Ni-P alloy coating continuous casting crystallizer copper plate and preparation process thereof

A crystallizer copper plate, nickel-phosphorus alloy technology, applied in the direction of metal layered products, layered products, chemical instruments and methods, etc., can solve the problems of high cost, large investment, and strict control of process conditions, and reduce the number of repairs , improve the service life and ensure the effect of product quality

Active Publication Date: 2012-11-14
XIXIA LONGCHENG SPECIAL MATERIALS CO LTD
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although some high-tech has emerged as the times require, the investment is large, the cost is high, and the control of process conditions is demanding, which cannot meet the production and development needs of enterprises.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ni-P alloy coating continuous casting crystallizer copper plate and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0017] The above object of the present invention can be achieved by the following measures, a continuous casting crystallizer copper plate coating, made of nickel-phosphorus alloy, wherein, by mass percentage, the nickel content is 95%, and the phosphorus content is 5%.

[0018] Described a kind of continuous casting crystallizer copper plate coating and preparation technology thereof, comprises the following steps:

[0019] 1) Pre-plating treatment of the substrate: degreasing the substrate, mechanical sand blasting, electrolytic degreasing, ultrasonic degreasing, acid spray activation;

[0020] 2) Prepare a composite electroplating solution containing electroplated Ni-P alloy layer materials in the electroplating tank: the composite electroplating solution is made of the following components: nickel sulfamate: 250g / L; phosphorous acid: 1g / L; nickel chloride: 5g / L; Boric acid: 28g / L; Sodium lauryl sulfate: 0.1g / L; Stress reliever (LC): 3ml / L; PH: 1.2, T: 49°C; Stirring condit...

Embodiment example 2

[0024] The above object of the present invention can be achieved by the following measures, a continuous casting crystallizer copper plate coating, made of nickel-phosphorus alloy, wherein, by mass percentage, the nickel content is 97.3%, and the phosphorus content is 2.7%. Described a kind of continuous casting crystallizer copper plate coating and preparation technology thereof, comprises the following steps:

[0025] 1) Pre-plating treatment of the substrate: degreasing the substrate, mechanical sand blasting, electrolytic degreasing, ultrasonic degreasing, acid spray activation;

[0026] 2) Prepare a composite electroplating solution containing electroplated Ni-P alloy layer materials in the electroplating tank: the composite electroplating solution is made of the following components: nickel sulfamate: 425g / L; phosphorous acid: 13g / L; nickel chloride: 12g / L; Boric acid: 31g / L; Sodium lauryl sulfate: 0.6g / L; Stress reliever (LC): 9ml / L; PH: 1.8, T: 56°C; Stirring condition...

Embodiment example 3

[0030] The above object of the present invention can be achieved by the following measures, a continuous casting crystallizer copper plate coating, made of nickel-phosphorus alloy, wherein, by mass percentage nickel content is 99.7%, phosphorus content is 0.3%. A continuous casting crystallizer copper plate coating and a preparation process thereof, comprising the steps of:

[0031] 1) Pre-plating treatment of the substrate: degreasing the substrate, mechanical sand blasting, electrolytic degreasing, ultrasonic degreasing, acid spray activation;

[0032] 2) Prepare a composite electroplating solution containing electroplated Ni-P alloy layer materials in the electroplating tank: the composite electroplating solution is made of the following components: nickel sulfamate: 600g / L; phosphorous acid: 25g / L; nickel chloride: 20g / L; Boric acid: 35g / L; Sodium lauryl sulfate: 1g / L; Stress reliever (LC): 15ml / L; PH: 2.5, T: 64°C; Stirring conditions: circulating pump stirring;

[0033...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a continuous casting crystallizer copper plate plating layer and a preparation process thereof. The Ni-P crystallizer copper plate plating layer comprises a crystallizer copper plate base body, wherein an Ni-P alloy layer is plated on the surface of the crystallizer copper plate base body, and contains nickel with the mass ratio being 95 percent to 99.7 percent, and phosphorus with the mass ratio being 0.3 percent to 5 percent. The preparation process of the continuous casting crystallizer copper plate plating layer comprises the following steps of: a, preplating the base body; b, preparing composite electroplate liquid containing Ni-P materials in a plating bath; and c, electroplating the Ni-P alloy layer. Due to the adoption of the scheme, the defects of low steel production, large abrasion, frequent repair of the continuous casting crystallizer copper plate can be overcome, and the continuous casting crystallizer copper plate plating layer with uniform densification, favorable binding force, low heat crack tendency, small internal stress, excellent wear-resisting property and long life cycle is obtained.

Description

technical field [0001] The invention belongs to the technical field of crystallizers for metallurgy, in particular to a nickel-phosphorus alloy coating continuous casting crystallizer copper plate and a preparation process thereof. technical background [0002] With the rapid development of iron and steel technology, the continuous casting mold has been developed in the direction of high casting speed, high mechanical strength, good thermal conductivity, high hardness, wear resistance and corrosion resistance. However, the conventional Cr plating, Ni plating, Ni–Fe plating, Ni–Co plating, and Co–Ni plating layer, in the application process of the high-speed continuous casting mold, have large wear, heat resistance and fatigue, resulting in copper plate Unplanned off-line, increased mold copper repair times, and shortened service life. Obviously, conventional coatings can no longer meet the needs of steel companies. Although some high-tech technologies have emerged as the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/059C25D3/56C25D5/50B32B15/01
Inventor 朱书成黄国团徐文柱赵家亮
Owner XIXIA LONGCHENG SPECIAL MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com