Antifouling, antistatic and water-based graphene-silicon-modified fluoroacrylic resin paint and preparation method thereof

A technology of fluoroacrylic resin and water-based coatings, which is applied in antifouling/underwater coatings, anticorrosion coatings, conductive coatings, etc. The anti-static effect of pollution is difficult to last and other problems, and achieve the effect of high hardness, high cross-linking density and good anti-static performance

Inactive Publication Date: 2019-04-16
UNION FOSHAN CHEM +1
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The above inventions all use additive coatings, the difference between the additive and the polymer structure is large, and the poor dispersion makes it difficult to form a homogeneous system, thereby affecting the electrical conductivity, antifouling and physical properties of the coating. Its antifouling and antistatic Unsustainable potency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of graphene, silicon-modified fluoroacrylic acid resin A, its preparation process is as follows:

[0032] 1) In a four-port reactor equipped with a thermometer, a condenser, and an agitator, add 2.2 parts of dimethylol propionic acid, 1.8 parts of graphene, 4.2 parts of polytetrahydrofuran ether glycol, hydroxypropyl 3.0 parts of end-blocked polydimethylsiloxane is heated up to 76-80°C, then 9.5 parts of isophorone diisocyanate is slowly added dropwise, stirred for 0.5-1.0 hours, then 0.06 parts of twice distilled water is added and stirred for 0.5-1.0 hours h, add 0.04 parts of dibutyltin dilaurate, heat up to 82-85°C for 2-2.5 hours, add 12.0 parts of methyl methacrylate and 3.0 parts of butyl methacrylate during the reaction to adjust the viscosity, and cool down to 76- At 80°C, add 1.8 parts of hydroxyethyl acrylate, continue the reaction for 1.5 hours, add 0.8 parts of anhydrous methanol to consume the remaining NCO;

[0033] 2) Continue to stir to reduce t...

Embodiment 2

[0036] A kind of graphene, silicon modified fluoroacrylic resin B, its preparation process is as follows:

[0037] 1) In a four-port reactor equipped with a thermometer, a condenser, and an agitator, add 3.5 parts of dimethylol propionic acid, 2.0 parts of graphene, 4.0 parts of polytetrahydrofuran ether glycol, hydroxypropyl Heat up 2.8 parts of blocked polydimethylsiloxane to 76-80°C, then slowly add 10.5 parts of isophorone diisocyanate dropwise, stir for 0.5-1.0 hours, then add 0.07 parts of twice distilled water and stir for 0.5-1.0 hours h, add 0.03 parts of dibutyltin dilaurate, heat up to 82-85°C for 2-2.5 hours, add 14.0 parts of methyl methacrylate and 3.5 parts of stearyl methacrylate during the reaction to adjust the viscosity, and cool down to 76 ~80°C, add 2.1 parts of hydroxyethyl acrylate, continue the reaction for 1.5h, add 0.6 parts of anhydrous methanol to consume the remaining NCO;

[0038] 2) Continue to stir to reduce the temperature of the reactant to b...

Embodiment 3

[0041] A graphene, silicon-modified fluoroacrylic resin antifouling and antistatic water-based coating, by weight percentage, it is composed of: graphene, silicon-modified fluoroacrylic resin A 60.0 parts, dipropylene glycol butyl ether 4.5 parts, titanium dioxide 10.0 parts , 6.0 parts of nano diamond beads, 0.4 parts of leveling agent, 0.6 parts of dispersant, 0.3 parts of defoaming agent, 0.6 part of waterproofing agent, 0.5 part of wetting agent, 3.5 parts of film-forming aid, 13.6 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to antifouling, antistatic and water-based graphene-silicon-modified fluoroacrylic resin paint. The paint is prepared from, by weight, 50.0-70.0 parts of graphene-silicon-modified fluoroacrylic resin, 3.0-6.0 parts of dipropylene glycol butyl ether, 5.0-25.0 parts of pigments and fillers, 4.0-10.0 parts of an auxiliary agent and 10.0-20.0 parts of deionized water, wherein thegraphene-silicon-modified fluoroacrylic resin is prepared by a reaction of a hard acrylate monomer, a soft acrylate monomer, a fluoroolefin monomer, dimethylolpropionic acid, polytetrahydrofuran ether diol, hydroxypropyl-terminated polydimethylsiloxane, secondary distilled water, polyisocyanate, graphene, hydroxyethyl acrylate, anhydrous methanol and a neutralizing agent. The antifouling, antistatic and water-based graphene-silicon-modified fluoroacrylic resin paint prepared by the method has the advantages of high hardness, good antistatic property, high crosslinking density, great corrosionresistance, low surface tension, excellent antifouling capability, superior acid and alkali resistance and the like. The paint can be used as wood paint, metal paint, marine paint and the like.

Description

technical field [0001] The present invention relates to the preparation of a graphene and silicon modified fluoroacrylic resin, in particular to a graphene and silicon modified fluoroacrylic resin antifouling and antistatic water-based coating and its preparation method, which can be used for cement concrete, metal, wood and other various surfaces, which belong to the technical field of synthetic resin and water-based paint. Background technique [0002] Coating is a viscous liquid polymer synthetic material with no fixed shape at room temperature. After coating, it can form a tough coating film on the surface of the base layer through the volatilization of solvent or water evaporation or reaction curing. Coatings can not only play an aesthetic role, but also effectively protect the substrate. However, once the general coating encounters oil stains, it is difficult to clean. Forcible cleaning will damage the film surface, so that the coating needs to be repainted. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D5/08C09D5/24C09D5/16C09D7/61C08F283/00C08F220/14C08F220/22C08F220/18C08F2/44C08G18/34C08G18/48C08G18/61C08G18/67C08G18/75C08G18/66
CPCC09D151/08C08F2/44C08F283/008C08G18/348C08G18/4854C08G18/61C08G18/672C08G18/755C09D5/08C09D5/1668C09D5/1687C09D5/24C08K2201/011C08G18/6692C08G18/0823C08K7/16C08K3/042C08K3/22C08F220/1818C08F220/1804
Inventor 张武康伦国姚东生许钧强阳京辉
Owner UNION FOSHAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com