A kind of high-strength, high-elongation ductile iron alloy and preparation method thereof

A ductile iron, high elongation technology, applied in the field of casting alloys, can solve the problems of difficult to improve material properties, high cost of heat treatment, unstable as-cast materials, etc., to promote clean molten iron, good graphite shape, pearlescent The effect of fine spacing between body pieces

Active Publication Date: 2022-03-11
HUBEI XINGYUAN SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still problems with the above-mentioned materials: firstly, the as-cast material is not stable enough, and the mechanical properties deviate greatly; secondly, the cost of the heat treatment state is too high, and the cost performance is poor; finally, the current technological level has reached the upper limit, and it is difficult to improve the material performance. space, it is difficult to meet higher demands
However, the existing ductile iron alloy materials are difficult to meet the performance indicators of high strength and high elongation at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength, high-elongation ductile iron alloy and preparation method thereof
  • A kind of high-strength, high-elongation ductile iron alloy and preparation method thereof
  • A kind of high-strength, high-elongation ductile iron alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074]A heavy-duty tractor balance bridge support casting in this embodiment has a chemical composition ratio of C3.75%, Si2.76%, Mn0.52%, P0.035%, S0.018%, Mg0.056%, Cr0.095%, Ni0.065%, Mo0.15%, Cu0.75%, Sn0.02%, Al0.015%, Ti0.036%, V0.01%, Ba0.0025%, Ca0.0025%, RE0.002%, N0.003%, O0.0015%.

[0075] Prepare according to the following production process:

[0076] Step 1: Select high-quality pig iron with a carbon content of 4.5%, high-quality carbon, low-alloy and low-impurity briquette scrap, calcined high-purity silicon carbide, graphite-type low-sulfur carburizer, high-quality long-term special inoculant, high-magnesium spheroidized wire, Pearlitic inoculated filaments and high-strength ductile iron alloy additives are used as raw materials.

[0077] Step 2: Manufacture a special model for high-strength ductile iron castings and a sand box with adjustable temperature control film.

[0078] Step 3: The raw materials are smelted into molten iron in an intermediate frequenc...

Embodiment 2

[0090] A heavy-duty tractor balance bridge support casting of this embodiment has a chemical composition ratio of C3.55%, Si2.7%, Mn0.50%, P0.035%, S0.018%, Mg0.050%, Cr0.09%, Ni0.06%, Mo0.12%, Cu0.7%, Sn0.01%, Al0.01%, Ti0.035%, V0.008%, Ba0.002%, Ca0.002%, RE0.018%, N0.0025%, O0.0012%.

[0091] Prepare according to the following production process:

[0092] Step 1: Select high-quality pig iron with a carbon content of 4.5%, high-quality carbon, low-alloy and low-impurity briquette scrap, calcined high-purity silicon carbide, graphite-type low-sulfur carburizer, high-quality long-term special inoculant, high-magnesium spheroidized wire, Pearlitic inoculated filaments and high-strength ductile iron alloy additives are used as raw materials.

[0093] Step 2: Manufacture a special model for castings of high-strength ductile iron heavy-duty tractor balance bridge bracket and a sand box with adjustable temperature control film.

[0094] Step 3: The raw materials are smelted int...

Embodiment 3

[0106] An engine mount bracket casting in this embodiment has a chemical composition ratio of C3.80%, Si2.8%, Mn0.55%, P0.035%, S0.018%, Mg0.058%, Cr0. 1%, Ni0.07%, Mo0.15%, Cu0.8%, Sn0.02%, Al0.02%, Ti0.038%, V0.01%, Ba0.003%, Ca0.003%, RE0. 002%, N0.003%, O0.0015%.

[0107] Prepare according to the following production process:

[0108] Step 1: Select high-quality pig iron with a carbon content of 4.5%, high-quality carbon, low-alloy and low-impurity briquette scrap, calcined high-purity silicon carbide, graphite-type low-sulfur carburizer, high-quality long-term special inoculant, high-magnesium spheroidized wire, Pearlitic inoculated filaments and high-strength ductile iron alloy additives are used as raw materials.

[0109] Step 2: Manufacture a special model for castings of high-strength ductile iron heavy-duty tractor balance bridge bracket and a sand box with adjustable temperature control film.

[0110] Step 3: The raw materials are smelted into molten iron in an i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength, high-elongation ductile iron alloy. The alloy adopts a special composition ratio; the alloy has a metallographic structure composed of austenite and pearlite. The invention also discloses the preparation method of the above alloy. Through raw material selection, mold preparation, smelting, component adjustment, spheroidization treatment, pouring and heat treatment, a metallographic structure composed of austenite and pearlite is prepared as the matrix structure. Ductile iron alloy. The invention has high strength, good toughness, excellent fatigue strength, impact toughness and good processing performance. The indoor temperature tensile strength can reach more than 900MPa, the yield strength can reach more than 600MPa, and the elongation can reach more than 10%. Also cheaper.

Description

technical field [0001] The invention belongs to the technical field of casting alloys, and in particular relates to a high-strength, high-elongation ductile iron alloy and a preparation method thereof. Background technique [0002] Ductile cast iron is a high-strength cast iron material developed in the 1950s. Its comprehensive performance is close to that of steel. It is based on its excellent performance that it has been successfully used to cast some complex stress, strength, toughness, and wear resistance. Parts with high performance requirements. Spheroidal graphite cast iron is obtained through spheroidization and inoculation treatment, which effectively improves the mechanical properties of cast iron, especially improves plasticity and toughness, thereby obtaining higher strength than carbon steel. Ductile iron castings are used in all major industrial sectors where high strength, ductility, toughness, wear resistance, resistance to severe thermal and mechanical shoc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C37/10C22C33/04C21C1/10C21D5/00
CPCC22C37/10C22C33/04C21C1/10C21D5/00
Inventor 冀元贵罗铖
Owner HUBEI XINGYUAN SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka