Novel glass fibre composition

A technology of glass fiber and composition, applied in the field of glass fiber composition, which can solve the problems of high raw material cost, lower molding temperature and liquidus temperature, and high molding temperature of glass fiber composition, so as to improve mechanical strength and chemical stability properties, low molding temperature and liquidus temperature, and improved mechanical strength

Active Publication Date: 2009-08-12
JUSHI GRP CO
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Excessive molding temperature and liquidus temperature will greatly increase energy consumption, and will also accelerate the high-temperature aging of the kiln and platinum bushing, thereby increasing production costs
Patent WO01 / 32576 describes a low boron glass fiber composition whose components also mainly include SiO 2 、Al 2 o 3 , CaO and MgO, in a preferred embodiment, the MgO content ranges from 1.5 to 4%, the glass fiber composition has a large ΔT value, and the molding temperature and liquidus temperature are not high, but the SiO 2 The low content (less than 58%) affects the mechanical strength of the glass to a certain extent
[0006] Glass fiber compositions with an MgO content of less than 1% are rare, and the few known patents all have certain problems and cannot well meet the needs of industrial production
For example, the patent WO00 / 73232 uses a glass fiber composition with an MgO content of less than 1%, which is mainly composed of SiO 2 -Al 2 o 3 -CaO ternary system composition, also added a certain amount of B 2 o 3 , Li 2 O, ZnO, MnO or MnO 2 , to achieve the purpose of reducing the molding temperature and liquidus temperature, but from the examples, either the molding temperature is still too high, or the ΔT value is far less than 50°C
And the raw material cost of this glass fiber composition is too high
As another example, the patent WO03 / 050049 describes a glass fiber composition suitable for automobile exhaust systems, which introduces less than 1% of MgO and higher than 1.5% of TiO 2 The purpose of improving acid resistance and high temperature resistance has been achieved, but due to the use of a large amount of TiO 2 , the glass fiber composition lacks cost advantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel glass fibre composition
  • Novel glass fibre composition
  • Novel glass fibre composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0088] The technical solution of the present invention is specifically described below through examples, and the content of the present invention is not subject to any restriction by the following examples.

[0089] In the examples of the present invention, for the convenience of operation, the total content of the glass fiber composition is 100%, and the total content of the components in the examples is slightly less than 100%. It can be understood that the residual amount is a small amount of impurities or a small amount of components that cannot be analyzed .

[0090] The main raw materials for producing glass fiber in the present invention are pyrophyllite, quartz powder, limestone, dolomite, boronite and the like. The concrete process of the embodiment of the present invention is as follows: each composition can obtain from suitable raw material (as SiO in quartz powder 2 , CaO in quicklime), mix the various raw materials in an appropriate proportion, so that each compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glass fiber composition. The composition comprises the following compositions in percentage by weight: 58 to 65 percent of SiO2, 20 TO 26 percent of CaO, 9 to 17 percent of Al2O3, 0.5 to 1 percent of MgO, 0 to 5 percent of B2O3, 0 to 1 percent of F2, 0.1 to 1 percent of TiO2, 0 to 0.8 percent of K2O and Na2O, 0.1 to 0.5 percent of Fe2O3, and 0 to 0.6 percent of SO3. The glass fiber composition uses SiO2-Al2O3-CaO three-element system as basis, introduces MgO and B2O3 with low content, and reasonably designs the gross weight of alkaline metal oxides and the proportional relationship between the MgO and the CaO, not only contributes to the improvement of the mechanical strength, the high temperature resistance and the chemical stability of the glass, but also has excellent drawing performance; furthermore, the glass fiber composition has low cost in raw materials, and meets the requirement of environmental protection.

Description

(1) Technical field [0001] The invention relates to a glass fiber composition, in particular to a glass fiber composition with low magnesium and boron content. (2) Background technology [0002] E-glass, or alkali-free glass, is the most commonly used glass component for the production of continuous glass fibers. The base of the alkali-free glass composition is SiO 2 -Al 2 o 3 -CaO ternary system, which is a eutectic point composed of anorthite, pseudowollastonite and α-tridymite in equilibrium with the liquid phase in the ternary phase diagram, and its components and weight percentages are: SiO 2 62%; Al 2 o 3 14.7%; CaO 22.3%. On this basis, adding B to the glass composition 2 o 3 Substitute part of SiO 2 , MgO replaces part of CaO to form the now commonly used alkali-free glass composition. Its typical features are described in patents US2334981 and US2571074, which are generally SiO 2 -Al 2 o 3 -CaO-B 2 o 3 based on the quaternary system. The glass comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C13/02
CPCC03C13/00
Inventor 张毓强曹国荣张兵章林邢文忠顾桂江
Owner JUSHI GRP CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products