A kind of high gwit flame retardant pbt/pet alloy material and its preparation method and application

A technology of alloy materials and PBT resin, applied in the field of engineering plastics, can solve the problems that the GWIT value of flame-retardant PBT/PET alloy materials cannot reach 850°C and cannot meet the GWIT requirements, and achieve the effect of excellent mechanical properties

Active Publication Date: 2022-07-12
KINGFA SCI & TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defect and deficiency that the GWIT value of the existing flame-retardant PBT / PET alloy material cannot reach 850°C and cannot meet the GWIT requirements of electronic and electrical products, and provide a high-GWIT flame-retardant PBT / PET Alloy materials, through the synergistic effect of antimony trioxide and calcium hydroxide, effectively improve the GWIT performance and mechanical properties of flame-retardant flame-retardant PBT / PET alloy materials, with 850 ° C and 1.6mmV0 level flame retardancy, and good mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high gwit flame retardant pbt/pet alloy material and its preparation method and application
  • A kind of high gwit flame retardant pbt/pet alloy material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～7

[0037] A high GWIT flame retardant PBT / PET alloy material, in weight percent, comprising the components shown in Table 1.

[0038] Among them, the relative density of PBT resin is 1.30-1.32g / cm 3 , melting point 215-230 ℃. Manufacturer: Changchun Chemical, Taiwan, China, brand: PBT 1200-211M

[0039] The density of PET resin is 1.31~1.33g / cm 3 , melting point 250-270 ℃. Manufacturer: Sinopec Yizheng Chemical Fiber, brand: PET FG600

[0040] The particle size of calcium hydroxide was 5 μm. Commercially available.

[0041] Brominated flame retardants are brominated epoxy resins. Manufacturer: Israel Chemical Group, brand: Powder-F-2100.

[0042] The preparation method of the high GWIT flame retardant PBT / PET alloy material is as follows:

[0043] 1) Dry the PBT at 135°C for 4 hours and set it aside for use;

[0044]2) Mix PBT resin, PET resin, brominated flame retardant, antimony trioxide and calcium hydroxide evenly, add them into the twin-screw extruder, and feed the ...

Embodiment 8

[0048] A flame-retardant PBT / PET alloy material with high GWIT, by weight percentage, comprising the following components:

[0049] 25.5 parts of PBT resin

[0050] 25 parts PET resin

[0051] 8 parts of brominated flame retardant

[0052] 0.5 parts of antimony trioxide

[0053] 4 parts calcium hydroxide

[0054] 35 parts of E-glass fiber.

[0055] Among them, the relative density of PBT resin is 1.30-1.32g / cm 3 , melting point 215-230 ℃.

[0056] The density of PET resin is 1.31~1.33g / cm 3 , melting point 250-270 ℃.

[0057] Brominated flame retardants are brominated epoxy resins.

[0058] The calcium hydroxide was calcium hydroxide with a particle size of 8 μm.

[0059] The preparation method of the flame-retardant PBT / PET alloy material with high GWIT is the same as that in Example 1.

Embodiment 9

[0061] A flame-retardant PBT / PET alloy material with high GWIT, by weight percentage, comprising the following components:

[0062] 25.5 parts of PBT resin

[0063] 25 parts PET resin

[0064] 8 parts of brominated flame retardant

[0065] 0.5 parts of antimony trioxide

[0066] 4 parts calcium hydroxide

[0067] 35 parts of E-glass fiber.

[0068] Among them, the relative density of PBT resin is 1.30-1.32g / cm 3 , melting point 215-230 ℃.

[0069] The density of PET resin is 1.31~1.33g / cm 3 , melting point 250-270 ℃.

[0070] Brominated flame retardants are brominated epoxy resins.

[0071] The calcium hydroxide was calcium hydroxide having a particle size of 10 μm.

[0072] The preparation method of the flame-retardant PBT / PET alloy material with high GWIT is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant PBT / PET alloy material with high GWIT and a preparation method and application thereof. The flame-retardant PBT / PET alloy material includes the following components in parts by weight: 13-48 parts of PBT resin, 5-40 parts of PET resin, 8-10 parts of brominated flame retardant, and 0.5-1 part of antimony trioxide , 3 to 6 parts of calcium hydroxide, and 25 to 35 parts of alkali-free glass fiber. The invention can effectively improve the GWIT value of the flame-retardant PBT / PET alloy material through the specific composition, reaching 850°C, achieving 1.60mmV0 level flame-retardant, and meeting the high requirements for GWIT of unattended electrical products. Furthermore, the high GWIT flame retardant PBT / PET alloy material of the present invention has high GWIT and V0 flame retardant effects, and also has excellent mechanical properties. Notched impact strength can reach about 9kJ / m.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, and more particularly, to a flame-retardant PBT / PET alloy material with high GWIT and a preparation method and application thereof. Background technique [0002] Compared with PBT materials, flame retardant reinforced PBT / PET materials have the advantages of brighter appearance and higher heat resistance temperature. They are widely used in electronic appliances and other fields. For a long time, flame retardant PBT / PET materials are usually compounded with bromine and antimony. The system has the advantages of high flame retardant efficiency and good flame retardant effect, but the conventional flame retardant PBT / PET engineering plastics can only meet the V-0 flame retardant requirements of UL-94. For the IEC glow wire test, the glow wire The ignition temperature (GWIT) is relatively low, usually only about 750℃, and many unattended electrical products put forward higher requiremen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L63/00C08K7/14C08K3/22
CPCC08L67/02C08L2201/02C08L2205/025C08L2203/20C08K2003/2206C08K2201/003C08L63/00C08K7/14C08K3/22C08K3/2279
Inventor 付学俊黄险波叶南飚陈锐殷年伟陈伟丁超
Owner KINGFA SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com