High-friction-coefficient polyamide material and preparing method and application thereof

A high friction coefficient, polyamide technology, applied in the field of wear-resistant materials, can solve the problems of small friction damping, increased damping and energy dissipation capacity, and complexity of side bearing wear plates, and achieve good wear resistance and high dynamic friction coefficient. Effect

Active Publication Date: 2019-06-28
JINYOUNG XIAMEN ADVANCED MATERIALS TECH CO LTD
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, semi-crystalline polyamide PA6 is more and more widely used in rail transit, automobile, electrical and other fields. However, these fields also have high requirements for the friction coefficient of materials. Existing polyamide materials meet the requirements of wear resistance. Under the premise that the coefficient of dynamic friction is less than 0.2, the frictional damping of side bearing wear plates used on trains using such materials is very small, and it often takes longer to reduce energy consumption or other damping devices to increase damping and energy consumption Capability, its cost and structure size are very large and complex, which is not conducive to promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-friction-coefficient polyamide material and preparing method and application thereof
  • High-friction-coefficient polyamide material and preparing method and application thereof
  • High-friction-coefficient polyamide material and preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Embodiment 1: Preparation of high friction coefficient polyamide material

[0036] Raw materials: see Table 1

[0037] Preparation method: Add PA6 resin, coated inorganic filler, toughening agent, antioxidant and lubricant into a high-speed mixer for stirring

[0038] The mixture obtained above is granulated through a co-rotating intermeshing twin-screw extruder to prepare a polyamide material with a high coefficient of friction.

[0039] The obtained polyamide material with high friction coefficient was injection molded into a flat plate, and the basic mechanical properties were measured by proofing. The static friction coefficient test was carried out according to the ISO8295 standard, as shown in Table 1.

Embodiment 2

[0040] Embodiment 2: Preparation of high friction coefficient polyamide material

[0041] Raw materials: see Table 1

[0042] Preparation method: with embodiment 1

[0043] The obtained polyamide material with high friction coefficient was injection molded into a flat plate, and the basic mechanical properties were measured by proofing. The static friction coefficient test was carried out according to the ISO8295 standard, as shown in Table 1.

Embodiment 3

[0044] Embodiment 3: Preparation of high friction coefficient polyamide material

[0045] Raw materials: see Table 1

[0046] Preparation method: with embodiment 1

[0047] The obtained polyamide material with high friction coefficient was injection molded into a flat plate, and the basic mechanical properties were measured by proofing. The static friction coefficient test was carried out according to the ISO8295 standard, as shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-friction-coefficient polyamide material and a preparing method and application thereof. The high-friction-coefficient polyamide material is prepared from, by weight, 60%-85% of polyamide resin, 5%-15% of a coating inorganic filler, 5%-25% of a toughening agent, 0.1%-0.2% of a silane coupling agent, 0.1%-0.5% of an antioxidant and 0.5%-0.8% of a lubricating agent. Thehigh-friction-coefficient polyamide material has the advantages of being good in abrasive resistance, high in dynamic friction coefficient and excellent in mechanical property.

Description

technical field [0001] The invention relates to the technical field of wear-resistant materials, in particular to a polyamide material with high friction coefficient and its preparation method and application. Background technique [0002] Polyamide (PA) is one of the top five engineering plastics with the largest output, the most varieties and the widest uses. Polyamide has high mechanical strength, high heat distortion temperature, good wear resistance, good oil resistance, good chemical resistance, excellent electrical insulation performance, and good self-extinguishing property. Polyamides are widely used in rail transit, automobile industry, electronic and electrical industry, agricultural machinery parts, aerospace and other fields. [0003] At present, semi-crystalline polyamide PA6 is more and more widely used in rail transit, automobile, electrical and other fields. However, these fields also have high requirements for the friction coefficient of materials. Existin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L51/06C08K9/10C08K3/34C08K3/30
Inventor 王腾刘凯申应军
Owner JINYOUNG XIAMEN ADVANCED MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com