Manufacturing and processing technology for electric stay insulator

A wire-drawing insulation and processing technology, applied in the field of electric wire-drawing insulator manufacturing and processing technology, can solve problems affecting product quality stability, general mechanical strength performance, electrical performance degradation, etc., achieve uniform and stable organization, excellent comprehensive performance, and ease of volume effect of change

Active Publication Date: 2022-01-28
江西凯佳电瓷电器有限公司
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The insulators in the prior art have mediocre mechanical strength and are prone to problems such as cracking, mechanical and electrical performance degradation during use, which seriously affect the quality stability of the product and cannot fully meet the needs of high-speed power

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A manufacturing and processing technology for electric cable insulators, comprising the following steps:

[0029]S1. Weigh the following raw materials: 12 parts of left cloud clay, 24 parts of bauxite / modified vapor phase white carbon composite material, 2 parts of granite powder, 4 parts of nano-boron nitride, mica powder-coated modified nano-calcium carbonate 12 parts of composite material, 5 parts of lamellar mica, 3 parts of potassium titanate whisker coated lignin fiber and coconut fiber composite material, 1 part of modified bentonite, 2 parts of zinc oxide / silicone rubber composite material, 3 parts of sintering aid share;

[0030] Among them, the preparation method of zinc oxide / silicone rubber composite material includes: adding zinc oxide with a particle size of 2 to 10 μm into silicone rubber, the mass ratio of zinc oxide to silicone rubber is 0.3:1, the frequency is 200Hz, and the power 100W ultrasonic dispersion for 60min.

[0031] Among them, the prepara...

Embodiment 2

[0045] A manufacturing and processing technology for electric cable insulators, comprising the following steps:

[0046] S1. Weigh the following raw materials: 14 parts of left dolomite, 26 parts of bauxite / modified vapor phase white carbon composite material, 3 parts of granite powder, 5 parts of nano-boron nitride, mica powder-coated modified nano-calcium carbonate 14 parts of composite material, 6 parts of lamellar mica, 4 parts of potassium titanate whisker coated lignin fiber and coconut fiber composite material, 2 parts of modified bentonite, 2.5 parts of zinc oxide / silicone rubber composite material, 4 parts of sintering aid share;

[0047] Among them, the preparation method of the zinc oxide / silicone rubber composite material includes: adding zinc oxide with a particle size of 2 to 10 μm into the silicone rubber, the mass ratio of zinc oxide to silicone rubber is 0.3:1, and the frequency is 300 Hz, the power 120 ultrasonic dispersion for 30 ~ 60min.

[0048] Among th...

Embodiment 3

[0062] A manufacturing and processing technology for electric cable insulators, comprising the following steps:

[0063] S1. Weigh the following raw materials: 16 parts of left dolomite, 28 parts of bauxite / modified vapor phase white carbon composite material, 4 parts of granite powder, 6 parts of nano-boron nitride, mica powder-coated modified nano-calcium carbonate 16 parts of composite material, 8 parts of lamellar mica, 5 parts of potassium titanate whisker coated lignin fiber and coconut fiber composite material, 3 parts of modified bentonite, 3 parts of zinc oxide / silicone rubber composite material, 5 parts of sintering aid share;

[0064] Among them, the preparation method of the zinc oxide / silicone rubber composite material includes: adding zinc oxide with a particle size of 2 to 10 μm into the silicone rubber, the mass ratio of zinc oxide to silicone rubber is 0.35:1, and the frequency is 400 Hz, the power 150W ultrasonic dispersion for 45min.

[0065] Among them, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing and processing technology for an electric stay insulator, and relates to the technical field of insulators. The technology comprises the following steps: weighing raw materials: Zuoyun soil, a bauxite / modified fumed silica composite material, granite powder, nano boron nitride, a mica powder coated modified nano calcium carbonate composite material, lamellar mica, a potassium titanate whisker coated lignin fiber and coconut fiber composite material, modified bentonite, a zinc oxide / silicone rubber composite material and a sintering aid. The process comprises: premixing the materials except a sintering aid to obtain a premix, putting the premix into a ball mill, and adding water for ball milling to obtain a mixture; sieving, removing iron, squeezing mud, aging, pugging in vacuum, forming, fettling and drying; pre-sintering; crushing the pre-sintered material; and pressing the crushed material and a sintering aid, and sintering a pressed part. The process has the beneficial effects that a prepared insulator has the advantages of high mechanical property, high strength and the like.

Description

technical field [0001] The invention relates to the field of insulators, in particular to a manufacturing and processing technology for electric cable insulators. Background technique [0002] Insulators are special insulation controls that can play an important role in overhead transmission lines. Insulators are mostly used on utility poles, and gradually developed into high-voltage wire connection towers where many disc-shaped insulators are hung at one end. It is used to increase the creepage distance, usually made of glass or ceramics, and is called an insulator. Insulators play two basic roles in overhead transmission lines, namely supporting wires and preventing current from returning to the ground. These two functions must be guaranteed. Insulators should not fail due to various electromechanical stresses caused by changes in the environment and electrical load conditions. Otherwise, the insulator will not play a significant role, and it will damage the service life ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/10C04B35/622C04B35/64H01B3/12H01B17/00
CPCC04B35/10C04B35/622C04B35/64H01B3/12H01B17/00C04B2235/3418C04B2235/349C04B2235/3427C04B2235/386C04B2235/3472C04B2235/3481C04B2235/3208C04B2235/3234C04B2235/3284C04B2235/483C04B2235/5212C04B2235/3232C04B2235/5276C04B2235/602C04B2235/656C04B2235/6562C04B2235/6567C04B2235/96
Inventor 晏良清张华
Owner 江西凯佳电瓷电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap