Reactive extrusion matte agent, low gloss PC/ABS alloy and its preparation method

A reactive extrusion, low gloss technology, applied in the field of PC/ABS alloy and its preparation, can solve the problems of large fluctuation of mechanical properties, poor gloss stability, chemical properties deterioration, etc., achieve good mechanical properties, excellent matteness, reduce material cost effect

Active Publication Date: 2012-03-21
SHANGHAI KUMHO SUNNY PLASTICS
View PDF8 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. Surface embossing, that is, skin texture treatment can achieve good results, but sometimes it cannot meet the required requirements, and a separate embossing link needs to be added, which increases the cost
At the same time, during subsequent use, the pattern may be removed due to wear and tear, causing the gloss to appear again
[0006] 2. Add fillers, such as titanium dioxide, silicon dioxide, silicate or aluminate and other similar inert minerals. Although it can also achieve the purpose of eliminating the surface gloss of molded products, a large amount of fillers must be added to achieve a certain degree of matteness. , which greatly reduces the physical and mechanical properties of molded products or leads to the deterioration of chemical properties, especially the great loss of material toughness
[0008] 4. Adding high-molecular polymers with reactive functional groups, such as PS-g-GMA, etc., due to poor reactivity when improving the gloss of products, requires a high amount of addition, low efficiency, and has a certain impact on mechanical properties.
[0014] However, these known technical solutions also have some shortcomings: poor gloss stability, large fluctuations in mechanical properties and high cost, which limit the application of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reactive extrusion matte agent, low gloss PC/ABS alloy and its preparation method
  • Reactive extrusion matte agent, low gloss PC/ABS alloy and its preparation method
  • Reactive extrusion matte agent, low gloss PC/ABS alloy and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] (1) Prepare materials according to the following components and weight percentage content:

[0050] Low-density polyethylene resin 96%, dicumyl peroxide 4%;

[0051] (2) First heat the dicumyl peroxide and control the temperature at 60-65°C to make it liquid;

[0052] (3) Pass low-density polyethylene resin (weight average molecular weight 40,000) through a twin-screw extruder, add dicumyl peroxide in a side-feeding manner, melt and extrude at a temperature of 160-200°C, and cool and granulate , to obtain the reactive extrusion matte agent.

Embodiment 2

[0054] (1) Prepare materials according to the following components and weight percentage content:

[0055] Linear low density polyethylene resin 97.5%, benzoyl peroxide 2.5%;

[0056] (2) First heat the benzoyl peroxide and control the temperature at 60-70°C to make it liquid;

[0057](3) Pass linear low-density polyethylene resin (weight average molecular weight 250,000) through a twin-screw extruder, add benzoyl peroxide in a side-feeding manner, melt and extrude at a temperature of 200-250°C, and cool and granulate , to obtain the reactive extrusion matte agent.

Embodiment 3

[0059] (1) Prepare materials according to the following components and weight percentage content:

[0060] High-density polyethylene resin 99.5%, di-tert-butyl peroxide 0.5%;

[0061] (2) First heat the di-tert-butyl peroxide and control the temperature at 70-80°C to make it liquid;

[0062] (3) Pass high-density polyethylene resin (weight average molecular weight 300,000) through a twin-screw extruder, add ditertbutyl peroxide in a side-feeding manner, melt and extrude at a temperature of 180-240°C, and cool and granulate , to obtain the reactive extrusion matte agent.

[0063] Preparation of Low Gloss PC / ABS Alloy Material

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a reactive extrusion matte agent, a low gloss PC / ABS alloy by using the reactive extrusion matte agent and a preparation method thereof. The low gloss PC / ABS alloy comprises the following components of: by weight, 20-80% of a polycarbonate resin, 5-50% of an ABS resin, 5-40% of a styrene-acrylonitrile resin, 1-10% of the reactive extrusion matte agent and 0.1-1.5% of a processing aid. The preparation method provided by the invention comprises the following steps of: premixing the above materials in a high-speed mixer for 3-10 minutes, allowing the premix to enter intoa double screw extruder for melting extrusion at the temperature of 230-300 DEG C, cooling, followed by granulation to obtain the low gloss PC / ABS alloy. In comparison with the prior art, the preparation method provided by the invention has advantages of reasonable technology, low cost, high efficiency of reducing gloss and stable product performance.

Description

technical field [0001] The invention relates to a PC / ABS alloy and a preparation method thereof, in particular to a reaction extrusion matting agent, [0002] Low gloss PC / ABS alloy and its preparation method. Background technique [0003] Among the various applications of the composition of polycarbonate and styrenic resin, some fields require a low-gloss surface. These application fields are mainly automobiles, decorations, electronic appliances, etc., such as automotive interior parts, and attention should be paid to the design The reflectivity of the instrument panel should not only improve the visibility of the instrument, but also reduce glare through the diffuse reflection method of the cover, and prevent the high points on the instrument panel from forming a reflected image on the inner surface of the windshield, so as not to disturb the driver Therefore, the surface of the instrument panel must be matte or matte to obtain a comfortable and safe driving feeling. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08K5/14B29B9/06B29C47/92C08L69/00C08L55/02C08L25/12B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 李文强李强杨春华罗明华辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com