EVA hot melt adhesive with high bonding strength

A technology of bonding strength and hot melt adhesive, which is applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., and can solve poor heat resistance, low bonding strength, and limited application range And other problems, to achieve excellent aging resistance, improve bonding performance, improve the effect of bonding strength

Active Publication Date: 2019-10-15
HUANGSHAN XINDECHENG GLUE IND CO LTD
View PDF12 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ethylene-vinyl acetate (EVA) hot melt adhesives have the characteristics of excellent weather resistance, non-toxicity, no pollution, and simple preparation methods. , poor heat resistance, which seriously limits its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • EVA hot melt adhesive with high bonding strength
  • EVA hot melt adhesive with high bonding strength

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An EVA hot-melt adhesive with high bonding strength, its raw materials include by weight: 100 parts of EVA resin, 19 parts of SBS thermoplastic elastomer, 4 parts of hydroxyl-terminated polyurethane resin, 0.9 part of polyacrylamide, 2-vinyl-1 - 0.15 parts of benzofuran, hydrogenated C 5 15 parts of petroleum resin, 5 parts of polyethylene wax, 1.7 parts of paraffin wax, 0.15 parts of antioxidant, 0.01 part of benzoyl peroxide, 0.07 part of europium acrylate, 28 parts of filler.

Embodiment 2

[0022] A kind of EVA hot-melt adhesive with high bonding strength, its raw materials include by weight: 100 parts of EVA resin, SBS thermoplastic elastomer YH-7928 parts, 7 parts of hydroxyl-terminated polyurethane resin, 1.3 parts of polyacrylamide, 2-vinyl -0.4 parts of 1-benzofuran, hydrogenated C 5 11 parts of petroleum resin, 9 parts of polyethylene wax, 3 parts of paraffin wax, 10100.34 parts of antioxidant, 0.1 part of benzoyl peroxide, 0.01 part of europium acrylate, 21 parts of filler;

[0023] Wherein, the mass content of VA in the EVA resin is 40wt%;

[0024] The filler is a mixture of nano-titanium dioxide and modified nano-calcium carbonate, and the weight ratio of modified nano-calcium carbonate to nano-titanium dioxide is 5:4; the modified nano-calcium carbonate is prepared according to the following process: using a silane coupling agent KH-570 is used as a modifier to modify nano-calcium carbonate to obtain coupling agent-modified nano-calcium carbonate; add ...

Embodiment 3

[0026] An EVA hot-melt adhesive with high bonding strength, its raw materials include by weight: 100 parts of EVA resin, 12 parts of SBS thermoplastic elastomer YH-792, 11 parts of hydroxyl-terminated polyurethane resin, 0.2 parts of polyacrylamide, 2-ethylene 0.8 parts of base-1-benzofuran, hydrogenated C 5 11.5 parts of petroleum resin, 13 parts of polyethylene wax, 1 part of paraffin wax, 0.2 part of antioxidant 168, 0.14 part of antioxidant DLTP, 0.07 part of benzoyl peroxide, 0.02 part of europium acrylate, 13 parts of filler;

[0027] Wherein, the mass content of VA in the EVA resin is 28wt%;

[0028]The filler is a mixture of nano-titanium dioxide and modified nano-calcium carbonate, and the weight ratio of modified nano-calcium carbonate to nano-titanium dioxide is 12:2; the modified nano-calcium carbonate is prepared according to the following process: using a silane coupling agent KH-570 is used as a modifier to modify nano-calcium carbonate to obtain coupling agent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an EVA hot melt adhesive with high bonding strength. The EVA hot melt adhesive with high bonding strength comprises the following raw materials in parts by weight: 100 parts ofEVA resin, 8-19 parts of SBS thermoplastic elastomer, 4-11 parts of hydroxyl-terminated polyurethane resin, 0.2-1.3 parts of polyacrylamide, 0.15-0.8 part of 2-vinyl-1-benzofuran, 11-15 parts of hydrogenated C5 petroleum resin, 5-13 parts of polyethylene wax, 1-3 parts of paraffin wax, 0.12-0.34 part of an antioxidant, 0.01-0.1 part of benzoyl peroxide, 0.01-0.07 part of europium acrylate and 13-28 parts of filler. The EVA hot melt adhesive with high bonding strength is high in bonding strength, good in high temperature resistance and excellent in aging resistance.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an EVA hot-melt adhesive with high bonding strength. Background technique [0002] Hot melt adhesive is a kind of adhesive that uses thermoplastic resin as the base material and adds a small amount of plasticizer, tackifier, filler, antioxidant, etc., and uses temperature changes for bonding. It has many excellent properties, such as 100% solid, short curing time, easy to operate and suitable for continuous industrial production, etc., it has been widely used in home decoration, perfect binding, plastic bonding and other fields. [0003] According to different main resins, hot melt adhesives can be divided into ethylene-vinyl acetate, styrene block elastomers, polyolefins, polyamides, polyesters, etc. Ethylene-vinyl acetate (EVA) hot melt adhesives have the characteristics of excellent weather resistance, non-toxicity, no pollution, and simple preparation methods. , The defec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/00C09J4/02C09J4/06C09J11/08C09J11/04
CPCC09J4/00C09J4/06C09J11/08C09J11/04
Inventor 王峰汪十荣程妤
Owner HUANGSHAN XINDECHENG GLUE IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products