, polyvinylpyrrolidone 12, calcium lignosulfonate 6, trifluoropropyl methyl silicone oil 22. Polyvinyl acetate emulsion 65, bis(...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion-resistant terafluoroethylene-propylene rubber / chlorosulfonated polyethylene rubber sealing gasket and a preparation method thereof. The sealing gasket is prepared from the following raw materials: terafluoroethylene-propylene rubber, chlorosulfonated polyethylene rubber, polyether ether ketone, carbon black N330, nano tin dioxide, calcined argil, modified nano ceramic, mica powder, dicumyl peroxide, 2,5-dimethyl-2,5-hexane-di-tert-butyl peroxide, triallyl isocyanurate, an accelerant CZ2-3, an accelerant ZDC (Zinc Diethyl Dithiocarbamate) and the like. According to the method, when the terafluoroethylene-propylene rubber, the chlorosulfonated polyethylene rubber, the polyether ether ketone and other high-molecular materials with the excellent performance of corrosion resistance are compounded and mixed together, the nano tin dioxide, the calcined argil, the modified nano ceramic, the mica powder and other inorganic filling materials capable of improving the corrosion resistance of the rubber are added at the same time. In addition, the modified nano ceramic can be used for improving the mechanical strength, abrasion resistance, oil resistance and the like of the rubber.

Description

technical field [0001] The invention relates to a sealing gasket and a preparation method thereof, in particular to a corrosion-resistant tetrapropylene fluororubber / chlorosulfonated polyethylene rubber sealing gasket and a preparation method thereof. Background technique [0002] With the rapid development of modern hydraulic transmission technology, the sealing problem of hydraulic devices is becoming more and more prominent. Existing sealing materials for hydraulic systems are incompatible with the requirements of equipment in terms of corrosion resistance and service life to varying degrees, and are far from meeting the actual needs. Therefore, it is urgent to develop a corrosion-resistant rubber sealing material. Contents of the invention [0003] The object of the present invention is to provide a corrosion-resistant tetrapropylene fluororubber / chlorosulfonated polyethylene rubber gasket and a preparation method thereof for the deficiencies of the prior art. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/12C08L23/34C08L61/16C08K13/06C08K9/04C08K3/28C08K3/14C08K3/38C08K3/04C08K3/22C08K3/34C08K5/098
Inventor 张开会陶庭鸿张火生
Owner WUHU YINHONG HYDRAULIC COMPONENTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products