Polyvinyl chloride composite material and preparation method thereof

A technology of polyvinyl chloride and composite materials, applied in the field of polyvinyl chloride composite materials and its preparation, to achieve the effects of both toughness, good cold resistance, and expanded temperature range

Inactive Publication Date: 2011-01-19
KANGTAI PLASTIC SCI & TECH GRP
View PDF7 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Thermoplastic polyurethane (TPU) elastomer is a non-toxic and environmentally friendly polymer with high strength, good toughness, wear resistance, cold resistance, temperature resistance, oil resistance, water resistance, aging resistance, and It has many excellent functions such as antibacterial, anti-mildew, anti-ultraviolet and energy release. There are no reports of adding thermoplastic polyurethane elastomers to polyvinyl chloride.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl chloride composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Raw material composition ratio is as follows:

[0035] 100 parts of polyvinyl chloride,

[0036] 25 parts of polyester thermoplastic polyurethane elastomer rubber (TPU),

[0037] Impact modifier MBS resin 12 parts,

[0038] 10 parts of nano active calcium carbonate,

[0039] 4 parts of calcium zinc stabilizer,

[0040] 2 parts epoxy soybean oil,

[0041] 2.5 parts of titanium dioxide,

[0042] 0.8 parts of stearic acid,

[0043] 0.3 parts of polyethylene wax.

[0044] The preparation method of polyvinyl chloride composite material comprises the following steps:

[0045] 1. Ingredients: Weigh all kinds of raw materials according to the above dosage.

[0046] 2. Mixing: first add polyvinyl chloride, nano-active calcium carbonate, stabilizer and lubricant into the high-speed mixer.

[0047] 3. High mixing: Start the high-speed mixer, and when the temperature reaches 85-95°C, add polyester thermoplastic polyurethane elastomer rubber (TPU) for pre-plasticization tre...

Embodiment 2

[0051] Raw material composition ratio is as follows:

[0052] 100 parts of polyvinyl chloride,

[0053] 25 parts of polyester thermoplastic polyurethane elastomer rubber (TPU),

[0054] Impact-resistant acrylate ACR401 10 parts,

[0055] 15 parts of light active calcium carbonate,

[0056] 5 parts of calcium stearate,

[0057] 2 parts of calcium zinc stabilizer,

[0058] 2 parts epoxy soybean oil,

[0059] Titanium dioxide 1.5 parts

[0060] 0.3 parts of polyethylene wax

[0061] 0.8 parts of stearic acid.

[0062] Its preparation process is with embodiment one. Its main physical properties are listed in Table 1.

Embodiment 3

[0064] Raw material composition ratio is as follows:

[0065] 125 parts of polyvinyl chloride,

[0066] 30 parts of polyester thermoplastic polyurethane elastomer rubber (TPU),

[0067] Impact modifier ethylene-vinyl acetate copolymer EVA15 parts,

[0068] 10 parts of nano active calcium carbonate,

[0069] 5 parts of barium stearate,

[0070] 2 parts of calcium zinc stabilizer,

[0071] 2 parts epoxy soybean oil,

[0072] 1.5 parts of titanium dioxide,

[0073] 0.3 parts of polyethylene wax,

[0074] 0.8 parts of stearic acid.

[0075] Its preparation process is with embodiment one. Its main physical properties are listed in Table 1.

[0076] Table 1

[0077]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of polymer composite materials and in particular relates to a polyvinyl chloride composite material and a preparation method thereof. The invention aims to solve the technical problem of providing a cold-resistant, heat-resistant and high-impact polyvinyl chloride composite material. The polyvinyl chloride composite material comprises 80-145 parts of polyvinyl chloride and 20-35 parts of thermoplastic polyurethane elastomer rubbers by weight. By adopting the thermoplastic polyurethane elastomer rubbers to modify polyvinyl chloride, the polyvinyl chloride composite material expands the applicable temperature range of the polyvinyl chloride materials, ensures the product to have strength, rigidity and toughness, has good cold resistance and heat resistance and is suitable for manufacturing pipes or profiles.

Description

technical field [0001] The invention belongs to the technical field of polymer composite materials, and in particular relates to a polyvinyl chloride composite material and a preparation method thereof. Background technique [0002] Polyvinyl chloride is a general-purpose plastic with low price, corrosion resistance and low energy consumption, which is widely used. However, its hard products have poor impact resistance and are prone to brittle cracks. At the same time, the plasticizer is easy to migrate, which reduces the material performance; moreover, PVC has disadvantages such as poor thermal stability, low cold resistance, low elasticity, and low comprehensive strength. limit its scope of application. [0003] Patent application number [201010191968.9] mentions a cold-resistant polyvinyl chloride plastic and its preparation method. The invention proposes to add cold-resistant plasticizers dioctyl sebacate (DOS) and dioctyl adipate (DOA) method to improve the cold resis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L75/04C08L75/06B29B9/06
Inventor 林云青张文霖郝洪波
Owner KANGTAI PLASTIC SCI & TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com