Lining board for inorganic nanometer chair and method for preparing same

An inorganic nano-liner technology, applied in the direction of sheet/board, manufacturing tools, ceramic molding machines, etc., can solve the problems of high production cost, limited product development, and non-compliance with environmental protection requirements for chair liners, and achieve low cost, The effect of safe and reliable use and beautiful appearance

Inactive Publication Date: 2008-12-31
湖州纳美消防科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the scarcity of wood, the production cost of chair liners is getting higher and higher, and the material itself will release pollutants such as formaldehyde, which does not meet environmental protection requirements, and greatly limits the development of the product market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Embodiment 1: Inorganic nano chair liner component weight ratio is: based on 100 parts, magnesium chloride is 12 parts, magnesium oxide is 15 parts, inorganic fiber is 1.2 parts, potassium permanganate is 0.2 parts, ferrous sulfate 0.2 parts of silica gel, 6 parts of silica gel, 0.2 parts of dispersant, 0.2 parts of concentrated sulfuric acid, 9 parts of nano silicon calcium powder, 16 parts of bamboo and wood fiber, 7 parts of nano active calcium, 15 parts of curing agent, water for the margin.

[0009] The preparation method of the lining board for the inorganic nano chair comprises the following steps: (1) using a heating reaction tank, adding magnesium chloride, magnesium oxide, potassium permanganate, ferrous sulfate, concentrated sulfuric acid into an appropriate amount of water, heating and stirring to make them mixed and reacted (2) After cooling to room temperature, add inorganic fiber, silica gel, dispersant, nano silicon calcium powder, bamboo fiber, nano act...

Embodiment 2

[0010] Embodiment 2: Inorganic nano chair liner component weight ratio is: based on 100 parts, magnesium chloride is 20 parts, magnesium oxide is 9 parts, inorganic fiber is 2.0 parts, potassium permanganate is 0.2 parts, ferrous sulfate 0.2 parts of silica gel, 2 parts of silica gel, 0.2 parts of dispersant, 0.2 parts of concentrated sulfuric acid, 15 parts of nano-calcium silica powder, 9 parts of bamboo and wood fiber, 11 parts of nano-active calcium, 9 parts of curing agent, water for the margin. Refer to Example 1 for the preparation method of the lining board for the inorganic nano chair.

Embodiment 3

[0011] Embodiment 3: Inorganic nano chair liner component weight ratio is: based on 100 parts, magnesium chloride is 16 parts, magnesium oxide is 12 parts, inorganic fiber is 1.6 parts, potassium permanganate is 0.2 parts, ferrous sulfate 0.2 parts of silica gel, 4 parts of silica gel, 0.2 parts of dispersant, 0.2 parts of concentrated sulfuric acid, 12 parts of nano-calcium silicon powder, 12.8 parts of bamboo and wood fiber, 8.8 parts of nano-active calcium, 12 parts of curing agent, water for the margin. Refer to Example 1 for the preparation method of the lining board for the inorganic nano chair.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a lining board for inorganic nano-chairs, and a preparation method. The components mainly comprise magnesium chloride, magnesia, inorganic fiber, potassium permanganate, ferrous sulfate, silica gel, dispersing agent, concentrated sulfuric acid, nano-calcium-silicon powder, bamboo fiber, nano-activated calcium and curing agent. The preparation method mainly comprises the following steps: the magnesium chloride, the magnesia, the potassium permanganate, the ferrous sulfate and the concentrated sulfuric acid are heated, stirred, mixed and reacted in a heating reaction vessel, then cooled to room temperature before the inorganic fiber, the silica gel, the dispersing agent, the nano-calcium-silicon powder, the bamboo fiber, the nano-activated calcium, the curing agent and sufficient water are added; then, all the components in the heating reaction vessel are stirred to form viscous gel with fluidity; the viscous gel with fluidity is poured into a mold for roll forming; after solidification, the gel is demoulded and baked. The invention uses some inorganic materials for mixed reaction and molding so as to replace the wooden chair-use lining boards, and has reasonable material selection and simple production process; the product has self-cleaning ability.

Description

technical field [0001] The invention relates to an inorganic nano chair liner and a preparation method thereof. Background technique [0002] In the prior art, the lining boards for chairs are mostly made of wood, or are bonded and pressed by bamboo and wood scraps. With the scarcity of wood, the production cost of chair liners is getting higher and higher, and the material itself will release pollutants such as formaldehyde, which does not meet environmental protection requirements, and greatly limits the development of the product market. Contents of the invention [0003] The present invention mainly solves the technical problems existing in the above-mentioned prior art, and provides an inorganic nano-chair liner and a preparation method thereof. [0004] The above-mentioned technical problems of the present invention are mainly solved by the following technical scheme: a liner for an inorganic nano-chair, the weight ratio of the components of the liner is: based on 1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32F16S1/00C04B14/38C04B18/26C04B14/04B28B1/52
CPCY02W30/91
Inventor 谢荣根谢荣林
Owner 湖州纳美消防科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products