A kind of resin grinding wheel and preparation method thereof

A technology of resin grinding wheel and phenolic resin solution, which is applied in the direction of manufacturing tools, metal processing equipment, abrasives, etc., can solve problems such as poor flatness, and achieve the effects of improving service life, high melting point, and increasing bonding strength

Active Publication Date: 2021-07-02
郑州九天工贸有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in grinding metal with grinding wheels, generally the higher the grinding ratio, the greater the grinding vibration amplitude, the rougher the grinding surface of the workpiece, and the poorer flatness, while the lower the grinding ratio, the smaller the grinding vibration amplitude, and the smoother the grinding surface of the workpiece

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of resin grinding wheel and preparation method thereof
  • A kind of resin grinding wheel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of resin grinding wheel, its raw material ratio is shown in Table 1.

[0041] S1. Mix brown corundum, white corundum and green silicon carbide evenly to obtain abrasives;

[0042] Among them, Al in brown corundum 2 o 3 The weight content is 95%; Al in white corundum 2 o 3 The weight content of SiC in green silicon carbide is 98%; the weight content of SiC in green silicon carbide is 97%.

[0043] S2, mixing cryolite, pyrite, and titanium dioxide evenly to obtain a mixture a;

[0044] Among them, Na in cryolite 3 AlF 6 The weight content is 97%; FeS in pyrite 2 The weight content is 75%; TiO2 in titanium dioxide 2 The weight content is 97%.

[0045]S3. In the case of constant stirring, spray the phenolic resin liquid into the abrasive, then add floating beads and alkaline earth oxide, then add the mixture a and wetting agent in turn, and mix evenly to obtain the mixture b;

[0046] Among them, the phenolic resin solution is selected from PF5401; the floa...

Embodiment 2

[0053] A kind of resin grinding wheel, its raw material ratio is shown in Table 1.

[0054] S1. Mix brown corundum, white corundum and green silicon carbide evenly to obtain abrasives;

[0055] Among them, Al in brown corundum 2 o 3 The weight content is 95%; Al in white corundum 2 o 3 The weight content of SiC in green silicon carbide is 98%; the weight content of SiC in green silicon carbide is 97%.

[0056] S2, mixing cryolite, pyrite, and titanium dioxide evenly to obtain a mixture a;

[0057] Among them, Na in cryolite 3 AlF 6 The weight content is 97%; FeS in pyrite 2 The weight content is 75%; TiO2 in titanium dioxide 2 The weight content is 97%.

[0058] S3. In the case of constant stirring, spray the phenolic resin solution into the abrasive, then add floating beads and alkaline earth oxide, then add the mixture a, synergist, and wetting agent in sequence, and mix evenly to obtain the mixture b;

[0059] Among them, the phenolic resin solution is selected fr...

Embodiment 3

[0066] A kind of resin grinding wheel, its raw material ratio is shown in Table 1.

[0067] S1. Mix brown corundum, white corundum and green silicon carbide evenly to obtain abrasives;

[0068] Among them, Al in brown corundum 2 o 3 The weight content is 95%; Al in white corundum 2 o 3 The weight content of SiC in green silicon carbide is 98%; the weight content of SiC in green silicon carbide is 97%.

[0069] S2, mixing cryolite, pyrite, and titanium dioxide evenly to obtain a mixture a;

[0070] Among them, Na in cryolite 3 AlF 6 The weight content is 97%; FeS in pyrite 2 The weight content is 75%; TiO2 in titanium dioxide 2 The weight content is 97%.

[0071] S3. In the case of constant stirring, spray the phenolic resin solution into the abrasive, then add floating beads and alkaline earth oxide, then add the mixture a, synergist, and wetting agent in sequence, and mix evenly to obtain the mixture b;

[0072] Among them, the phenolic resin solution is selected fr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
magnetic flux densityaaaaaaaaaa
diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a resin grinding wheel and a preparation method thereof, belonging to the technical field of resin grinding wheel production. The raw materials of the resin grinding wheel include abrasive, phenolic resin liquid, phenolic resin powder, cryolite, pyrite, titanium dioxide, floating beads, alkaline earth oxide ,lubricant. The resin grinding wheel, through the synergistic effect between the raw materials, makes the resin grinding wheel have a higher workpiece wear and grinding ratio under the condition of the polished surface of the workpiece and no black spots, and also has a lower grinding wheel loss. The service life of the resin grinding wheel is improved, and the resin grinding wheel also has good compressive strength and hardness, so that the resin grinding wheel has a good use effect. The preparation method of the resin grinding wheel, by adding a circular magnetic field, twice machine pressing, and twice curing, the raw materials are fully reacted and self-combined, the density and bonding strength of the resin grinding wheel are increased, and the resin grinding wheel shows good comprehensive performance. , but also has the advantage of being easy to control.

Description

technical field [0001] The invention relates to the technical field of resin grinding wheel production, more specifically, it relates to a resin grinding wheel and a preparation method thereof. Background technique [0002] Grinding wheel is the main tool for grinding. It is a porous substance composed of abrasives, fillers and binders. It is widely used in metallurgy, construction, railway and other fields. It is mainly used for cutting and polished. At present, in grinding metal with grinding wheels, generally the higher the grinding ratio, the greater the grinding vibration amplitude, the rougher the workpiece grinding surface and poor flatness, and the lower the grinding ratio, the smaller the grinding vibration amplitude, and the smoother the workpiece grinding surface. With the continuous advancement of science and technology, the requirement for the smoothness of the polished surface of the workpiece is increased, and there is an urgent need for a method to improve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D3/28
CPCB24D3/285
Inventor 李蒙
Owner 郑州九天工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products