Grinding technique for aluminum alloy drum of external-drum type plate-making machine

A grinding process and plate-making machine technology, applied in optics, anodizing, instruments, etc., can solve the problems of reducing grinding productivity, increasing grinding wheel clogging, and low melting point, so as to improve processing accuracy and smoothness, simplify procedures, and reduce costs Effect

Active Publication Date: 2010-03-03
HANGZHOU CRON MACHINERY & ELECTRONICS CO LTD
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Low hardness and strength: the highest hardness of aluminum alloy is HB110-120, and the maximum tensile strength is generally 20-30kg / cm 2
Due to the low hardness, the ability of the material to resist plastic deformation or scratches is poor, and it is easy to scratch and bruise the surface of the workpiece during grinding.
[0004] 2. Large plasticity, plastic adhesion occurs during the grinding process, blocking the surface of the grinding wheel; at the same time, the melting point of the aluminum alloy is low (660-780 ° C), and the metal on the surface melts and adheres to the surface of the grinding wheel at high temperatures in the grinding area. Increased wheel clogging due to hot melt adhesion
[0005] 3. Large coefficient of linear expansion: under the action of grinding heat, it is easy to cause deformation of aluminum alloy workpiece, thus affecting the grinding accuracy of workpiece surface
[0006] 4. Low grinding efficiency: In order to overcome the thermal deformation of the aluminum alloy workpiece during grinding, reduce the adhesion and clogging of the grinding wheel surface, and ensure the quality of the processed surface, the number of dressings must be increased, thus reducing the grinding productivity
[0007] Because the grinding process of the optical drum of the external drum platemaking machine often fails to meet the precision requirements, the grinding process has never been used to process the optical drum in the industry, and only the turning process is usually used to make it; but because the accuracy level of the lathe is lower than For grinding machines, it is necessary to ensure that the dimensional accuracy of the diameter is within 0.02mm and the cylindricity is within 0.01mm, which has high requirements for the accuracy level of the lathe and the skill of the operator, which also has a certain impact on the product cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The grinding process of the aluminum alloy light drum of the external drum plate-making machine is carried out in sequence according to the following steps:

[0034] 1) Cover and seal screws made of non-aluminum materials with silica gel.

[0035] 2) Carry out conventional metal machining and treatment; including rough turning, high temperature aging treatment, semi-finishing turning, medium temperature aging treatment, assembly and milling, low temperature aging treatment and finish turning; the temperature of high temperature aging treatment is 360°C, time 28h; the temperature of the medium temperature aging treatment is 230°C, and the time is 27h; the temperature of the low temperature aging treatment is 130°C, and the time is 28h.

[0036] 3) Surface cleaning treatment and anodic oxidation pretreatment;

[0037] Surface cleaning treatment is: degreasing and degreasing treatment; the treatment solution is one or more mixed solutions of sulfuric acid, phosphoric acid...

Embodiment 2

[0053] Embodiment 2 is basically the same as Embodiment 1; the difference only lies in:

[0054] 1. The temperature of high temperature aging treatment is 400°C, time 20h; the temperature of medium temperature aging treatment is 270°C, time 21h; the temperature of low temperature aging treatment is 180°C, time 20h.

[0055] 2. The surface cleaning treatment is: degreasing and degreasing treatment; the treatment liquid is:

[0056] HNO 3 (nitric acid) 10g / L

[0057] HF (hydrofluoric acid) 8g / L

[0058] Sodium persulfate 7g / L

[0059] Sodium dodecylbenzenesulfonate (surfactant) 3g / L (all kinds of surfactants can be used,

[0060] Such as anionic surfactants, cationic surfactants

[0061] zwitterionic surfactant, nonionic surfactant)

[0062] Processing temperature 60°C

[0063] The processing time is 100s.

[0064] The concentration of NaOH (sodium hydroxide) in the alkaline treatment solution before anodic oxidation is 30g / L, the complexing agent added is sodium gluconate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to grinding technique for an aluminum alloy drum of an external-drum type plate-making machine. The technical problem needed to be solved is as follows: the provided technique can effectively process the drum of the plate-making machine, and have the characteristics of high processing precision, good quality, high working efficiency and convenient processing. The technical scheme is that the grinding technique for the aluminum alloy drum of the external-drum type plate-making machine is implemented in sequence according to the following steps of: 1) implementing conventional metal machinery processing to basically shape the profile of the drum; 2) implementing the cleaning processing of the surface of the drum and pre-processing of anodic oxidation; 3) implementing the processing of hard anodic oxidation on the surface of the drum to lead the thickness of a hard oxidation layer to achieve 0.03-0.05mm and lead the rigidity to achieve HV390-410; and 4) grinding until the requirements are met. Rough turning, high temperature aging, semi-fine turning, middle temperature aging, assembling and milling, low temperature aging and fine turning are implemented in the step 1) in sequence; and the surface cleaning processing in the step 2) refers to the processing of degreasing and oil removing.

Description

technical field [0001] The invention relates to a processing technology of CTP equipment components, in particular to a grinding processing technology of an aluminum alloy light drum of an external drum type plate making machine. Background technique [0002] In CTP (computer to plate) equipment, the light drum of the plate making machine is usually made of aluminum alloy; the precision of the light drum is high, and the cylindricity should be within 0.01mm, such as the diameter of the light drum is 343.5mm, and the length is 1195mm. The optical drum also requires that the cylindricity should be within 0.01mm, which is difficult to process for the characteristics of aluminum alloy; the reasons are: [0003] 1. Low hardness and strength: the highest hardness of aluminum alloy is HB110-120, and the maximum tensile strength is generally 20-30kg / cm 2 . Due to the low hardness, the material has poor ability to resist plastic deformation or scratches, and it is easy to scratch a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G03G5/00C25D11/04C25D11/08C22F1/04C23G1/12
Inventor 项建龙卢伟毅
Owner HANGZHOU CRON MACHINERY & ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products