Anti-aging tea polyphenol, naringin or emodin modified chinlon master batch and preparation process thereof

A preparation process, the technology of tea polyphenols, applied in the field of fiber manufacturing, can solve the problems of easy wash-off, poor antibacterial rate of nylon masterbatch, poor aging resistance of nylon masterbatch, etc., and achieve good aging resistance and washing resistance , good antibacterial effect

Active Publication Date: 2020-09-01
BYHERB BIGBIO TECH QINGDAO CO LTD +1
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The above patented technology cannot be used in the modified nylon masterbatch process of tea polyphenols, naringin or emodin, but it cannot achieve effective modifier immobilization, and the spinning performance of the masterbatch is also greatly affected
[0009] Existing technology For the technology of modifying nylon masterbatch with tea polyphenols, naringin or emodin, the prior art has the following technical defects: (1) Nylon modified by tea polyphenols, naringin or emodin The masterbatch does not have far-infrared function; (2) The nylon masterbatch modified by tea polyphenols, naringin or emodin has poor aging resistance; (3) The modified tea polyphenols, naringin or emodin The nylon masterbatch has poor antibacterial rate and is easy to wash off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The preparation method of loading agent:

[0031] (1) Raw material pretreatment

[0032] The raw materials for the preparation of the loading agent include: montmorillonite, zeolite powder, aerogel, porous nano-SiO 2 ;

[0033] Montmorillonite used: pH value is 7, density is 2-2.4g / cm 3 , the apparent viscosity is 24-25 mPa.s, and the water content is 9%;

[0034] Zeolite powder used: density 1.9-2.6 g / cm 3 , bulk density 1.6 g / cm 3 , porosity 58-64%, water content 10%.

[0035] Spray the montmorillonite with water until the water content is 18%; then import it into a microwave device and treat it for 2.5 minutes under the condition of microwave frequency 12GH; export it after microwave treatment, cool the montmorillonite to 85°C at a rate of 2°C / min, and then Imported into a drying device, dried at 85°C to a water content of 9%; then the dried montmorillonite was naturally cooled to 25°C for later use.

[0036] Spray the zeolite powder with water until the water...

Embodiment 2

[0046] Example 2 A preparation process of tea polyphenol modified nylon masterbatch

[0047] Include the following steps:

[0048] Step 1. Modifier Dissolution

[0049] Add a certain amount of deionized water into a beaker, add tea polyphenol powder, and stir at a speed of 2500 rpm for 30 minutes to dissolve completely, with a bath ratio of 1:10; to obtain a tea polyphenol solution.

[0050] The tea polyphenols: active ingredient content ≥ 50%, water content ≤ 7%.

[0051] Step 2, preparation of loading agent

[0052] The preparation of the loading agent was carried out according to the method of Example 1.

[0053] Step 3, preparation of functional modifier

[0054] Mix the loading agent with the tea polyphenol solution, start stirring at a speed of 30r / min, and stir for 30 minutes, so that the tea polyphenols can fully enter the interior of the porous material, and the obtained nanocomposite material is the functional modifier containing tea polyphenols. The mass ratio ...

Embodiment 3

[0060] Example 3 A preparation process of naringin-modified nylon masterbatch

[0061] Include the following steps:

[0062] Step 1. Modifier Dissolution

[0063] Add a certain amount of deionized water into a beaker, add naringin powder, heat in a water bath to 50°C, stir until completely dissolved, and the bath ratio is 1:5; obtain a naringin solution.

[0064] The naringin powder: active ingredient content ≥ 98%, water content ≤ 5%.

[0065] Step 2, preparation of loading agent

[0066] The preparation of the loading agent was carried out according to the method of Example 1.

[0067] Step 3, preparation of functional modifier

[0068] Mix the loading agent with the naringin solution, start stirring at a speed of 60r / min, and stir for 120min, so that the naringin fully enters the interior of the porous material, and the obtained nanocomposite is the functional modifier containing naringin. The mass ratio of the nano microspheres to the naringin solution is 1:19.

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation process of an anti-aging tea polyphenol, naringin or emodin modified chinlon master batch. The preparation process comprises a loading agent preparation step, andthe preparation of a loading agent comprises the steps of raw material pretreatment, blending, heat treatment, elution and drying. In the blending step, preparation raw materials of the loading agentare added into a stirring kettle and stirred for 8-15 min at the rotating speed of 1200-1500 rpm to obtain a mixed material A, the mixed material A is mixed with far infrared nano-powder to obtain a mixed material B, and the mixed material B is subjected to ultrasonic treatment for 28-32min at the temperature of 28-30 DEG C and at the ultrasonic frequency of 33-38 KHZ to obtain blended powder. Theheat treatment comprises the steps of mixing the blended powder with a treatment liquid, heating the mixture to 99-100 DEG C at a rate of 5-6 DEG C / min, and carrying out heat preservation and heat treatment for 30-40 minutes. The modified chinlon master batch prepared by the method is good in antibacterial property and remarkable in ageing resistance.

Description

technical field [0001] The invention belongs to the technical field of fiber manufacturing, and in particular relates to an anti-aging tea polyphenol, naringin or emodin modified nylon masterbatch and a preparation process thereof. Background technique [0002] Modified nylon is a kind of engineering plastics, which is a granular product formed by changing the physical properties of nylon raw materials. The output of such products is modified according to the needs of some manufacturers. [0003] Modified nylon generally includes: reinforced nylon, toughened nylon, wear-resistant nylon, halogen-free flame-retardant nylon, conductive nylon, flame-retardant nylon and so on. 1. Thermal properties: glass transition temperature (Tg) and melting point (Tm); high heat distortion temperature (HDT); high long-term service temperature (UL-746B); wide service temperature range; small thermal expansion coefficient. 2. Mechanical properties: high strength, high mechanical modulus, low ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/22C08L77/00C08L33/26C08L71/02C08K9/12C08K5/13C08K5/1545C08K5/05D01F1/09D01F1/10D01F6/90
CPCC08J3/226D01F1/09D01F1/103D01F1/10D01F6/90C08J2477/00C08J2423/26C08J2471/02C08J2377/00C08K9/12C08K5/13C08K5/1545C08K5/05
Inventor 黄效华郑来久蔡强姜义军甄丽姜亚明伏广伟刘宇
Owner BYHERB BIGBIO TECH QINGDAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More