Photocatalytic nano composite catalyst and preparation method thereof

A nanocomposite and catalyst technology, applied in the field of photocatalytic nanomaterial synthesis, can solve the problems of low photocatalytic pure water splitting efficiency, high price, scarce reserves of precious metal catalysts, etc., and achieve good catalytic activity and stability, low price, The effect of mild reaction conditions

Active Publication Date: 2020-11-27
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the scarcity of precious metal catalysts, high price and large work function, the reverse reaction of oxygen reduction in photocatalytic water splitting is more obvious, resulting in low efficiency of photocatalytic pure water splitting.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photocatalytic nano composite catalyst and preparation method thereof
  • Photocatalytic nano composite catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method of a photocatalytic nanocomposite catalyst, comprising the following steps:

[0026] Weigh 0.008mol of lanthanum nitrate, 0.008mol of aluminum nitrate and 0.084mol of SrTiO, respectively 3 , mixed and ground in an agate mortar for 1 hour, the ground mixture was placed in a ball mill, ball milled at 4000 revolutions for 10 hours, and then 1 mol of SrCl was added. 2 Continue ball milling for 1 hour; sieve and separate the ball-milled mixture, place it in a muffle furnace, keep it at 800 degrees for 12 hours, take it out, filter and wash it with a large amount of deionized water, and then place the material in a drying box at 80 degrees Dry overnight to obtain La,Al-SrTiO 3 Nanoparticles; La,Al-SrTiO 3 With the mass ratio of 2.0wt% (NH 4 ) 2 WS 4 WS formed after 800 degree pyrolysis peeling 2The nanosheets and chromium salts were uniformly ground and mixed for 4 hours, and kept at 500 degrees for 4 hours under the protection of inert gas to obtai...

Embodiment 2

[0029] A preparation method of a photocatalytic nanocomposite catalyst, comprising the following steps:

[0030] Weigh 0.005mol of lanthanum nitrate, 0.005mol of aluminum nitrate and 0.09mol of SrTiO respectively 3 , mixed and ground in an agate mortar for 1 hour, the ground mixture was placed in a ball mill, ball-milled at 4000 revolutions for 24 hours, and then 1 mol of SrCl was added. 2 Continue ball milling for 1 hour; sieve and separate the ball-milled mixture, place it in a muffle furnace, and keep it at 1000 degrees for 8 hours; after taking it out, filter and wash it with a large amount of deionized water, and then place the material in a drying box at 80 degrees Dry overnight to obtain La,Al-SrTiO 3 Nano catalyst material; La,Al-SrTiO 3 With the mass ratio of 1.0wt% (NH 4 ) 2 WS 4 WS formed after 400 degree pyrolysis peeling 2 The nanosheets and the chromium salt were uniformly ground and mixed for 4 hours, and kept at 400 degrees for 2 hours under the protectio...

Embodiment 3

[0032] A preparation method of a photocatalytic nanocomposite catalyst, comprising the following steps:

[0033] Weigh 0.001mol of lanthanum nitrate, 0.001mol of aluminum nitrate and 0.098mol of SrTiO respectively 3 , mixed and ground in an agate mortar for 1 hour, the ground mixture was placed in a ball mill, ball-milled at 4000 revolutions for 24 hours, and then 1 mol of SrCl was added. 2 Continue ball milling for 1 hour; sieve and separate the ball-milled mixture, place it in a muffle furnace, and keep it at 800 degrees for 4 hours; after taking it out, filter and wash it with a large amount of deionized water, and then place the material in a drying box at 80 degrees Dry overnight to obtain La,Al-SrTiO 3 Nano catalyst material; La,Al-SrTiO 3 with a mass ratio of 0.5wt% (NH 4 ) 2 WS 4 WS formed after 400 degree pyrolysis peeling 2 The nanosheets and chromium salts were uniformly ground and mixed for 4 hours, and kept at 500 degrees for 4 hours under the protection of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-composite catalyst for photocatalytic decomposition of water and a preparation method thereof, and belongs to the technical field of synthesis of photocatalytic nano-materials. A pure water decomposition reaction under ultraviolet-visible light catalysis is realized, and the catalyst has good catalytic activity and stability. The preparation process is simple to operate, reaction conditions are mild, and used reagents are low in price. The invention discloses design and preparation methods of a novel photocatalytic nano material, namely La and Al bimetallic ion co-doped SrTiO3, as a photocatalytic light absorption semiconductor material. WS2@CrOx is loaded as a hydrogen evolution cocatalyst, CoOOH is loaded is an oxygen evolution cocatalyst, the molar ratio of La to Al is respectively 1%-10%, and the loading capacity of the cocatalysts is 0.5-5 wt%, so that different WS2@CrOx / La, Al-SrTiO3 / CoOOH composite nano-materials are obtained.

Description

technical field [0001] The invention belongs to the technical field of synthesis of photocatalytic nanomaterials, in particular to a photocatalytic nanocomposite catalyst and a preparation method thereof. Background technique [0002] Semiconductor photocatalysis can facilitate a variety of difficult chemical reactions under mild conditions, such as photocatalytic degradation of organic matter, photocatalytic synthesis of ammonia, methanol and other high value-added chemical raw materials, photocatalytic water splitting, etc. A key technology for converting photon energy into chemical energy. Due to its high combustion calorific value and environmental friendliness, hydrogen is considered to be a clean alternative energy source. 2 mol of water can be split into 2 mol of hydrogen and 1 mol of oxygen. When storable hydrogen energy is available, photocatalytic pure water splitting technology may replace the pure consumption mechanism of fossil fuels at a high level, so it has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J27/049C01B3/04C01B13/02
CPCB01J27/049B01J37/0036C01B3/042C01B13/0207B01J35/39B01J35/23Y02E60/36
Inventor 常焜秦亚雷徐旺韩文君林惠文
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com