A kind of polyester high-strength fishing net with self-luminous function and preparation method thereof

A technology of self-illumination and polyester, which is applied in the manufacture of rayon, complete sets of equipment for the production of rayon, stretching spinning, etc. It can solve the problems of difficulty in guaranteeing the strength of self-luminous polyester high-strength yarn, poor dispersion of luminescent powder, and poor light storage effect of fibers and other problems, to avoid poor mechanical properties, long afterglow time, and low cost

Active Publication Date: 2021-12-28
JIANGSU HENGKE ADVANCED MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the luminescent powder is directly added as an additive to the polyester and then spun into filaments. The problem of poor dispersion of the luminescent powder in polyester is common, which leads to poor light storage effect and low strength of the fiber.
In order to obtain fibers with higher strength, high-strength stretching in the later stage is required, but it is difficult to directly obtain high-strength stretching of polyester fibers with luminescent powder, so it is necessary to obtain high-strength polyester filaments by using multi-stage stretching, but Since the product specification of high-strength polyester filament is usually greater than 550dtex, the production cost is higher if it is smaller than this specification, and it is usually drawn at high speed, the total number of drafting is only two levels, and the strength of self-luminous polyester high-strength filament is difficult to guarantee

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyester high-strength fishing net with self-luminous function and preparation method thereof
  • A kind of polyester high-strength fishing net with self-luminous function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] Such as Figure 1-2 The present invention provides a kind of preparation method of polyester high-strength fishing net thread with self-illuminating function, comprising the following steps:

[0032] 1) The alkaline earth aluminate luminescent material and the alkaline earth silicate luminescent material are mixed and compounded according to the mass ratio of 1:0.5~0.8, and the mixed luminescent powder is obtained through grinding and sieving;

[0033] 2) After uniformly mixing ordinary polyester chips with the mixed luminescent powder, the self-luminescent polyester masterbatch is obtained through twin-screw melt extrusion and granulation, and the self-luminescent polyester masterbatch is pre-crystallized and dried to Moisture content <25ppm; the mass ratio of the mixed luminescent powder to the common polyester chips is 1~3:7~9;

[0034] 3) Put the self-luminous polyester masterbatch obtained through step 2) into a screw extruder for melt extrusion to obtain a self-l...

Embodiment 1

[0043] 1. Preparation of self-luminous polyester masterbatch:

[0044] 10 parts by weight of alkaline earth aluminate luminescent material SrAl 2 o 4 :Eu 2+ , Dy 3+ and 6 parts by weight of alkaline earth silicate luminescent material Sr 3 MgSi 2 o 8 :Eu 2+ , Dy 3+ Mix and compound, pass through a 325-mesh sieve after being ground by a ball mill to obtain a mixed luminescent powder with a particle size of 40 μm, take 12 parts by weight of the mixed luminescent powder and 48 parts by weight of polyester chips with an intrinsic viscosity of 0.66dl / g and mix evenly , obtained from luminous polyester masterbatch by twin-screw melt extrusion and granulation.

[0045] 2. Spinning self-luminous polyester FDY filament:

[0046] according to figure 1 Melt direct spinning polyester FDY production flow chart with screw on-line adding device for spinning self-luminous polyester FDY filaments, specifically:

[0047] (1) Put the self-luminous polyester masterbatch into the chip d...

Embodiment 2

[0054] 1. Preparation of self-luminous polyester masterbatch:

[0055] 10 parts by weight of alkaline earth aluminate luminescent material SrAl 2 o 4 :Eu 2+ , Dy 3+ and 5 parts by weight of alkaline earth silicate luminescent material Sr 3 MgSi 2 o 8 :Eu 2+ , Dy 3+ Mix and compound, pass through a 1340-mesh sieve after being ground by a ball mill to obtain a mixed luminescent powder with a particle size of 10 μm, take 6 parts by weight of the mixed luminescent powder and 54 parts by weight of polyester chips with an intrinsic viscosity of 0.64dl / g and mix evenly , obtained from luminous polyester masterbatch by twin-screw melt extrusion and granulation.

[0056] 2. Spinning self-luminous polyester FDY filament:

[0057] according to figure 1 Melt direct spinning polyester FDY production flow chart with screw on-line adding device for spinning self-luminous polyester FDY filaments, specifically:

[0058](1) Put the self-luminous polyester masterbatch into the chip dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyester high-strength fishing net thread with self-luminous function and a preparation method thereof, comprising: compounding alkaline earth aluminate luminescent materials and alkaline earth silicate luminescent materials to obtain mixed luminescent powder; The powder self-luminous polyester masterbatch melt and ordinary polyester melt are mixed dynamically and statically to obtain a mixed melt containing low-concentration luminescent powder; by adjusting the spinning parameters, a large amorphous area and low crystallinity are produced. It is more suitable for self-luminous polyester FDY filaments of multi-stage drafting, and then low-speed, multi-stage drafting treatment. The polyester high-strength fishing net yarn with self-luminous function prepared by the present invention has a breaking strength of >6.5cN / dtex, a boiling water shrinkage rate of <4%, and can continue to glow in the dark for more than 12 hours after being fully illuminated.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polyester high-strength fishing net yarn with self-luminous function and a preparation method thereof. Background technique [0002] In pelagic fisheries, fishing nets are usually used for one-time use. After fishing on the boat, the fishing nets are cut open, the fish in the nets are sorted and put into fish bins, and new fishing nets are replaced when the nets are lowered again. Most deep-sea fish have phototaxis. If the fishing net can emit weak light under the water surface, especially at night, it can attract more fish, greatly increase the fishing output of each net, and improve economic benefits. [0003] After absorbing all kinds of visible light for 10-20 minutes, the high-efficiency light-storing luminescent powder can continue to emit light in the dark for more than 12 hours, and has excellent low-light display and indication functions. In the prior art, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10D01D1/04D01D5/14D01D13/00
CPCD01F6/92D01F1/10D01D13/00D01D1/04D01D5/14
Inventor 赵军柳敦雷刘彪
Owner JIANGSU HENGKE ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products