Malleable high chromium ferritic alloy

A high-chromium ferrite and alloy technology, applied in the field of metal functional materials, can solve the problems of high brittle transition temperature, notch sensitivity, harmful ferritic stainless steel, etc.

Active Publication Date: 2009-09-09
JIANGSU XIHU SPECIAL STEEL
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ferrite exists C and N interstitial elements in stainless steel to strongly form and stabilize austenite, which is very harmful to ferritic stainless steel, mainly because the diffusion speed of C and N elements in ferritic stainless steel is fast, about 600 times that of the ferritic stainless steel. During the cooling process after high temperature heating, carbon and nitride will precipitate out, resulting in ferritic stainless steel brittleness at 475 ° C, high temperature brittleness, low room temperature toughness, high brittle transition temperature, and sensitivity to notches, etc. shortcoming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A ductile iron-chromium-molybdenum ferrite alloy, the mass percent of its chemical composition is: C0.001, N0.005, Si0.05, Mn0.05, Cr31, Mo0.12, P0.014, S0.003, The balance is Fe and unavoidable impurities, and the stability ratio Mo / (C+N) is 20.

Embodiment 2

[0045] A ductile iron-chromium-molybdenum ferrite alloy, the mass percent of its chemical composition is: C0.001, N0.004, Si0.04, Mn0.04, Cr30, Mo0.05, P0.012, S0.002, The balance is Fe and unavoidable impurities, and the stability ratio Mo / (C+N) is 10.

Embodiment 3

[0047] A ductile iron-chromium-molybdenum ferrite alloy, the mass percent of its chemical composition is: C0.001, N0.003, Si0.03, Mn0.03, Cr29, Mo0.032, P0.010, S0.002, The balance is Fe and unavoidable impurities, and the stability ratio Mo / (C+N) is 8.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a malleable high chromium ferritic alloy, which comprises the following chemical compositions according to weight percentage: less than or equal to 0.001 percent of C, less than or equal to 0.001 percent of N, less than or equal to 0.05 percent of Si, less than or equal to 0.05 percent of Mn, 29 to 31 percent of Cr, less than or equal to 0.12 percent of Mo, less than or equal to 0.014 percent of P, less than or equal to 0.003 percent of S, and the balance of Fe and inevitable impurities. The stability ratio of the Mo to (the C and the N) is 8 to 20. The malleable high chromium ferritic alloy has excellent corrosion resistance and toughness.

Description

technical field [0001] The invention relates to metal functional materials, in particular to a high-chromium ferrite alloy with excellent toughness. Background technique [0002] In recent years, the price of rare metal nickel has soared, which has doubled the price of austenitic stainless steel. The application of nickel-based austenitic stainless steel has been seriously affected, while the use of ferritic and horse-based stainless steel has been further expanded. High chromium (25-31%) Ferritic stainless steel not only has excellent corrosion resistance, but also has excellent stress corrosion resistance, crevice corrosion resistance, and pitting corrosion resistance. It can replace expensive nickel-based and titanium and other advanced corrosion-resistant alloy materials. Although high-chromium ferritic stainless steel has excellent corrosion resistance, its severe brittleness prevents it from being widely used. Ferrite exists C and N interstitial elements in stainless ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/30
Inventor 翟世先徐华翟海平翟华平翟玉亭
Owner JIANGSU XIHU SPECIAL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com