Thermoplastic resin, molded object, and monomer for thermoplastic resin

A thermoplastic resin and molded body technology, applied in the field of thermoplastic resin monomers, can solve the problems of high material cost, practical obstacles, high technology, etc., and achieve the effect of excellent optical characteristics

Active Publication Date: 2021-11-19
MITSUBISHI GAS CHEM CO INC
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As far as optical glass is concerned, it has excellent heat resistance, transparency, dimensional stability, chemical resistance, etc., and has various refractive indices (nD) and Various materials with Abbe number (νD), but there are problems such as high material cost, poor molding processability, and low productivity
In particular, processing it into an aspheric lens used for aberration correction requires extremely high technology and high cost, so it becomes a big obstacle in practical use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic resin, molded object, and monomer for thermoplastic resin
  • Thermoplastic resin, molded object, and monomer for thermoplastic resin
  • Thermoplastic resin, molded object, and monomer for thermoplastic resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0270] Hereinafter, the present invention will be described by way of examples, but the present invention is not limited by these examples. In addition, the measured values ​​in the examples were measured by the following methods or devices.

[0271] (1) Weight average molecular weight (Mw)

[0272] A calibration curve was prepared by gel permeation chromatography (GPC) using tetrahydrofuran as a developing solvent and standard polystyrene with known molecular weight (molecular weight distribution=1). Calculated from the retention time of GPC based on this calibration curve.

[0273] (2) Refractive index nd

[0274] The resin is press-molded (molding conditions: 200°C, 100kgf / cm 2 , 2 minutes) into a circular plate with a diameter of 40 mm and a thickness of 3 mm, cut out a test piece at a right angle, and use a precision refractometer (manufactured by Shimadzu Corporation, product name "KPR-200") for the test piece. Determination.

[0275] (3) Glass transition temperatur...

manufacture example 1

[0292] Production Example 1 (Synthesis of D-NDM-Me)

[0293] The synthesis scheme of D-NDM-Me is as follows.

[0294]

[0295] In addition, the conditions of the gas chromatography measurement and GC-MS measurement of the product obtained by each process of manufacture example 1 are as follows.

[0296] (1) Gas Chromatography Determination Conditions

[0297] ・Analyzer: Shimadzu Corporation, Capillary Gas Chromatograph GC-2010Plus

[0298] ・Analytical column: manufactured by GL Sciences Inc., InertCap1 (30 m, 0.32 mm I.D., film thickness 0.25 μm)

[0299] Oven temperature: 60°C (0.5 minutes) - heating rate 15°C / min - 280°C (4 minutes)

[0300] ·Detector: FID, temperature 280°C

[0301] (2) GC-MS measurement conditions

[0302] ・Analyzer: Shimadzu Corporation, GCMS-QP2010 Plus

[0303] ·Ionization voltage: 70eV

[0304] Analytical column: manufactured by Agilent Technologies Co., Ltd., DB-1 (30m, 0.32mm I.D., film thickness 1.00μm)

[0305] Oven temperature: 60°C (0.5 ...

Embodiment 1

[0321] Diphenyl carbonate and 20.0mg (6.0×10 -5 mol) of tetrabutoxytitanium were added to a 500mL reactor equipped with a stirrer and a distillation device, and nitrogen gas was introduced into the system, and heated to 180°C for 1 hour while stirring under a nitrogen atmosphere of 101.3kPa. Then, after reaching 180°C, while decompressing to 40kPa over 30 minutes, the temperature was raised to 255°C over 2 hours from the start of depressurization, and when the distilled methanol and phenol reached 60%, the pressure was further increased for 1 hour. Reduce the pressure to below 0.133kPa. Then, it was held at 0.133 kPa or less for 30 minutes to obtain a polycarbonate resin (1).

[0322] Polycarbonate resin (1) is to have the structural unit shown in above-mentioned general formula (IA) (wherein, R 1 is methyl, R 2 and R 3 is a polymer of Mw=28,000).

[0323] Furthermore, the physical properties of the polycarbonate resin (1) are refractive index nd: 1.525, Tg: 127°C, specif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
photoelasticityaaaaaaaaaa
photoelasticityaaaaaaaaaa
Login to View More

Abstract

Provided is a thermoplastic resin which includes a constituent unit represented by general formula (I). [In formula (I), R1 represents a hydrocarbon group having 1-6 carbon atoms, and R2 and R3 each independently represent a hydrogen atom or a methyl group.].

Description

technical field [0001] The present invention relates to a thermoplastic resin, a molded article formed by molding a resin composition containing the thermoplastic resin, and a thermoplastic resin monomer used as a raw material of the thermoplastic resin. Background technique [0002] Optical glass or optical transparent resin is used as a material for optical elements mounted in various cameras such as still cameras, film-integrated cameras, and video cameras. [0003] For optical glass, there are many materials that are excellent in heat resistance, transparency, dimensional stability, and chemical resistance, and have various refractive indices (nD) and Abbe numbers (νD). However, materials with There are problems of high cost, poor moldability, and low productivity. In particular, processing into an aspheric lens used for aberration correction requires extremely high technology and high cost, which is a major obstacle to practical use. [0004] On the other hand, optica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G64/02C08G63/199
CPCC08G63/199C08G64/0208C08G63/64C08G64/02
Inventor 本多荣一平川学吉村康明佐竹雄一郎
Owner MITSUBISHI GAS CHEM CO INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com