Polyvinylidene fluoride composite membrane prepared through multilayer coextrusion tape casting method
A polyvinylidene fluoride, multi-layer co-extrusion technology, applied in the direction of flat products, household appliances, other household appliances, etc., can solve the problems of unfavorable industrial production, reduce the good quality of PVDF film, complicated operation process, etc., and achieve anti-ultraviolet performance. Excellent, large-scale continuous production, and high process controllability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] Add 1% silane coupling agent KH-550 into TiO2, and mix it with a high-speed mixer for 20 minutes at 80°C. Add 100g of treated TiO2 to 1000g of PVDF, mix evenly, extrude and granulate, and use it as material A. Add 20g of treated TiO2 and 400g of PMMA to 1000g of PVDF, mix evenly, extrude and granulate, and use as B material. Add material A and material B above to machine A and machine B of the three-layer co-extrusion equipment respectively; at the same time, add EVA resin to machine C of the three-layer co-extrusion equipment, and extrude and cast it into a film. The film thickness was 25 μm, and the film width was 1000 mm. . The film is A / B / C three-layer composite, and the thickness ratio of the three layers A:B:C is 1:1:1. The outer layer of the film is a PVDF protective layer, the middle is a modified layer, and the inner layer is an EVA adhesive layer. After testing, the tensile strength of the film is 40.2 MPa (ASTM D882-80, A method 22° C.), and the peel stre...
Embodiment 2
[0022] Add 1.2% silane coupling agent KH-550 to TiO2, and mix it with a high-speed mixer for 20 minutes at 80°C. Add 70g of treated TiO2 to 1000g of PVDF, mix evenly, extrude and granulate, and use it as material A. Add 15g of treated TiO2 and 430g of PMMA to 1000g of PVDF, mix evenly, extrude and granulate, and use as B material. Add material A and material B above to machine A and machine B of the three-layer co-extrusion equipment respectively; at the same time, add EVA resin to machine C of the three-layer co-extrusion equipment, and extrude and cast it into a film. The film thickness was 38 μm, and the film width was 800 mm. The film is A / B / C three-layer composite, and the thickness ratio of the three layers A:B:C is 1.5:2:1. The outer layer of the film is a PVDF protective layer, the middle is a modified layer, and the inner layer is an EVA adhesive layer, which has good adhesive performance. After testing, the tensile strength of the film is 44 MPa (ASTM D882-80, A m...
Embodiment 3
[0024] Add 1.5% silane coupling agent KH-550 to TiO2, and mix it with a high-speed mixer for 20 minutes at 80°C. Add 50g of treated TiO2 to 1000g of PVDF, mix evenly, extrude and granulate, and use it as material A. Add 20g of treated TiO2 and 450g of PMMA to 1000g of PVDF, mix evenly, extrude and granulate, and use as B material. The above-mentioned material A and material B are respectively added to machine A and machine B of the double-layer co-extrusion equipment, and the double-layer co-extrusion is cast into a film. The film thickness was 30 μm, and the film width was 500 mm. The film is an A / B double-layer composite, and the thickness ratio of the two layers A:B is 1:1.5. The outer layer of the film is a PVDF protective layer, and the inner layer is a PVDF modified layer, which has good adhesive properties. After testing, its tensile strength is 42.4MPa (ASTM D882-80, A method 22 ℃), and the surface tension of the inner layer is 38 dyne.
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com