Anti-aging wood-plastic composite material board and preparation method thereof

A wood-plastic composite material and anti-aging technology, applied in the field of wood-plastic composite materials, can solve problems such as shortening the service life, limiting the scope of use, and prone to cracking, so as to reduce the cost of raw materials, not easy to warp and deform, and reduce felling. amount of effect

Inactive Publication Date: 2012-10-17
G&S HUZHOU ENTERPRISES
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But even so, there are some obvious deficiencies in the use of wood-plastic composite materials, such as long-term use, especially in open-air use, it is prone to cracking, fading and other aging phenomena under the action of light and oxygen, thereby shortening its service life. limited its scope of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Wood powder (80 mesh) 100kg, plastic particles (polypropylene) 40kg,

[0059] Dicumyl peroxide 1.5kg, nano titanium dioxide (50nm) 2kg,

[0060] Antioxidant (2,6-di-tert-butyl p-cresol) 0.25kg, antioxidant synergist 0.1kg,

[0061] Light stabilizer 0.2kg, basic magnesium sulfate whiskers 13kg,

[0062] Stearic acid 0.5kg, oxidized polyethylene 3kg, pigment (iron red) 0.25kg

[0063] The present invention is a kind of preparation method of aging-resistant plastic-wood composite material plate, and it comprises the following steps:

[0064] (1) Weigh each raw material according to the formula quantity;

[0065] (2) Put plastic particles, dicumyl peroxide, nano-titanium dioxide, antioxidant, antioxidant synergist, light stabilizer, basic magnesium sulfate whisker, stearic acid, and oxidized polyethylene into the machine Stir in the stirring tank for 8 minutes;

[0066] (3) After mixing, use an extruder for melt blending and granulation. The barrel temperature of the e...

Embodiment 2

[0070] Wood powder (60 mesh) 100kg, plastic particles (polyethylene) 30kg,

[0071] Dicumyl peroxide 1kg, nano titanium dioxide (20nm) 1kg,

[0072] Antioxidant (2,6-di-tert-butyl p-cresol) 0.2kg, antioxidant synergist 0.08kg,

[0073] Light stabilizer 0.1kg, basic magnesium sulfate whiskers 10kg,

[0074] Stearic acid 0.3kg, oxidized polyethylene 2kg, pigment (iron yellow) 0.2kg

[0075] The present invention is a kind of preparation method of aging-resistant plastic-wood composite material plate, and it comprises the following steps:

[0076] (1) Weigh each raw material according to the formula quantity;

[0077] (2) Put plastic particles, dicumyl peroxide, nano-titanium dioxide, antioxidant, antioxidant synergist, light stabilizer, basic magnesium sulfate whisker, stearic acid, and oxidized polyethylene into the machine Stir in the stirring tank for 6 minutes;

[0078] (3) After mixing, use an extruder for melt blending and granulation. The barrel temperature of the ex...

Embodiment 3

[0082] Wood powder (100 mesh) 100kg, plastic particles (polystyrene) 50kg,

[0083] Dicumyl peroxide 2kg, nano titanium dioxide (80nm) 3kg,

[0084] Antioxidant (2,6-di-tert-butyl p-cresol) 0.3kg, antioxidant synergist 0.12kg,

[0085] Light stabilizer 0.3kg, basic magnesium sulfate whiskers 16kg,

[0086] Stearic acid 0.7kg, oxidized polyethylene 4kg, pigment (iron black) 0.3kg

[0087] The present invention is a kind of preparation method of aging-resistant plastic-wood composite material plate, and it comprises the following steps:

[0088] (1) Weigh each raw material according to the formula quantity;

[0089] (2) Put plastic particles, dicumyl peroxide, nano-titanium dioxide, antioxidant, antioxidant synergist, light stabilizer, basic magnesium sulfate whisker, stearic acid, and oxidized polyethylene into the machine Stir in the stirring tank for 10 minutes;

[0090] (3) After mixing, use an extruder for melt blending and granulation. The barrel temperature of the ex...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to an anti-aging wood-plastic composite material board and a preparation method of the board. The preparation method comprises the steps of: firstly, evenly stirring plastic particles, diisopropylbenzene peroxide, nano-titanium dioxide, antioxidant, antioxidant synergist, light stabilizer, basic magnesium sulfate whisker, stearic acid and oxidized polyethylene; carrying out melt blending and pelleting by adopting an extruder to obtain modified plastic particles; and then stirring the modified plastic particles, wood powder and pigment, and carrying out melt blending and extruding forming by adopting the extruder to obtain the anti-aging wood-plastic composite material board. The anti-aging wood-plastic composite material board is convenient to produce and manufacture, low in cost, less in plastic consumption and wood consumption, environment-friendly and high in modulus and rigidity, does not easily cause buckling deformation, and is free from cracking and damage by worms, resistant in ultraviolet light and thermal oxidizing aging, free from color fading and decomposition and long in service life. The anti-aging wood-plastic composite material board can be used as an open-air table and chair, a stool, a picnic table, a flower box, a guardrail, a sign and the like to be widely applied to occasions such as a park, a court, municipal administration, a dock and the like.

Description

technical field [0001] The invention relates to a plastic-wood composite material, in particular to an aging-resistant plastic-wood composite material board and a preparation method thereof. Background technique [0002] Wood-plastic composite materials, also known as environmentally friendly wood, technological wood, and recycled wood, are made of resins such as polyethylene, polypropylene, and polystyrene, or recycled waste plastics and natural biological fibers such as wood powder, straw powder, and rice husk powder. It has the dual characteristics of wood and plastic, its appearance is close to natural wood, and it can be recycled. It fully embodies a series of advanced concepts such as resource utilization, environmental protection, and alternative products. It is an ideal green product. Its main features are: resource utilization of raw materials, plasticization of products, environmental protection in use, economical cost, recycling and regeneration. It has a wide r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L23/06C08L23/12C08L25/06C08L23/30C08K13/04C08K7/08C08K5/14C08K3/22C08K5/09B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/92704B29C2948/92895B29C2948/92904
Inventor 周才良吕战强
Owner G&S HUZHOU ENTERPRISES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More