Method for antiseptic treatment of marine climate resistant engineering component

A marine climate and anti-corrosion treatment technology, applied in hot-dip plating process, metal material coating process, coating, etc., can solve the problems of surface shape, difficult size control, difficult to handle large-area parts, high cost of vapor deposition, etc., to achieve The effect of low material cost, reduced mechanical property mismatch, and eliminated risk of corrosion

Active Publication Date: 2010-06-23
JIANGSU LINLONG NEW MATERIALS
View PDF0 Cites 54 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the plating layer of electroplating and electroless plating is too thin, generally only a few microns, and the hardness of the coating itself is too low to resist the erosion of particle-containing airflow
Although thermal spraying has the advantages of large coating thickness and easy operation, it is difficult to control the surface shape and size of the protected parts, which is basically not suitable for the research target parts of this project.
However, the cost of vapor deposition is high, it is difficult to deal with large-area parts, and the thickness of the coating itself is thin, there are pinholes and Cl in salt spray - Rapid corrosion occurs under the attack of
In addition, the common problems of the above-mentioned means are that the above-mentioned technical means are complex in process and high in production cost, and more seriously, the coating layer obtained by using the above-mentioned technical means is easy to peel off under the synergistic effect of environment and stress. Lose the protective effect, therefore, research and development of effective new anti-corrosion technology has become an urgent need for the current industrial development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for antiseptic treatment of marine climate resistant engineering component
  • Method for antiseptic treatment of marine climate resistant engineering component

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050](1) After the parts are cleaned and degreased, they are treated with pickling and rust removal, and rinsed with deionized water.

[0051] (2) Etch the degreasing and rust-removing parts in a mixed solution of hydrochloric acid HCl 94% (volume fraction) + hydrofluoric acid HF 6% (volume fraction), at room temperature for 1 minute, and rinse with deionized water.

[0052] (3) Activation treatment in a mixed solution of ethylene glycol, acidic ammonium fluoride, nickel chloride, boric acid, lactic acid, and acetic acid at a temperature of 40°C for 40 minutes, rinsed with deionized water, and dried.

[0053] (4) Put the parts treated in (1) to (3) into the atmosphere protection furnace, and preheat at 500°C for 20 minutes.

[0054] (5) In the atmosphere protection melting furnace, immerse the preheated steel parts in the plating solution for 1 minute, and rotate the parts during the immersion process.

[0055] (6) Put the immersion-plated parts into a vacuum furnace, keep w...

Embodiment 2

[0058] (1) After the parts are cleaned and degreased, they are treated with pickling and rust removal, and rinsed with deionized water.

[0059] (2) The parts after degreasing and derusting are etched in a mixed solution of hydrochloric acid HCl 95% (volume fraction) + hydrofluoric acid HF 5% (volume fraction) at room temperature for 2 minutes, and rinsed with deionized water.

[0060] (3) Activation treatment in a mixed solution of ethylene glycol, acidic ammonium fluoride, nickel chloride, boric acid, lactic acid, and acetic acid at a temperature of 50°C for 35 minutes, rinsed with deionized water, and dried.

[0061] (4) Put the parts treated in (1) to (3) into the atmosphere protection furnace, and preheat at 600°C for 15 minutes.

[0062] (5) In the atmosphere protection melting furnace, immerse the preheated steel parts in the plating solution for 3 minutes, and rotate the parts during the immersion process.

[0063] (6) Put the immersion-plated parts into a vacuum furn...

Embodiment 3

[0066] (1) After the parts are cleaned and degreased, they are treated with pickling and rust removal, and rinsed with deionized water.

[0067] (2) The parts after degreasing and derusting are etched in a mixed solution of hydrochloric acid HCl 96% (volume fraction) + hydrofluoric acid HF4% (volume fraction) at room temperature for 3 minutes, and rinsed with deionized water.

[0068] (3) Activation treatment in a mixed solution of ethylene glycol, acidic ammonium fluoride, nickel chloride, boric acid, lactic acid, and acetic acid at a temperature of 60°C for 30 minutes, rinsed with deionized water, and dried.

[0069] (4) Put the parts treated in (1) to (3) into the atmosphere protection furnace, and preheat at 650°C for 10 minutes.

[0070] (5) In the atmosphere protection melting furnace, immerse the preheated steel parts in the plating solution for 5 minutes, and rotate the parts during the immersion process.

[0071] (6) Put the immersion-plated parts into a vacuum furna...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for antiseptic treatment of marine climate resistant engineering component, comprising: 1. carrying out rust removal treatment on components; 2. carrying out etching treatment to components; 3. carrying out surface activation treatment on the components; 4. putting components into a special atmosphere oven to preheat; 5. dipping the preheated components into plating solution to dip, wherein the components rotate in the dipping process; 6. carrying out diffusion treatment; and 7. adopting coating for seal treatment. Components treated by the method of the invention can endow full corrosion resistance and washing corrosion resistance under the condition of marine climate.

Description

technical field [0001] The invention relates to a method for carrying out anti-corrosion treatment of marine climate-resistant engineering parts. Background technique [0002] With the rapid development of science and technology, more and more engineering equipment is used in offshore and marine environments. According to the ISO 9225 environmental evaluation standard, its service conditions are generally >C5, which belongs to extremely harsh environments. The ambient atmosphere is rainy, high temperature, salty spray and strong wind flow. The exposed parts will be subjected to the combined effects of strong atmospheric corrosion, electrochemical corrosion and airflow erosion. The service life of various steel structures is much lower than that of ordinary inland outdoor environment. For example, wind power generation equipment, one of the typical engineering equipment serving in marine climate conditions, because wind power generators use wind energy to generate electri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C2/04C23C2/02C23C2/26
Inventor 冯立新张敏燕缪强
Owner JIANGSU LINLONG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com