Carbon-free high-speed steel and preparation method thereof

A high-speed steel and high-speed technology, applied in the field of carbon-free high-speed steel and its preparation, can solve the problems of not improving material hardness and material brittleness well, achieve superior tool material performance, improve tempering resistance and red hardness, The effect of controlling the cost of raw materials

Inactive Publication Date: 2021-06-18
XIANGTAN UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For Fe-Co-Mo materials, the presence of a large amount of Fe elements saves the cost of raw materials, but because of the large amount of Fe elements, the excessive addition of B elements will lead to the formation of grid-like brittle iron-boron compounds, resulting in material overall brittleness
However, the addition of too little B element can not improve the hardness of the material, so it is necessary to explore the LaB 6 The effect of adding amount on the hardness of Fe-Co-Mo material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon-free high-speed steel and preparation method thereof
  • Carbon-free high-speed steel and preparation method thereof
  • Carbon-free high-speed steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] The present invention is a carbon-free high-speed steel and its preparation method, and its technical characteristics will be described through six specific examples. The preparation process in each described embodiment is the same, but the process parameters are different.

[0038] The carbon-free high-speed steel of the present invention is composed of 60-76% Fe powder, 14.85-24.95% Co powder, 9-15% Mo powder, 0.05-0.15% LaB 6 Powder composition; Said percentage is mass percent.

[0039] The Fe powder, Co powder, Mo powder and LaB 6 The purity of the powder is 99.9%, the purity is 100% by mass, and the particle size is 74-100um.

[0040] Table 1: Components of each example

[0041]

[0042] The concrete process that the present invention proposes to prepare described carbon-free high-speed steel is:

[0043] Step 1, ball milling:

[0044]Weigh the ingredients. The weighed raw material powder is placed in a ball mill, and absolute ethanol is added to perform b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses carbon-free high-speed steel and a preparation method thereof. According to the carbon-free high-speed steel provided by the invention, iron powder is introduced to replace molybdenum powder and cobalt powder, and a small amount of LaB6 is introduced to improve the tempering resistance and red hardness of the material; and through joint addition of La and B, strengthening is caused, austenite transformation is delayed, structure coarsening and desolvation of alloy elements during tempering are inhibited, so that the red hardness and the hot hardness of the Fe-Co-Mo material are improved. Meanwhile, a preparation process is simple, the cost of the raw materials is reduced, the excellent cutter material performance is shown, and a prepared cutter can keep high hardness and is not sticky under the long-time cutting action, and important application value in the industry is achieved.

Description

technical field [0001] The invention relates to the field of chipping titanium alloys, in particular to a carbon-free high-speed steel and a preparation method thereof. Background technique [0002] At present, the application of titanium alloy is becoming more and more extensive. The output of titanium processing materials in my country is more than 550,000 tons, which are used in aerospace, medicine, chemical industry, military industry, automobile, electric power, etc., represented by aerospace, medicine, military industry and marine engineering. The application proportion of high-end titanium materials is increasing year by year, but as far as the current tool materials are concerned, due to the low thermal conductivity, high chemical activity and low elastic modulus of titanium alloys, titanium alloys generate a large amount of heat during cutting and cannot be conducted. , Excessively high temperature also causes the hardness of the tool to decrease, the cutting edge wea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/10C22C38/12C22C33/02B22F3/02B22F3/10B22F3/24B22F9/04C21D1/18C21D1/26C21D1/773C21D6/00
CPCB22F3/02B22F3/1007B22F3/1017B22F3/24B22F9/04B22F2003/248B22F2009/043C21D1/18C21D1/26C21D1/773C21D6/007C22C33/0285C22C38/002C22C38/005C22C38/10C22C38/12
Inventor 尹付成李明欢欧阳雪枚胡静娴刘永雄
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products