Coated piece and manufacturing method thereof

A manufacturing method and coating technology, applied in chemical instruments and methods, sputtering plating, ion implantation plating, etc., can solve problems such as shedding, discoloration, and inability to effectively prevent electrochemical corrosion of aluminum or aluminum alloy substrates

Inactive Publication Date: 2012-05-23
HONG FU JIN PRECISION IND (SHENZHEN) CO LTD +1
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, since the standard electrode potential of aluminum or aluminum alloy is very low, and the PVD decorative coating itself will inevitably have tiny pores, therefore, direct plating on the surface of aluminum or aluminum alloy substrates such as TiN layer, TiNO layer, TiCN lay...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coated piece and manufacturing method thereof
  • Coated piece and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] see figure 1 According to a preferred embodiment of the present invention, the covering member 10 includes an aluminum or aluminum alloy substrate 11 , an amorphous alloy layer 13 and a color layer 15 sequentially formed on the aluminum or aluminum alloy substrate 11 . The covering part 10 may be a covering part of 3C electronic products, and may also be parts of glasses frames, building parts, automobiles and other vehicles.

[0020] The amorphous alloy layer 13 is Fe 70 Cr 10 B 13 x 7 layer, wherein X is selected from any one of phosphorus (P), carbon (C) and silicon (Si). The thickness of the amorphous alloy layer is 2.0-3.0 μm.

[0021] The color layer 15 is a TiN layer with a thickness of 0.5-3.0 μm. It can be understood that the color layer 15 can also be a TiNO layer, a TiCN layer, a CrN layer, a CrNO layer, a CrCN layer or other decorative film layers with an anti-corrosion function.

[0022] Both the amorphous alloy layer 13 and the color layer 15 can be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a coated piece which comprises an aluminum or aluminum alloy substrate, an amorphous alloy layer and a colored layer with an anti-corrosion function, wherein the amorphous alloy layer and the colored layer are formed on the aluminum or aluminum alloy substrate in turn; the amorphous alloy layer is Fe70Cr10B13X7; and X is any one selected from phosphorus, carbon and silicon. The coated piece has excellent corrosion resistance and decorative appearance. The invention also provides a manufacturing method for the coated piece.

Description

technical field [0001] The present invention relates to a covering and a manufacturing method thereof. Background technique [0002] Vacuum coating technology (PVD) is a very environmentally friendly film-forming technology. The film layer formed by vacuum coating has the advantages of high hardness, high wear resistance, good chemical stability, firm combination with the substrate, and bright metal appearance. Therefore, vacuum coating is used on aluminum, aluminum alloy, magnesium, and magnesium alloys And stainless steel and other metal substrate surface decorative treatment field is more and more widely used. [0003] However, since the standard electrode potential of aluminum or aluminum alloy is very low, and the PVD decorative coating itself will inevitably have tiny pores, therefore, direct plating on the surface of aluminum or aluminum alloy substrates such as TiN layer, TiNO layer, TiCN layer, CrN layer, CrNO layer, CrCN layer or other PVD decorative coatings wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/02C23C14/06C23C14/35B32B9/04B32B15/00
Inventor 张新倍陈文荣蒋焕梧陈正士张满喜
Owner HONG FU JIN PRECISION IND (SHENZHEN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap