Environmental protection highly effective water-based primer

A water-based primer and high-efficiency technology, applied in the field of paint, can solve the problems of far less anodic protection, harm to construction team personnel, lack of electrical conductivity, etc., to achieve excellent electrochemical anti-corrosion performance, excellent resistance to organic solvents, flexibility Sexual effect

Inactive Publication Date: 2007-02-07
武汉市大汉科技发展有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thermal spraying of zinc and aluminum is sprayed on the metal substrate after melting and atomizing the wire rod, which has residual stress, high porosity, and poor shielding performance, so a sealing coating must be added, and the zinc mist generated during construction is harmful to the construction team. Personnel are at great risk
Both organic and inorganic zinc-rich coatings use high-fineness zinc powder as raw material, which has good shielding performance on metal substrates, but organic mostly uses epoxy resin as base material, which does not have conductivity, so its anodic protection performance is far inferior to that of thermal spray coatings. Zinc, aluminum and inorganic zinc-rich coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental protection highly effective water-based primer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The environment-friendly high-efficiency water-based primer of the present invention has a component weight of Kg:

[0052] Recipe 1:

[0053] Silicate liquid 60

[0054] Sodium oxide, potassium oxide mixed oxide 20

[0055] Acrylic emulsion 15

[0056] Isopropyl alcohol 5

[0057] Recipe 2:

[0058] Zinc powder 80

[0059] White composite silicon titanium antirust powder 20

[0060] 1. Add 60Kg of silicate liquid in formula 1, 20Kg of potassium oxide and sodium oxide mixture in metal oxide, 15Kg of acrylic emulsion, and 5Kg of isopropanol to the reaction kettle, under the condition of 50-100℃ Mix and react for 3-72 hours, filter after passing the inspection, put in barrels, and put into storage.

[0061] 2. Crush, grind and mix the zinc powder 50Kg and the white composite silicon titanium antirust powder 30Kg in formula two, inspect, package, and leave the factory.

Embodiment 2

[0063] The environment-friendly high-efficiency water-based primer of the present invention has a component weight of Kg:

[0064] Recipe 1:

[0065] Silicate liquid 50

[0066] Lithium oxide 30

[0067] Acrylic emulsion 13

[0068] Catalyst, magnesium oxide mixture 7

[0069] Recipe 2:

[0070] Zinc powder 70

[0071] White composite silicon titanium antirust powder 30

[0072] 1. Add 50Kg of silicate solution in formula 1, 30Kg of lithium oxide mixture in metal oxide, 13Kg of acrylic emulsion, 5Kg of catalyst and magnesium oxide mixture, into the reaction kettle, and mix at a temperature of 50-100℃ , After reacting for 3-72 hours, filter after passing the inspection, put in barrels, and put into storage.

[0073] 2. Crush, grind and mix the zinc powder 70Kg and the white composite silicon titanium antirust powder 30Kg in formula two, inspect, package, and leave the factory.

Embodiment 3

[0075] The environment-friendly high-efficiency water-based primer of the present invention has a component weight of Kg:

[0076] Recipe 1:

[0077] Silicate liquid 45

[0078] Potassium oxide 25

[0079] Acrylic emulsion 20

[0080] Catalyst, magnesium oxide mixture 10

[0081] Recipe 2:

[0082]Zinc powder 75

[0083] White composite silicon titanium antirust powder 25

[0084] 1. Put 45Kg of silicate solution in formula 1, 25Kg of potassium oxide in metal oxide, 20Kg of acrylic emulsion, 10Kg of catalyst and magnesium oxide mixture into the reaction kettle, and mix at a temperature of 50-100°C. After 3-72 hours of reaction, filter after passing the inspection, put in barrels, and put into storage.

[0085] 2. After the zinc powder 75Kg and the white composite silicon-titanium anti-rust powder 25Kg in formula two are crushed, ground and mixed evenly, inspect, package, and leave the factory.

[0086] The production process of white composite silicon titanium antirust powder is a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmental-protective water-based priming paint, which comprises two formulations: one is 50-60% metasilicate liquid, 20-30% metal dioxide, 15-20% emulsion and 1-10% adjuvant; the other is 70-80% zinc powder and 20-30% white compound Si-Ti rust-proofing powder. The invention adopts water as solvent without polluting and VOC drainage, which can bear washing after drying for 30 min.

Description

Technical field [0001] The invention relates to the technical field of paint making, in particular to an environmentally friendly high-efficiency water-based primer. Background technique [0002] Most of the metal components are made of carbon steel, manganese steel, cast steel and other materials, and have been exposed to alternating wet and dry conditions, sunlight exposure, high-speed water flow, salt spray, and water media, microbial adhesion and other environments for a long time. Anti-corrosion treatment should be carried out according to the degree of time to extend its service life. General anti-corrosion coatings, such as chlorinated rubber, iron red epoxy, epoxy and other coatings, only have a shielding effect. Hot-sprayed zinc and aluminum are sprayed on the metal substrate after the wire is melted and atomized. There are residual stresses, high porosity, and poor shielding performance. Sealing coatings must be added, and the zinc mist generated dur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/12C09D5/02
Inventor 金广泉
Owner 武汉市大汉科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap