Method for manufacturing nylon conductive fibers

A technology of conductive fiber and manufacturing method, which is applied in the direction of conductive/antistatic filament manufacturing, single-component polyamide artificial filament, etc., can solve the problems of reducing conductive performance and easily scratching the surface of polyester conductive fiber, and achieves the preparation process Simple, inexpensive to prepare effect

Active Publication Date: 2013-06-26
JIANGSU ZJA NEW MATERIAL
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Textiles are extensively treated with alkali in the process of weaving and printing and dyeing, and polyester conductive fibers are not resistant to alkali treatment, so the surface of polyester conductive fibers is easily damaged during the post-processing of textiles, which reduces the conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation steps are as follows:

[0025] 1) According to the number of parts by mass, take 10 parts of the characteristic parameters of the needle-shaped zinc oxide whisker with a diameter of 0.2-1mm and a length of 5-15mm, and 4 parts of a conductive titanic acid with a diameter of 0.2-0.6mm and a length of 5-12mm Potassium whiskers; after mixing the above materials evenly, bake them in a vacuum furnace at 450°C for 4 hours; after cooling, add them to 300 parts of deionized water at 55°C containing 4% sodium metaphosphate and 0.5% calcium stearate for ultrasonic dispersion After 60 minutes, filter and dry the filter cake in a vacuum oven to obtain a coated whisker mixture.

[0026] 2) Take 0.8 parts of multi-walled carbon nanotubes and add 50 parts of nitric acid solution, ultrasonically disperse at 20°C for 60 minutes, ultrasonic frequency is 20KHz, then heat to 90°C, and oxidize for 30 minutes. After cooling, filter and wash, dry in vacuum, and grind in a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
electrical resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for manufacturing nylon conductive fibers. The method comprises the following steps of: (1) uniformly mixing four-needle type zinc oxide crystal whisker and conductive potassium titanate crystal whisker, roasting, cooling, adding into deionized water, performing ultrasonic dispersion, filtering, and drying, and thus obtaining wrapped crystal whisker mixtures; (2) adding multi-wall carbon nano tubes into a hydrogen nitrate solution, performing ultrasonic dispersion, heating, oxidizing, cooling, filtering, drying and grinding; (3) stirring the crystal whisker mixtures, the multi-wall carbon nano tubes, stibium-doped tin oxide conductive powder, a coupling agent, polymethylene, an antioxidant and nylon sliced powder in a closed manner, and granulating the mixtures through a screw extruder, and thus obtaining nylon conductive mother particles; and (4) respectively putting the nylon conductive mother particles and polyamide 6 into the corresponding screw extruders, spraying from a composite spinneret plate, cooling and winding to obtain the nylon conductive fibers. The nylon conductive fibers have conductive characteristics and are high in processing property and spinning property.

Description

technical field [0001] The invention relates to the field of nylon fiber manufacturing, in particular to a method for manufacturing nylon and nylon conductive fibers. Background technique [0002] The vast majority of polymer materials are insulating materials, and chemical fibers made of polymer materials, such as polyester, polypropylene, nylon, etc., are also insulating, and their resistance value is 10 13 Ω or more. During the use of these fibers, static electricity continues to accumulate, but the charge cannot be released, and eventually discharges with a high potential, which has serious consequences for the safety of production in special occasions such as the petrochemical industry and chemical industry. At the same time, static electricity will also produce field effects. In the manufacture and use of high-precision instruments, it must be strictly eliminated in the electronics industry; in the civilian field, static electricity will cause electric shock when pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/09
Inventor 周焕民
Owner JIANGSU ZJA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com