Steel pipe surface treating agent and anti-corrosion treatment method

A surface treatment agent and anti-corrosion treatment technology, applied in anti-corrosion coatings, special surfaces, pre-treated surfaces, etc., can solve the problems of saving investment and maintenance costs, no solutions, short service life, etc., to achieve a large product market, Conducive to maintenance and improvement of corrosion resistance

Inactive Publication Date: 2020-08-18
安徽唐道电子科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing steel pipes are highly corrosive, have a short service life, save investment and maintenance costs, and are difficult to construct
For related technical problems, no effective solutions have been proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A steel pipe anticorrosion treatment method is carried out in the following order:

[0021] (1) Pickling the steel pipe first;

[0022] (2) Wash the cleaned steel pipe with water and let it dry naturally;

[0023] (3) Dip the cleaned and dried steel pipe into the molten surface treatment agent to form an anti-corrosion coating. The surface treatment agent is composed of the following components and proportioned by weight percentage: polytetrafluoroethylene 6%, two Methylformamide 12%, Trifluoroacetyl Chloride 4%, Triethyl Benzene Tricarboxylate 3%, Zinc Undecylenate 6%, Carbon Nanotube 6%, Trifluoroethyl Acrylate 6%, Nano Diamond 8% , magnesium reagent 2%, dioctyl sebacate 5%, diphenylphosphoryl chloride 2%, amino 8%, alkoxy 12%, silane 20%.

[0024] (4) Put the soaked steel pipe into the furnace for drying, raise the furnace temperature to 120°C, keep it for 9 hours, then raise the furnace temperature to 180°C, keep it for 24 hours, and cool down to room temperature ...

Embodiment 2

[0030] A steel pipe anticorrosion treatment method is carried out in the following order:

[0031] (1) Pickling the steel pipe first;

[0032] (2) Wash the cleaned steel pipe with water and let it dry naturally;

[0033] (3) Dip the cleaned and dried steel pipe into the molten surface treatment agent to form an anti-corrosion coating. The surface treatment agent is composed of the following components and proportioned by weight percentage: polytetrafluoroethylene 9%, two Methylformamide 11%, Trifluoroacetyl Chloride 5%, Triethyl Benzene Tricarboxylate 3%, Zinc Undecylenate 4%, Carbon Nanotube 8%, Trifluoroethyl Acrylate 5%, Nano Diamond 7% , magnesium reagent 2%, dioctyl sebacate 5%, diphenylphosphoryl chloride 3%, amino 8%, alkoxy 12%, silane 18%.

[0034] (4) Put the soaked steel pipe into the furnace for drying, raise the temperature of the furnace to 180°C, keep it for 16 hours, then raise the temperature of the furnace to 320°C, keep it for 28 hours, and cool down to ro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel pipe surface treating agent and an anti-corrosion treatment method. The surface treating agent is composed of the following components in percentage by weight: 3%-9% ofpolytetrafluoroethylene, 6%-12% of dimethyl formamide, 3%-6% of trifluoroacetyl chloride, 1%-3% of triethyl phenyltricarboxylate, 3%-6% of zinc undecylenate, 6%-8% of carbon nanotubes, 2%-6% of trifluoroethyl acrylate, 5%-8% of nano diamond, 1%-3% of a magnesium reagent, 3%-6% of dioctyl sebacate, 1%-3% of diphenyl phosphoryl chloride, 2%-8% of amino, 6%-12% of alkoxy and 10%-20% of silane. The steel pipe surface treating agent can effectively prevent a steel pipe from being corroded, the service life of the steel pipe is prolonged, the strength of the steel pipe is effectively improved, andapplication prospects are good.

Description

technical field [0001] The invention relates to the technical field of pipelines, in particular to a steel pipe surface treatment agent and an anti-corrosion treatment method. Background technique [0002] Steel pipes have a hollow section whose length is much greater than the diameter or circumference of steel. According to the cross-sectional shape, it is divided into circular, square, rectangular and special-shaped steel pipes; according to the material, it is divided into carbon structural steel pipes, low alloy structural steel pipes, alloy steel pipes and composite steel pipes; Steel pipes for thermal equipment, petrochemical industry, machinery manufacturing, geological drilling, high-pressure equipment, etc.; according to the production process, they are divided into seamless steel pipes and welded steel pipes, among which seamless steel pipes are divided into hot-rolled and cold-rolled (drawn) Two kinds, welded steel pipe is divided into straight seam welded steel ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/06C09D4/02C09D5/08C09D7/61C09D7/63B05D7/14B05D7/24B05D3/10B05D5/00
CPCB05D3/102B05D5/00B05D7/14B05D7/24C09D4/06C09D5/08C09D7/61C09D7/63
Inventor 赵凯
Owner 安徽唐道电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com