Water-based matte finishing varnish as well as preparation method and application thereof

A finishing varnish and matte technology, applied in the direction of coating, etc., can solve the problems of two-component coatings, such as difficulty in construction, matte stain resistance, short open period, etc., to achieve excellent matteness, convenient construction, Excellent film-forming performance

Pending Publication Date: 2021-10-08
ASIA CUANON TECH SHANGHAI +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although two-component water-based coatings have better resistance and better stain resistance than one-component water-based coatings, the two-component coatings have disadvantages such as difficult construction, short open period, and certain toxicity, which limit Its large-scale application, and in many patents of stain-resistant coatings, can only achieve glossy effects, that is, the gloss at 60° angles is above 70°, and it does not solve the problem of matte stain resistance in actual household applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based matte finishing varnish as well as preparation method and application thereof
  • Water-based matte finishing varnish as well as preparation method and application thereof
  • Water-based matte finishing varnish as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The present embodiment provides a kind of water-based matte finish varnish, according to the total parts by weight of each component of the water-based matte finish varnish is 100 parts by weight, and the water-based matte finish varnish comprises the following components according to parts by weight: 65 parts of silicone acrylic resin, 0.3 parts of polysiloxane (polydimethylsiloxane), 2 parts of wax dispersion, 0.1 part of defoamer (BYK-093), 3 parts of film-forming aid (propylene glycol ether), 0.1 part of antifreeze (ethylene glycol), 0.1 part of thickener (ethoxylated polyurethane water-soluble polymer) and water to 100 parts.

[0051] The preparation method of above-mentioned water-based matte finish varnish comprises the steps:

[0052] (1) Mix the silicone acrylic resin and the defoamer at 500 rpm for 5 minutes to obtain the first mixed solution;

[0053] (2) Mix the film-forming aid, antifreeze and water for 3 minutes to obtain the second mixed solution;

[00...

Embodiment 2

[0056] The present embodiment provides a kind of water-based matte finish varnish, according to the total parts by weight of each component of the water-based matte finish varnish is 100 parts by weight, and the water-based matte finish varnish comprises the following components according to parts by weight: 65 parts of silicone acrylic resin, 0.3 parts of polysiloxane (polyether-polydimethylsiloxane copolymer), 5 parts of wax dispersion, 0.5 parts of defoamer (BYK-A550), 6 parts of coalescent (tripropylene glycol n-butyl ether), 1 part of antifreeze (propylene glycol), 0.5 parts of thickener (ethoxylated polyurethane water-soluble polymer) and water to 100 parts.

[0057] The preparation method of above-mentioned water-based matte finish varnish comprises the steps:

[0058] (1) Mix the silicone acrylic resin and the defoamer at 500 rpm for 5 minutes to obtain the first mixed solution;

[0059] (2) Mix the film-forming aid, antifreeze and water for 3 minutes to obtain the se...

Embodiment 3

[0062] The present embodiment provides a kind of water-based matte finish varnish, according to the total parts by weight of each component of the water-based matte finish varnish is 100 parts by weight, and the water-based matte finish varnish comprises the following components according to parts by weight: 70 parts of silicone acrylic resin, 0.5 parts of polysiloxane (polydimethylsiloxane and polyether-polydimethylsiloxane copolymer with a mass ratio of 1:1), 2 parts of wax dispersion, defoaming 0.5 parts of agent (TEGO-810), 4 parts of coalescent (hexanediol butyl ether acetate), 0.5 parts of antifreeze (ethylene glycol monobutyl ether), 0.3 parts of thickener (ethoxylated polyurethane water-soluble polymer matter) parts and water to 100 parts.

[0063] The preparation method of above-mentioned water-based matte finish varnish comprises the steps:

[0064] (1) Mix the silicone acrylic resin and the defoamer at 500 rpm for 5 minutes to obtain the first mixed solution;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based matte finishing varnish as well as a preparation method and application thereof. The water-based matte finishing varnish comprises the following components in parts by weight: 65-70 parts of silicone acrylic resin, 0.3-0.5 part of polysiloxane, 2-5 parts of wax dispersion, 0.1-26 parts of auxiliaries and the balance of water, totaling 100 parts. The water-based matte finishing varnish has excellent low-temperature (5 DEG C) film-forming performance on the premise that the addition amount of a coalescing agent is small and matting powder does not need to be added, has excellent matte property, anti-doodling property, stain resistance and scratch resistance after being formed into a film, is light in smell, ensures the low-temperature film-forming effect and is convenient for construction.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based matte finish varnish and a preparation method and application thereof. Background technique [0002] The technical requirements of architectural coatings are one base and two sides, while the traditional latex paint topcoats are poor in stain resistance, graffiti resistance and scratch resistance. Even if the score of stain resistance has passed the standard score, there will still be stain marks on the surface of the paint film, and the stain resistance is poor. Compared with traditional architectural coatings, the current interior latex paint has improved its stain resistance to a certain extent. However, for some stains, it may be wiped off immediately in a short time, but after more than two hours, it is almost difficult to wipe it off. Leaves very visible marks and has limited stain resistance. In addition, the coating formed by architectural coatings is gen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D7/65
CPCC09D143/04C09D7/65C08L2205/03C08L83/04C08L91/06C08L83/12
Inventor 王志鑫裴道海桂中秀李勇李金钟
Owner ASIA CUANON TECH SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com