Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

High-end bearing steel material for machine tool bearing ring and manufacturing method of high-end bearing steel material for machine tool bearing ring

A technology for bearing rings and manufacturing methods, which is applied in the field of special steel smelting and forging, can solve problems such as carbide segregation and unsatisfactory properties of steel materials, and achieve the effects of increased carbide level, uniform carbide distribution, and high purity

Active Publication Date: 2019-09-20
建龙北满特殊钢有限责任公司
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the carbides in the steel material for bearing rings are segregated and distributed in a network shape, the performance of the steel material cannot meet the requirements of high-end CNC machine tools, the present invention provides a high-end bearing steel material for machine tool bearing rings and its manufacturing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-end bearing steel material for machine tool bearing ring and manufacturing method of high-end bearing steel material for machine tool bearing ring
  • High-end bearing steel material for machine tool bearing ring and manufacturing method of high-end bearing steel material for machine tool bearing ring
  • High-end bearing steel material for machine tool bearing ring and manufacturing method of high-end bearing steel material for machine tool bearing ring

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment provides a high-end bearing steel material for machine tool bearing rings, the chemical components contained include C: 0.93-0.98%, Si: 0.15-0.35%, Mn: 0.25-0.45%, Cr: 1.45~1.60%, Ni: 0.05~0.10%, Mo: 0.02~0.08%, Al: 0.015~0.035%, Cu: 0.06~0.10%, P≤0.010%, S≤0.008%, Nb: 0.010~0.045%, Y≤0.020%, Ce≤0.010%, Ti≤0.0015%, O≤0.0020%, As≤0.040%, Sn≤0.030%, Sb≤0.0050%, Pb≤0.0020%, and Si+Mn+Cr≥2.0%, The rest is Fe and unavoidable impurities.

[0046] Carbon is an important element that affects the performance of steel, and is one of the important elements to ensure that bearing steel can have sufficient hardenability, hardness and wear resistance. The carbon strengthening effect is very high, the carbon content in the steel increases, the yield point and tensile strength increase, but the toughness is significantly reduced. In order to improve the safety and reliability of the bearing steel, and consider controlling the carbon segregation of the steel ingot to im...

Embodiment 2

[0056] This embodiment provides a method for manufacturing high-end bearing steel materials for bearing rings of machine tools. The manufacturing method includes electric furnace→LF refining and VD process→die casting→hot delivery / cover cooling→heating and rolling→slow cooling→ball annealing;

[0057] In the electric furnace process:

[0058] Load pig iron, molten iron or steel material into the electric furnace, release the oxidized slag when the molten steel temperature is ≥1580°C and the C content is ≥0.30%, and start tapping the electric furnace. Slag, aluminum ingots, alloys and lime;

[0059] In the LF refining and VD process:

[0060] After the molten steel reaches the refining position, the temperature is raised to 1550°C, and ferrosilicon and new composite slag are added to form slag. After the slag is melted, diffusion deoxidizer is added in batches for slagging. When the slag reaches the refining slag system, that is, CaO 46-55% , SiO 2 ≤7%, Al 2 o 3 32~38%, M...

Embodiment 3

[0068] The difference between this embodiment and Embodiment 2 is only that in the electric furnace process of the manufacturing method of the high-end bearing steel material for the bearing ring of the machine tool in the present embodiment:

[0069] Put pig iron, molten iron or iron and steel materials into the electric furnace according to the weight ratio of 4:6, and the iron and steel materials use non-Ti-containing steel grade materials; when the molten steel temperature is ≥ 1580 °C and the C content is ≥ 0.30%, the oxidation slag is released, and start Electric furnace tapping, the amount of steel remaining in the electric furnace is more than 7 tons during the tapping process, to prevent the oxidation slag from being carried out during the tapping process, if the oxidation slag is brought in during the tapping process, the FeO, P in the oxidation slag 2 o 5 、TiO 2 It will be reduced to P and Ti during the refining process, resulting in the return of phosphorus and ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-end bearing steel material for a machine tool bearing ring and a manufacturing method of the high-end bearing steel material for the machine tool bearing ring, and belongs to the technical field of special steel smelting forging. The high-end bearing steel material aims to solve the problem that the performance of the steel material cannot meet the requirement of a high-end numerical control machine tool due to the fact that the carbide inside the steel material for the bearing ring is segregated and distributed in a mesh mode, the steel material is caused not to meet the requirement of the high-end numerical control machine tool, the invention provides the high-end bearing steel material for the machine tool bearing ring and the manufacturing method of the high-end bearing steel material for the machine tool bearing ring, and comprises the following steps of electric furnace, LF refining and VD process, die casting, hot charging / cover cooling, heating rolling, slow cooling, and spheroidizing annealing. According to the steel material and the method, Ni, Mo and rare earth element are added on the basis of existing bearing steel, the content of Al and Cu is strictly controlled, and a good mechanical property index is provided for the steel material; the carbide in the manufacturing process is effectively diffused, the carbide level of the steel material is improved, the steel material for the bearing ring of the machine tool has a high elastic limit, tensile strength, contact fatigue strength and wear resistance, and can effectively reduce the phenomena of fatigue peeling, blocking and the like.

Description

technical field [0001] The invention belongs to the technical field of special steel smelting and forging, and in particular relates to a high-end bearing steel material for machine tool bearing rings and a manufacturing method thereof. Background technique [0002] With the rapid development of numerical control technology, the technology of machine tool industry is also developing rapidly. Among them, high-speed machining can effectively improve the machining efficiency of machine tools and shorten the machining cycle of workpieces. This requires the machine tool spindle and its related components to meet the needs of high-speed machining. At present, the spindle bearings of CNC machine tools are basically limited to four structural types: angular contact ball bearings, cylindrical roller bearings, two-way thrust angular contact ball bearings and tapered roller bearings. [0003] The bearing ring is a ring-shaped part of a radial rolling bearing with one or several racew...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/06C22C38/42C22C38/48C21C5/52C21C7/06C21C7/10C21D8/00C21D1/32
CPCC21C5/52C21C7/06C21C7/10C21D1/32C21D8/005C21D2211/005C21D2211/009C22C38/005C22C38/02C22C38/04C22C38/06C22C38/42C22C38/44C22C38/48Y02P10/20
Inventor 熊洪进陈列董贵文李彬王强马忠存陈迦杉杨平
Owner 建龙北满特殊钢有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com