Preparation method of pure water cracking semiconductor catalyst for realizing visible light response by bimetal ion co-doped strontium titanate

A technology of metal ions and photocatalysts, which is applied in the field of synthesis of photocatalytic nanomaterials, can solve the problems of low photocatalytic water splitting activity and loss of activity, achieve good catalytic activity and stability, mild and safe reaction conditions, and easy preparation process operation simple effect

Pending Publication Date: 2022-06-07
扬州市常发新能源科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Studies have shown that by doping Cr 3+ Metal ions can enhance the SrTiO 3 photocatalytic activity, but Cr 3+ The ions are easily oxidized to Cr during the reaction 6+ Thereby losing activity, often through trivalent metals such as La 3+ Ion doping at the A site, replacing Sr 2+ ions to stabilize the perovskite structure; however, for perovskite SrTiO 3 For semiconductor catalysts, oxygen defects are ubiquitous, resulting in low photocatalytic water splitting activity. Recently, an article reported that Al 3+ The introduction of ions can regulate oxygen vacancies. Although visible light response cannot be realized, the photocatalytic water splitting activity in the ultraviolet light response range can be greatly improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of pure water cracking semiconductor catalyst for realizing visible light response by bimetal ion co-doped strontium titanate
  • Preparation method of pure water cracking semiconductor catalyst for realizing visible light response by bimetal ion co-doped strontium titanate
  • Preparation method of pure water cracking semiconductor catalyst for realizing visible light response by bimetal ion co-doped strontium titanate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] an Al 3+ , Cr 3+ The preparation method of the ion co-doped strontium titanate semiconductor catalyst comprises the following steps:

[0033] Weigh 0.08mol of strontium nitrate, 20ml of ethylene glycol and 6ml of isopropyl titanate respectively, mix them in a beaker, heat and stir at 80°C for 100min, continue to add 0.0008mol of aluminum nitrate and 0.0008mol of chromium nitrate, and transfer the mixture They were placed in an oil bath and heated at 120 °C for 600 min to obtain a transparent resin gel, and then heat-treated in air at 450 °C for 6 hours to obtain double metal ion co-doped SrTiO 3 The precursor, the precursor is generally black. Double metal ion co-doped SrTiO obtained after the precursor heat treatment at 900℃ 3 , again with excess SrCl 2 After uniform grinding, it was kept in a muffle furnace at 1000°C for 10 hours. After taking it out, it was filtered and washed with a large amount of deionized water, and then the material was dried in a drying bo...

Embodiment 2

[0039] a Ga 3+ , Rh 3+ The preparation method of the ion co-doped strontium titanate semiconductor catalyst comprises the following steps:

[0040] Weigh 0.15 mol of strontium nitrate, 25 ml of ethylene glycol and 10 ml of isopropyl titanate, respectively, mix them in a beaker, heat and stir at 90°C for 100 min, continue to add 0.0015 mol of gallium nitrate and 0.0015 mol of rhodium nitrate, and transfer the mixture. Placed in an oil bath and heated at 150 °C for 700 min to obtain a transparent resin gel, and then heat-treated at 550 °C in air for 6 hours to obtain double metal ion co-doped SrTiO 3 The precursor, the precursor is generally black. Double metal ion co-doped SrTiO obtained after the precursor heat treatment at 900℃ 3 , again with excess SrCl 2 After uniform grinding, it was kept in a muffle furnace at 1100°C for 12 hours. After taking out, it was filtered and washed with a large amount of deionized water, and then the material was dried in a drying box at 80...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a pure water cracking semiconductor catalyst for realizing visible light response by bimetallic ion co-doped strontium titanate, which comprises the following steps: conventionally mixing a (III) IA source compound and a (III) IB source compound with a common chemical containing Sr and Ti elements in proportion, and carrying out chemical complexation through simple heating treatment to obtain the pure water cracking semiconductor catalyst. And the double metal ion co-doped SrTiO3 body is directly synthesized. The preparation method comprises the following steps: uniformly mixing SrTiO3 with SrCl2, carrying out a certain thermal insulation heat treatment, removing excess SrCl2 by using a large amount of water to obtain a target product, and synthesizing the bimetallic ion co-doped SrTiO3 with specific morphology of (III) and (III) , the molar ratio of (III) ions is 0.1-0.5%, the molar ratio of (III) ions is 0.1-0.5%, and RhCrOx and CoOOH are loaded as cocatalysts. The reaction conditions are mild and safe, and the used reagents are low in price.

Description

technical field [0001] The invention belongs to the technical field of synthesis of photocatalytic nanomaterials, and particularly relates to two types of (III) valence bimetallic ion co-doped strontium titanate semiconductor catalysts and a preparation method thereof. Background technique [0002] Semiconductor photocatalysis can favorably facilitate many difficult chemical reactions under mild conditions, such as photocatalytic degradation of organic compounds, photocatalytic CO 2 Reduction, synthesis of ammonia, methanol and other high value-added chemical raw materials, photocatalytic water splitting, etc., are sustainable strategies for the production of fuels and chemicals, and photocatalysis is considered as a key technology for converting photon energy into chemical energy. Due to its high combustion calorific value and environmental friendliness, hydrogen is considered to be a clean alternative energy source. 2mol of water can be split into 2mol of hydrogen and 1mol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/89C01B3/04
CPCB01J23/8993B01J23/002C01B3/042B01J35/39Y02E60/36Y02P20/133
Inventor 常焜高维荣
Owner 扬州市常发新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products