Transmutation overglaze and preparation method thereof, and porcelain

A kiln-changing glaze and surface glaze technology, which is applied in the field of ceramics, can solve the problems of rough glaze surface, poor thermal stability, and poor high-temperature fluidity, and achieve the effects of simple production process, good firing performance, and less environmental pollution

Inactive Publication Date: 2020-08-25
潮州市荣嘉陶瓷有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many types of surface glazes in production. For example, the tiles of the prior art have different requirements for the frit in the glazing procedure, and the performance of the glaze is different. The amount of glaze must have a certain thickness. , poor thermal stability, easy to produce color difference, easy to deform the product, small scope of application, poor high temperature fluidity, resulting in rough glaze, poor antifouling performance, low yield, etc. In addition, the transparency and smoothness of the product need to be further improved space

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The embodiment of the present invention provides a kind of kiln-changing glaze glaze, its components and the mass percentage of each component are: frit 70%~75%, kaolin 5%~8%, zinc oxide 4.5%~6.5%, barium carbonate 1.2% %~2.5%, titanium dioxide 4.5%~6%, bone meal 2.5%~4.5%, ferric oxide 1%~2%, cobalt oxide 1%~2%.

[0021] According to the surface glaze prepared by the surface glaze formula of this embodiment, its chemical composition includes: SiO 2 、Al 2 o 3 , B 2 o 3 、Na 2 O, ZnO, TiO 2 , CaO, BaO, Fe 2 o 3 、Co 3 o 4 ,P 2 o 5 、K 2 O, MgO, MnO, Cl, ZrO 2 , SrO, SO 3 , Li 2 O. The weight percentage of the chemical composition of the surface glaze is: SiO 2 45%~50%, Al 2 o 3 9%~12%, B 2 o 3 8%~11%, Na 2 O 7%~9%, ZnO 4.5%~6.5%, TiO 2 4.5%~6%, CaO 2.2%~3.8%, BaO 1.2%~2.5%, Fe 2 o 3 1%~2%, Co 3 o 4 1%~2%, P 2 o 5 1%~2%, K 2 O 0.5%~1.0%, MgO 0.1%~0.2%, MnO 0.05%~0.1%, Cl 0.05%~0.1%, ZrO 2 0.03%~0.07%, SrO 0.03%~0.05%, SO 3 0.01%~0.05%, Li 2...

Embodiment 2

[0029] The embodiment of the present invention provides a kind of kiln-changing glaze glaze, its components and the mass percentage of each component are: frit 74.0%, kaolin 7.4%, zinc oxide 5%, barium carbonate 2.0%, titanium dioxide 5.2%, bone powder 3.5% %, ferric oxide 1.5%, cobalt oxide 1.4%.

[0030] The weight percentage of the top glaze prepared according to the above top glaze formula is: SiO 2 48.44%, Al 2 O3 11.01%, B 2 o 3 10.09%, Na 2 O 8.01%, ZnO 5.49%, TiO 2 5.20%, CaO 3.02%, BaO 2.00%, Fe 2o 3 1.50%, Co 3 o 4 1.40%, P 2 o 5 1.10%, K 2 O 0.92%, MgO 0.15%, MnO 0.07%, Cl 0.06%, ZrO 2 0.05%, SrO 0.04%, SO 3 0.03%, Li 2 O<0.01%; its discretion rate is lower than 1.44%.

[0031] The preparation method of present embodiment face glaze comprises steps:

[0032] Proportion weighing: Proportion weighing according to the formula of surface glaze raw materials;

[0033] Raw material ball milling: Put the prepared surface glaze raw materials into a bal...

Embodiment 3

[0039] The embodiment of the present invention provides a kind of kiln-changing glaze glaze, its components and the mass percentage of each component are: frit 70.0%, kaolin 6.6%, zinc oxide 7.0%, barium carbonate 2.0%, titanium dioxide 6.0%, bone meal 4.5% %, ferric oxide 2%, cobalt oxide 1.9%.

[0040] The weight percentage of the top glaze prepared according to the above top glaze formula is: SiO 2 45.05%, Al 2 O3 10.73%, B 2 o 3 8.26%, Na 2 O 8.71%, ZnO 7.0%, TiO 2 6.00%, CaO 3.78%, BaO 2.00%, Fe 2 o 3 2.00%, Co 3 o 4 1.90%, P 2 o 5 1.99%, K 2 O 0.81%, MgO 0.14%, MnO 0.08%, Cl 0.08%, ZrO 2 0.06%, SrO 0.05%, SO 3 0.02%, Li 2 O<0.01%; its discretion rate is lower than 1.35%.

[0041] The preparation method of present embodiment face glaze comprises steps:

[0042] Proportion weighing: Proportion weighing according to the formula of surface glaze raw materials;

[0043] Raw material ball milling: Put the prepared surface glaze raw materials into a ball m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a transmutation overglaze. The overglaze comprises the following components in percentage by mass: 70%-75% of frit, 5%-8% of kaolin, 4.5%-6.5% of zinc oxide, 1.2%-2.5% of barium carbonate, 4.5%-6% of titanium dioxide, 2.5%-4.5% of bone meal, 1%-2% of ferric oxide and 1%-2% of cobalt oxide. The invention further discloses a preparation method of the transmutation overglaze and porcelain. According to the transmutation overglaze and the preparation method thereof and the porcelain in the invention, the preparation method of the transmutation overglaze is simple in production process and low in environmental pollution; a unique overglaze formula is adopted, and through mutual cooperation and combined action of all the components and the content of the components, the overglaze is transparent and smooth in surface, good in glaze slip performance and good in firing performance; and an overglaze porcelain product is good in decorative effect, fine and smooth in glazesurface and good in texture. The invention belongs to the technical field of ceramics.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a kiln-transformed glaze, a preparation method thereof, and porcelain. Background technique [0002] Top glaze is a layer of enamel covering the surface or bottom glaze of ceramic products in the manufacturing process of ceramic products, which can resist corrosion and increase the decorative effect of products. At present, there are many types of surface glazes in production. For example, the tiles of the prior art have different requirements for the frit in the glazing procedure, and the performance of the glaze is different. The amount of glaze must have a certain thickness. , poor thermal stability, easy to produce color difference, easy to deform the product, small scope of application, poor high temperature fluidity, resulting in rough glaze, poor antifouling performance, low yield, etc. In addition, the transparency and smoothness of the product need to be further improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C04B41/89
CPCC03C8/20C03C2204/04C03C2205/02C04B41/52C04B41/89C04B41/504C04B41/0072C04B41/5022C04B41/4539C04B41/4543
Inventor 吴作明吴岱迅许腾曾利鹏蔡钊杰
Owner 潮州市荣嘉陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com