Preparation method for composite oxide carrier

A composite oxide and oxide technology, applied in catalyst carriers, chemical instruments and methods, chemical/physical processes, etc., can solve problems affecting the physical properties and surface properties of carriers, rapid precipitation of zirconia or titania, and different particle sizes. problem, to achieve the effect of easy vulcanization, easy reduction, and simple production process

Active Publication Date: 2012-05-16
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 50 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the zirconium or titanium in the above method is added after the alumina is gelled, and the pH value of the alumina is in the alkaline range, while the zirconium-containing solution or the titanium-containing solution is acidic. When the two are mixed, it is easy to cause zirconia or titanium oxide Rapid precipitation, different particle sizes, re-peptization of the original alumina precipitation, wide particle size distribution of alumina, which in turn affects the physical and surface properties of the carrier

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for composite oxide carrier
  • Preparation method for composite oxide carrier

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Mix 1000ml 2mol / L aluminum nitrate with 22ml silica gel (containing SiO 2 25wt%), mixed with ammonia water, adjusted to a pH value of 8.5, and reacted at 60° C., and the resulting precipitate was washed and filtered to obtain a wet filter cake. 10g / 100ml of Zr(NO 3 ) 4 The solution is mixed with a theoretical amount of ammonium tartrate to obtain a complex solution. The wet filter cake was added into the complex solution and stirred vigorously, heated to 40°C for aging for 2 hours, suction filtered, and the filter cake was dried at 120°C for 3 hours and pulverized to obtain a composite oxide dry glue. The composite oxide dry glue was calcined at 600°C for 3 hours to obtain a composite oxide, in which the content of zirconia was 10 wt%, and the content of silicon oxide was 5 wt%. The main properties are listed in Table 1.

[0035] Take 131g of composite oxide dry glue, 13.9g of SB powder, add 3g of scallop powder, 5ml of dilute nitric acid, knead, extrude, dry at 120°...

Embodiment 2

[0037] Mix 1 mol / L aluminum sulfate and 1 mol / L sodium metaaluminate in parallel, adjust the pH value to 7.0, and react at 50°C. The resulting precipitate is washed and filtered to obtain a wet filter cake. 20g / 100ml of Zr(NO 3 ) 4 The solution is mixed with a theoretical amount of ammonium tartrate to obtain a complex solution. The rest are the same as in Example 1 to obtain the composite oxide dry glue. The composite oxide dry glue was calcined at 600°C for 3 hours to obtain a composite oxide, in which the content of zirconia was 50 wt%, and its main properties are listed in Table 1.

[0038] Take 118g of composite oxide dry glue, 27.8g of SB powder, add 3g of scallop powder, 3ml of dilute nitric acid and 2ml of acetic acid, knead, extrude, dry at 120°C for 3 hours, and roast at 600°C for 3 hours to obtain a composite oxide carrier . Its main properties are listed in Table 2.

Embodiment 3

[0040] Mix 1000ml 2mol / L aluminum nitrate with 22ml silica gel (containing SiO 2 25 wt%), mixed with ammonia water, adjusted to a pH of 7.5, reacted at 60° C. and aged for 3 hours, and the resulting precipitate was washed and filtered to obtain a wet filter cake. 10g / 100ml of TiCl 4 The solution is mixed with a theoretical amount of EDTA to obtain a complex solution. The wet filter cake was added into the complex solution and stirred vigorously, filtered with suction, and the filter cake was dried at 120° C. for 3 hours and pulverized to obtain the composite oxide dry glue. The composite oxide gel was calcined at 600° C. for 3 hours to obtain a composite oxide, wherein the content of titanium oxide was 10 wt %, and the content of silicon oxide was 5 wt %. The main properties are listed in Table 1.

[0041] Take 141g of composite oxide dry glue, 13.9g of SB powder, add 3g of scallop powder, 5ml of dilute nitric acid, knead, extrude, dry at 120°C for 3 hours, and bake at 600°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a preparation method for a composite oxide carrier. According to the method of the present invention, a composite oxide dry glue is prepared by the following steps, wherein the steps comprise: firstly preparing an aluminum hydroxide wet filter cake and an aqueous solution containing an IVB group metal complex; adding the wet filter cake to the complex solution, andstrongly stirring; carrying out filtering and drying to obtain the composite oxide dry glue. With the composite oxide dry glue prepared by the method, most of the IVB group metal oxide can be distributed on the surface of aluminum oxide so as to reduce the influence on the pore structure of the aluminum oxide, improve the assistant catalysis effect of the IVB group metal oxide, and improve the pore structure and the surface performance of the composite oxide carrier. In addition, with the present invention, the sulfurization performance of the catalyst adopting the composite oxide carrier as the carrier can be improved, and the loaded active metal is easy to reduce.

Description

technical field [0001] The invention relates to a preparation method of a composite oxide carrier, in particular to a preparation method of a composite oxide carrier used for preparing a hydrogenation refining catalyst. Background technique [0002] The preparation process of the alumina support is simple, the specific surface area is high, the mechanical strength is good, and the pore size is suitable. It is one of the most widely used catalyst supports at present. Inactive species, such as nickel-aluminum spinel, are less likely to form highly reactive type II active phases. Therefore, the preparation and modification of alumina carriers and the preparation of aluminum-containing composite oxides have always been the research direction of scientists. At present, Group IVB metal oxides (zirconia, titania) have shown unique catalytic activity as supports or catalysts in the field of catalysis due to their simultaneous acidic and basic surface centers, oxidizing and reducing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J32/00B01J21/06B01J35/10B01J27/19C10G45/08
Inventor 徐黎明高玉兰李崇慧陈光
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com