Production method of hot-rolled strip steel for low-cost and low-yield-strength DC01 cold-rolled sheet

A low-yield strength, hot-rolled strip technology, applied in metal rolling, temperature control, metal rolling, etc., can solve the problems of production cost and high strength performance, and achieve the effect of improving smelting efficiency, obvious effect and clear method

Active Publication Date: 2021-11-30
安钢集团冷轧有限责任公司 +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention mainly relates to the field of continuous hot rolling production of hot rolling raw materials for the production of high-quality and efficient DC01 cold-rolled sheets, solves the problems of high production cost and high strength performance of commonly used cold-rolled sheets DC01, and invents a low-cost and low-yield Production method of hot-rolled steel strip of strength DC01 cold-rolled plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] When this embodiment produces 0.6mm*1250 general cold-rolled sheet DC01, the specific requirements of the production process of each process are as follows:

[0022] 1) Steelmaking, 150t converter smelting to provide high-efficiency and high-quality hot-rolled strip steel for general-purpose cold-rolled plate DC01 adopts the top-bottom double blowing process, the smelting time is 28min, the tapping temperature is 1660°C, and the composition system during tapping is: C 0.05 %, Si 0.01%, Mn0.18%, P 0.012%, S 0.010%, Al 0.042%, N 0.0032%, and the rest are Fe and unavoidable impurities.

[0023] 2) Continuous casting. After the converter smelting is completed, the tundish containing molten steel is directly transferred to the continuous casting platform for pouring. The thickness of the continuous casting slab is 210mm, the width is 1290mm, and the casting speed of the continuous casting slab is 1.05m / min. The continuous casting slab of the head 18m and the tail 10m of the ...

Embodiment 2

[0028] When this embodiment produces 1.5mm*1250 cold-rolled sheet DC01 for general use, the specific requirements of the production process of each process are as follows:

[0029] 1) Steelmaking, 150t converter smelting, when providing high-efficiency and high-quality hot-rolled raw materials for general-purpose cold-rolled sheet DC01, the top-bottom combined blowing process is adopted. The smelting time is 30 minutes, and the tapping temperature is 1685°C. The composition system during tapping is: C 0.03% , Si 0.01%, Mn0.17%, P 0.010%, S 0.008%, Al 0.045%, N 0.0035%, and the rest are Fe and unavoidable impurities.

[0030] 2) Continuous casting. After the converter smelting is completed, the tundish containing molten steel is directly transferred to the continuous casting platform for casting. The thickness of the continuous casting slab is 230mm, the width is 1450mm, and the casting speed of the continuous casting slab is 1.2m / min. The continuous casting slab of the head 16...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

Production method of hot-rolled strip steel for low-cost and low-yield-strength DC01 cold-rolled sheet The invention discloses a production method of hot-rolled strip steel for a low-cost and low-yield-strength DC01 cold-rolled sheet, and relates to the technical field of ferrous metallurgy. The production method specifically comprises the following procedures of being subjected to a 150t converter, a 210mm / 230mm slab continuous casting machine, hot-state slab heating, two roughing mills and seven 1780mm hot continuous rolling units, coiling and warehousing after steel coil cooling, and cold rolling. Under the condition that the product quality is guaranteed, the smelting process is simplified, and the smelting efficiency is improved; the mode of heating a plate blank in a heating furnace is improved, the heating time is shortened, the heating temperature is reduced, the gas consumption is reduced, and the production cost is reduced; and the rolling temperature after rolling is optimized, ferrite grains of hot-rolled raw materials are properly increased, the distribution state of cementite is improved, under the condition that the cold-rolling production process is not changed, the yield strength of the DC01 cold-rolled sheet is reduced, and the deep processing requirement of a user is met. The production method is clear, simple to operate, obvious in effect and wide in popularization and application.

Description

technical field [0001] The invention relates to the technical field of iron and steel metallurgy, in particular to a method for producing hot-rolled steel strips for low-cost low-yield strength DC01 cold-rolled plates. Background technique [0002] In GB / T 5213-2019 "Cold-rolled low-carbon steel plates and steel strips", DC01 is classified as general-purpose cold-rolled plates according to their uses. The product performance requirements are: yield strength ≤ 280MPa, tensile strength 270MPa~410MPa, elongation Rates are graded according to specification requirements. Although the standard has a wide range of requirements for yield strength, users often have problems with poor formability or cracking during processing due to the high yield strength during processing, and have repeatedly proposed to manufacturers to reduce the yield strength of DC01 cold-rolled sheets. Require. [0003] The DC01 cold-rolled plate produced by the process of "steelmaking→LF refining→slab contin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/46B21B37/00B21B37/74C22C33/04C21C5/28C22C38/02C22C38/04C22C38/06B22D11/00C21D8/02C21D1/26
CPCB21B1/466B21B37/00B21B37/74C22C33/04C21C5/28C22C38/02C22C38/04C22C38/06B22D11/001C21D8/0205C21D8/0226C21D8/0236C21D8/0247C21D1/26B21B2201/04Y02P10/20
Inventor 何晓波程官江黄重戚新军厚健龙崔占利向华李龙飞陈战锋于永业李堃刘伟云成晓举高艳张玉琴孟晓涛
Owner 安钢集团冷轧有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products