A kind of high cti value, high gwit value environmental protection flame retardant glass fiber reinforced pp/pa612 alloy material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of PA612 and alloy materials, which is applied in the field of PP/PA612 alloy materials and its preparation, to achieve the effects of improving impact performance, reducing friction coefficient and improving slipperiness
Inactive Publication Date: 2015-09-09
SHANGHAI SUNNY
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, there is no report on the environmentally friendly flame-retardant glass fiber reinforced PP / PA612 alloy material with high CTI value and high GWIT value and excellent comprehensive performance.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0058] Example 1 Preparation of PP / PA612 alloy material of the present invention (1)
[0059] Weigh raw materials by weight percentage: PP 25%, PA612 (intrinsic viscosity: 2.8dl / g) 25.1%, compound flame retardant 12%, antimony trioxide 4%, alkali-free glass treated with silane coupling agent Fiber 30%, maleic anhydride grafted PP 3%, antioxidant 1330 0.4%, iron oxide 0.5%; put the weighed raw materials into a high-mixer and mix for 5 minutes, and discharge; extrude with a twin-screw extruder For granulation, the processing temperature is 220-240°C, the screw speed is 35HZ, and the specific processing conditions are shown in the table below.
[0060]
Embodiment 2
[0061] Example 2 Preparation of PP / PA612 alloy material of the present invention (2)
[0062] Weigh raw materials by weight percentage: PP 25%, PA612 (intrinsic viscosity: 2.8dl / g) 23%, compound flame retardant 12%, antimony trioxide 4%, alkali-free glass treated with silane coupling agent Fiber 30%, maleic anhydride grafted PP 5%, antioxidant 1330 0.4%, iron oxide 0.6%; put the weighed raw materials into a high-mixer and mix for 2 minutes, and discharge; extrude with a twin-screw extruder For granulation, the processing temperature is 220-240°C, the screw speed is 35HZ, and the specific processing conditions are shown in the table below.
[0063]
Embodiment 3
[0064] Example 3 Preparation of PP / PA612 alloy material of the present invention (3)
[0065] Weigh raw materials by weight percentage: PP 23%, PA612 (intrinsic viscosity: 2.8dl / g) 22%, compound flame retardant 20%, antimony trioxide 4.3%, alkali-free glass treated with silane coupling agent Fiber 20%, maleic anhydride grafted PP 10%, antioxidant 1330 0.1%, iron oxide 0.6%; put the weighed raw materials into a high-mixer and mix for 2 minutes, and discharge; extrude with a twin-screw extruder For granulation, the processing temperature is 220-240°C, the screw speed is 30HZ, and the specific processing conditions are shown in the table below.
[0066]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a high-CTI (Creepage Tracking Index) high-GWIT (Glow-Wire Ignition Temperature) environmental-friendly flame-retardant glass fiber reinforced PP / PA612 (Polypropylene / Polyamide 612) alloy material which is prepared from the following raw materials in percentage by weight: 23%-41% of PP, 22%-41% of PA612, 6%-20% of compound flame retardant, 3%-15% of antimony trioxide, 20%-30% of glass fibers, 2%-10% of compatilizer, 0.1%-1% of antioxidant and 0.1%-1% of oxide, wherein the compound flame retardant contains the following materials in percentage by weight: 50% of BPS (Brominated Polystyrene), 25% of magnesium hypophosphite and 25% of talcum powder. The invention also provides a preparation method of the high-CTI high-GWIT environmental-friendly flame-retardant glass fiber reinforced PP / PA612 alloy material. The high-CTI high-GWIT environmental-friendly flame-retardant glass fiber reinforced PP / PA612 alloy material provided by the invention has the advantages that the GWIT value is increased by 50-100 DEG C due to adoption of a novel flame-retardant compounding system, so that the material can pass 850 DEG C glow-wire test; the GWIT value is also obviously increased through the addition of the glass fibers; moreover, and impact property and ageing-resistant property are improved, processing fluidity and smoothness are increased and friction factor is lowered.
Description
technical field [0001] The invention relates to a PP / PA612 alloy material and a preparation method thereof, in particular to an environmentally friendly flame-retardant glass fiber reinforced PP / PA612 alloy material with a high CTI value and a high GWIT value and a preparation method thereof. Background technique [0002] Nylon (Nylon), Chinese name polyamide, English name polyamide, referred to as PA, is the general term for thermoplastic resins containing repeated amide groups—[NHCO]—on the main chain of the molecule, and its naming is determined by the specific number of carbon atoms in the synthetic monomer , such as PA-6, PA-66, PA-1010, PA-610. PA has high crystallinity and obvious melting point; high surface hardness, wear resistance, small friction coefficient, self-lubrication and noise reduction; good low temperature performance and certain heat resistance (can be used below 100°C); non-toxic , Odorless, no mildew, self-extinguishing, good weather resistance, but ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.