Aluminium and aluminium alloy surface antiseptic treatment method and product prepared by same

An aluminum alloy surface, anti-corrosion treatment technology, applied in thin material treatment, metal material coating process, superimposed layer plating and other directions, can solve the problems of easy pitting corrosion, shortened service life of aluminum products, large environmental pollution, etc. To achieve good corrosion resistance and improve the effect of bonding force

Inactive Publication Date: 2012-07-11
HONG FU JIN PRECISION IND (SHENZHEN) CO LTD +1
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aluminum oxide protective film will be formed on the surface of aluminum alloy in the air. In the general atmospheric environment, the aluminum oxide film on the surface of aluminum alloy can effectively protect the aluminum alloy substrate, but in the moisture containing electrolyte, such as the ocean surface atmosphere environment, the surface of aluminum alloy is prone to pitting corrosion, which seriously damages the appearance of aluminum alloy products and shortens the service life of aluminum products
[0003] In order to improve the corrosion resistance of aluminum alloy, it is usually necessary to carry out surface film-forming treatment on the surface of aluminum alloy. The common treatment methods include anodic oxidation treatment, baking paint, etc., but these processes have great environmental pollution problems.
Although the vacuum coating (PVD) technology is a very environmentally friendly coating process, and can be coated with a variety of coatings and excellent wear resistance, but the surface of the aluminum alloy usually has many depressions or pores, and the PVD process deposited The film layer usually has a profiling structure on the surface of the substrate, and the film layer deposited in these depressions or voids is often thinner in other areas, so during use, the depressions or void areas are often more prone to pitting, making the film layer cannot effectively prevent the aluminum alloy substrate from being corroded

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium and aluminium alloy surface antiseptic treatment method and product prepared by same
  • Aluminium and aluminium alloy surface antiseptic treatment method and product prepared by same
  • Aluminium and aluminium alloy surface antiseptic treatment method and product prepared by same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] A preferred embodiment of the present invention, the aluminum and aluminum alloy surface anticorrosion treatment method comprises the following steps:

[0033] see figure 1 , providing an aluminum substrate 20 . The aluminum base 20 can be made of pure aluminum or aluminum alloy.

[0034] The aluminum substrate 20 is chemically degreased. Chemical degreasing involves immersing the aluminum substrate 20 in a 60-80°C degreasing solution for 30-60s. The degreasing solution used is containing 25-30g / L sodium carbonate (Na 2 CO 3 ), 20-25g / L trisodium phosphate (Na 3 PO 4 12H 2 O) and the aqueous solution of 1-3g / L emulsifying agent, wherein said emulsifying agent can use the emulsifying agent of trade name OP-10, and its main component is the condensate of alkylphenol and oxirane.

[0035] Alkali etching treatment is performed on the aluminum substrate 20 . The alkaline etching treatment step is to immerse the aluminum substrate 20 in an alkaline etching solution a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an aluminium and aluminium alloy surface antiseptic treatment method which comprises the following steps of: providing an aluminium matrix; carrying out chemical degreasing on the aluminium matrix; carrying out zincate treatment on the aluminium matrix to form a zinc layer on the aluminium matrix; and forming a ceramic coating consisting of a refractory compound on the zinc layer by a vacuum plating method. The invention provides an aluminium product prepared by the antiseptic treatment method.

Description

technical field [0001] The invention relates to a method for anticorrosion treatment of aluminum and aluminum alloy surfaces and products thereof. Background technique [0002] Aluminum alloy has the advantages of light weight and good heat dissipation performance, and is widely used in communication, electronics, transportation, construction, aerospace and other fields. In the air, an aluminum oxide protective film will be formed on the surface of aluminum alloy. In the general atmospheric environment, the aluminum oxide film on the surface of aluminum alloy can effectively protect the aluminum alloy substrate, but in the moisture containing electrolyte, such as the ocean surface atmosphere The surface of aluminum alloy is prone to pitting corrosion, which seriously damages the appearance of aluminum alloy products and shortens the service life of aluminum products. [0003] In order to improve the corrosion resistance of aluminum alloys, it is usually necessary to carry o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C28/00
CPCC23C28/3455C23C28/34C23C28/345C23C28/3225Y10T428/12535Y10T428/12549
Inventor 张新倍陈文荣蒋焕梧陈正士毛盾
Owner HONG FU JIN PRECISION IND (SHENZHEN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com