Method for preparing wear-resistant coating on surface of driving sheave race of elevator by laser cladding

A technology of wear-resistant coating and elevator traction, which is applied in laser welding equipment, coating, metal material coating technology, etc., can solve the problems that the process parameters cannot be adapted or not seen, and achieve the improvement of wear resistance and corrosion resistance and service life, good bonding performance, uniform effect of alloy coating

Active Publication Date: 2012-05-16
SHENYANG DALU LASER COMPLETE EQUIP
View PDF8 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for other specific equipment components, such as special structures such as elevator traction wheel grooves, the process parameters provided by the existing laser cladding process are obviously unable to adapt
[0014] According to the applicant's search and verification: there is no domestic precedent for using laser cladding technology to prepare wear-resistant coating on the surface of the elevator traction wheel groove, and there are no related reports abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The process of preparing a wear-resistant composite coating by laser rapid cladding on the surface of the traction wheel groove of the present invention includes the following process:

[0052] 1. Surface pretreatment

[0053] Use an angle grinder at room temperature to degrease and derust the processed parts. Use the coloring flaw detection method to inspect the upper and lower processing parts of the wheel groove, and it is required that the processing parts have no cracks, pores, inclusions and other defects;

[0054] 2. Selection of alloy powder and adjustment of automatic powder feeding device

[0055] The nickel-based alloy powder with good toughness, high strength and good compatibility with the matrix metallurgy is selected as the base layer, and the cobalt-based alloy powder with high wear resistance and matching with the friction performance of the steel wire rope is selected as the working layer, and the automatic powder feeding device is adjusted so that th...

Embodiment 2

[0079] The process of preparing a wear-resistant composite coating by laser rapid cladding on the surface of the traction wheel groove provided by the present invention includes the following process:

[0080] 1. Surface pretreatment

[0081] At room temperature, use an angle grinder to degrease and derust the processing parts, and use the coloring flaw detection method to inspect the processing parts above and below the wheel groove. It is required that the processing parts have no defects such as cracks, pores, inclusions, etc.;

[0082] 2. Selection of alloy powder and adjustment of automatic powder feeding device

[0083] The nickel-based alloy powder with good toughness, high strength and good compatibility with the matrix metallurgy is selected as the base layer, and the cobalt-based alloy powder with high wear resistance and matching with the friction performance of the steel wire rope is selected as the working layer, and the automatic powder feeding device is adjusted...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a wear-resistant coating on the surface of a driving sheave race of an elevator by laser cladding. A rendering transition layer with good toughness, which is clad on the surface of the race and forms metallurgical bonding with a base body, is rapidly scanned by laser through high-power laser; and a wear-resistant cobalt-base alloy which has good corrosive resistance and a frication coefficient in fit with that of a steel wire rope is prepared on a rendering alloy surface through laser cladding. The method is characterized by comprising the following special steps of: firstly, pre-treating the surface of the race; secondly, selecting alloy powder and an automatic powder sending device; thirdly, carrying out the laser cladding on the rendering alloy and the cobalt-base alloy powder with the frication coefficient in fit with that of the steel wire rope so that a wear-resistant coating with the thickness of 0.5-1.2 mm is formed on the surface of the race; and finally, carrying out flaw detection after cladding. The method provided by the invention has the characteristics of high productivity, lower energy consumption, small machining allowance of a cladding layer, high field, low combined cost and the like.

Description

technical field [0001] The invention relates to a wear-resistant and anti-corrosion method for the surface of conveying equipment components, in particular to a method for preparing a wear-resistant coating on the surface of an elevator traction wheel groove by adopting laser cladding technology, which belongs to the technical field of laser cladding. Background technique [0002] The elevator traction sheave is a very important part of the elevator. The main form of damage to the elevator traction sheave is wear and corrosion, and the uneven wear between the grooves often causes the failure of the entire part, which eventually leads to the scrapping of the equipment; because the elevator traction sheave has to bear the load of the car, load capacity, counterweight and other devices All dynamic and static loads require the traction sheave to have high strength, good toughness, wear resistance and impact resistance, so QT60-2 nodular cast iron is often used as the material. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C24/10B23K26/34
Inventor 陶兴启黄旭东崔忠宝王悦斌
Owner SHENYANG DALU LASER COMPLETE EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com