Gradient laminated glass and preparation technology thereof

A technology of laminated glass and glass, applied in glass/slag layered products, adhesives, acrylonitrile butadiene styrene polymer adhesives, etc., can solve the problem of reduced bearing capacity of laminated glass and poor sound wave blocking effect , small shear modulus, etc., to achieve the effect of good UV protection, good sound insulation, and improved bonding tightness

Active Publication Date: 2019-04-19
江苏儒耀装饰设计道具有限公司
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The PVB film and SGP film used to bond two pieces of glass in the existing gradient laminated glass can make the glass fragments still adhere to the intermediate laminated film when the glass is broken, and the broken glass surface remains clean and smooth , to ensure personal safety, and has the advantages of blocking infrared and ultraviolet rays, but the PVB film and SGP film have a poor blocking effect on sound waves, and the sound insulation effect is poor, and the PVB film is relatively soft and has a small shear modulus, which makes laminated glass. Reduced bearing capacity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gradient laminated glass and preparation technology thereof
  • Gradient laminated glass and preparation technology thereof
  • Gradient laminated glass and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1-3

[0043] The maleic anhydride grafted vinyl acetate copolymer is selected from the model EVA-G-MAH type maleic anhydride grafted vinyl acetate copolymer sold by Nanjing Deba Polymer Material Co., Ltd., and the trans polyisoprene rubber is selected from the above The model sold by Haishucan Industrial Co., Ltd. is yc-8742 trans-polyisoprene rubber. The PVB resin is selected from SD-5 PVB resin sold by Qingdao Haocheng Industrial Co., Ltd., and the ABS resin is selected from Suzhou Qiaoshun Plastic Chemical Co., Ltd. The PA-717C ABS resin sold by the company, the borax crosslinking agent is selected from the DS-PS pentahydrate borax of Guangzhou Desheng Chemical Co., Ltd., and the bentonite is selected from the QGF bentonite sold by Lingshou County Jingkun Mineral Products Processing Factory , the silica airgel powder is selected from the silica airgel powder powder of Hongda Technology (Beijing) Co., Ltd. with a particle size of 5-10 μm.

preparation example 1

[0044] Preparation Example 1: (1) According to the ratio in Table 1, stir 0.3kg of trans polyisoprene rubber at 70°C for 10 minutes, add 40kg of PVB resin heated to 60°C into trans polyisoprene rubber In, after mixing evenly, add 1kg of plasticizer, mix evenly, the plasticizer is tributyl citrate;

[0045] (2) Heat 15kg of rosin to 135°C, then mix and grind 10kg of modified diatomite, 5kg of bentonite, 1kg of heat insulating material, 5kg of ultraviolet absorber and 1kg of glass fiber until the particle size is 2μm. The final powder is added to the rosin and mixed evenly;

[0046] Among them, the modified diatomite is prepared by the following method: mix 10kg of diatomite with 40kg of sulfuric acid solution with a mass fraction of 10%, heat to 40°C, stir for 20min, cool and stand still, wash until the pH is 6.8, and then It is dried at 100° C. for 30 min;

[0047] The heat insulation material is a mixture of ferric oxide, indium tin oxide and silica airgel powder with a mas...

preparation example 2

[0051] Preparation Example 2: (1) According to the ratio in Table 1, stir 0.5kg of trans polyisoprene rubber at 75°C for 15 minutes, add 50kg of PVB resin heated to 65°C into trans polyisoprene rubber In, after mixing evenly, add 3kg plasticizer, mix evenly, plasticizer is epoxy soybean oil;

[0052] (2) Heat 18kg of rosin to 145°C, then mix and grind 13kg of modified diatomite, 8kg of bentonite, 3kg of heat insulating material, 8kg of ultraviolet absorber and 3kg of glass fiber until the particle size is 4μm. The final powder is added to the rosin and mixed evenly;

[0053] Among them, the modified diatomite is prepared by the following method: mix 13kg of diatomite with 50kg of sulfuric acid solution with a mass fraction of 15%, heat to 50°C, stir for 25min, cool and stand still, wash until the pH is 7.0, and then It is dried at 103° C. for 40 min;

[0054] The heat insulation material is a mixture of ferric oxide, indium tin oxide and silica airgel powder with a mass rati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a gradient laminated glass and a preparation technology thereof. The gradient laminated glass comprises a glass sheet, a soundproof film and a gradient film, the glass sheet comprises a first glass sheet and a second glass sheet, the soundproof film and the gradient film are located between the first glass sheet and the second glass sheet, and the soundproof film is in contact with the second glass sheet; and the soundproof film comprises PVB resin, trans-polyisoprene rubber, a plasticizer, hollow glass beads, ABS resin, a maleic anhydride-grafted ethylene-vinyl acetatecopolymer, a borax crosslinker, modified diatomite, bentonite, glass fibers, rosin, a heat insulating material and an ultraviolet absorber. The preparation technology of the gradient laminated glasscomprises the following steps: S1, cleaning the glass sheet; S2, sheet combination; S3, hot press molding. The gradient laminated glass of the invention has the advantages of good soundproof effect and high carrying capacity.

Description

technical field [0001] The invention relates to the technical field of glass manufacturing, more specifically, it relates to a gradient laminated glass and its preparation process. Background technique [0002] Gradient laminated glass is made of two pieces of glass, a layer of gradient film and a layer of intermediate laminated film. Gradient laminated glass is also called gradient glass. In many large shopping malls and office areas, gradient glass is used as a partition. To ensure the unimpeded light, the unique artistic effect of gradient glass can bring people a feeling of tranquility and comfort to the greatest extent, which not only makes our office environment more humane, but also regulates our tense body and mind, so as to ensure that our alliance is happy, Work efficiently. [0003] In the prior art, the Chinese utility model patent document with the application number CN201721312005.3 discloses a gradient color laminated glass, which includes an antifouling nano...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B17/10B32B17/06B32B27/30B32B27/22B32B27/18B32B27/06B32B33/00B32B37/06B32B37/10C09J155/02C09J129/14C09J11/04C09J7/10
CPCB32B7/10B32B17/06B32B17/10165B32B17/1055B32B17/10605B32B17/10614B32B17/10678B32B17/10871B32B27/06B32B27/18B32B27/22B32B27/302B32B27/304B32B33/00B32B2307/102B32B2307/304B32B2307/71C08K2003/2272C08L2205/035C09J11/04C09J155/02C09J7/10C08L29/14C08L9/00C08L93/04C08K7/14C08K3/346C08K7/28C08K3/22C08K7/26
Inventor 邓杰强
Owner 江苏儒耀装饰设计道具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap