Denture adhesive compositions

A technology of adhesives and compositions, applied in dental preparations, dentistry, dental prostheses, etc., can solve problems such as insufficient holding force, messy and difficult removal of adhesives

Inactive Publication Date: 2002-08-21
THE PROCTER & GAMBLE COMPANY
View PDF17 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These deficiencies include insufficient retention, adhesive oozing from under the plates during insertion and fitting, and messy and difficult removal of residual adhesive from mouth and dentures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment I

[0052] Example I (A-O)

[0053] A

B

C

D

components

(gram)

(gram)

(gram)

(gram)

water

2850

2850

2841

2850

Calcium hydroxide

17.08

17.08

8.54

strontium carbonate

39.71

5.67

11.35

39.71

Zinc oxide

12.51

12.51

10.95

3.13

AVE / MA anhydride polymer 1

120

120

120

120

mixed salt

Sr(35%) / Zn

(20%) / FA (45%)

Ca(30%) / Sr

(5%) / Zn(20

%) / FA(45%)

Ca(30%) / Sr(10

%) / Zn(17.5%) /

FA (42.5%)

Ca(15%) / Sr(35

%) / Zn(5%) / FA

(45%)

E

F

G

H

components

(gram)

(gram)

(gram)

(gram)

water

2842

2850

2850

2850

Calcium hydroxide

14.24

5.13

2.7

strontium carbona...

Embodiment II

[0057] Weight / grams)

[0058] Weigh, mix red dye, petroleum jelly and mineral oil in a glass bottle and heat at 50-60°C until visually uniform. Next, weigh and vibrate the mixed powder (silica colloid, CMC, AVE / MA copolymer mixed salt or AVE / MA / IB mixed salt) in the container. Then, use a spatula to mix the powder into the liquid until you see an even pink cream. The above cream can be modified by increasing or decreasing the amount of AVE / MA mixed salt or AVE / MA / IB mixed salt by 0-18.75 grams, petrolatum by 0-18.75 grams and / or CMC by 0-18.75 grams sex. The above cream composition can also be modified by using a mixture of different AVE / MA polymer mixed salts and / or AVE / MA / IB mixed salts. The subject applied 0.1-2 grams of the cream composition to the dentures. The subjects then place the dentures in their mouths and press them into place.

Embodiment III

[0060] Weight / grams)

[0061] All ingredients are mixed. The above composition can be modified by increasing or decreasing the amount of AVE / MA mixed salt or AVE / MA / IB polymer mixed salt by 0-50 grams, and / or increasing or decreasing CMC by 0-40 grams. The powder compositions described above can also be modified by using mixtures of different AVE / MA mixed salts and / or AVE / MA / IB mixed salts. The subject applied 0.1-2 grams of the composition to the pre-moistened denture and allowed it to briefly hydrate. The subjects then place the dentures in their mouths and press them into place.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a denture adhesive composition comprising mixed salts of an alkyl vinyl ehter-maleic acid or anhydride copolymer and / or terpolymer with isobutylene wherein the mixed salt contains a cationic salt function comprising at least about 1 % strontium cations, from about 1 % to about 40 % of zinc cations, from 0 % to about 2.5 % of a cation selected from the group consisting of iron, boron, aluminum, vanadium, chromium, manganese, nickel copper, yttrium, titanium, and mixtures thereof; from about 36 % to about 60 % free acid component; and from 0 % to about 65 % of a cation selected from the group consisting of magnesium, calcium, and mixtures thereof. In addition, the present invention relates to denture adhesive compositions comprising the above composition and at least one non-adhesive self-supporting layer. The present invention further relates to a method of increasing the adhesion of dentures to the oral cavity by applying the above compositions to dentures, directly to the oral cavity, palate or ridge of the oral cavity, or applying it to both, and thereafter securing the dentures to the ridge or palate of the oral cavity.

Description

background of the invention [0001] Typically removable dentures, dental plates, etc. consist of teeth secured in a suitable plate or base. Denture stabilizers are used to fill the gap between the denture and the gum or tissue. Before the denture is placed in the mouth, the denture stabilizer is placed on the surface of the denture board, it should evenly contact the gums and oral tissues for a good fit. Denture stabilizers are not only formulated to be adhesive, but also to provide a lining or cushion between the denture and the gums or tissues, thereby holding the denture securely in place in the oral cavity. [0002] Over the years, considerable efforts have been made to develop improved denture adhesive compositions. Synthetic and natural polymers and gums have been used alone or in combination, and in combination with various adhesives and other materials to overcome certain deficiencies. These deficiencies include insufficient retention, adhesive seeping from under the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61C13/23A61K6/00A61K6/884C08F8/44
CPCA61K6/0026C08F8/44A61K6/35C08L35/08C08L1/28C08L1/08C08L89/04C08L5/04C08L5/08C08L71/02C08L33/26C08L33/08C08L29/04C08L83/04C08L39/06A61K6/00
Inventor J·拉贾哈C·A·舒马赫J·R·惠特尼K·A·吉尔达-韦伯E·D·史密斯三世
Owner THE PROCTER & GAMBLE COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com