A high flame retardant grade hips composite material

A composite material, high flame-retardant technology, applied in the field of engineering plastics, to achieve the effect of good comprehensive performance, balanced strength and notched impact performance, and wide processing window

Active Publication Date: 2021-09-07
江苏金发再生资源有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the development of society and people's increasing emphasis on safety, some household appliances and electronic products have put forward higher requirements for flame retardant materials. For example, the shells of electronic controllers such as refrigerators and microwave ovens require 5VA flame retardant, and the thickness also increases with The design trend is becoming thinner and thinner (2.5-2.0mm), and the existing ordinary V-0 flame-retardant HIPS materials can no longer meet this requirement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high flame retardant grade hips composite material
  • A high flame retardant grade hips composite material
  • A high flame retardant grade hips composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5 and comparative example 1～6

[0027] The formulations of the HIPS composite materials of Examples 1-5 and Comparative Examples 1-6 are shown in Table 1.

[0028] The HIPS composite material formula of table 1 embodiment 1~5 and comparative examples 1~6

[0029]

[0030]

[0031] "-" means do not add.

Embodiment 6～9

[0033] The HIPS composite material formulations of Examples 6-9 differ from Example 4 only in the ratio of the toughening agent to the inorganic filler. The HIPS composite material formulations of Examples 6-9 are shown in Table 2.

[0034] The HIPS composite material formula of table 2 embodiment 6~9

[0035] Raw materials (parts by weight) Example 6 Example 7 Example 8 Example 9 PS resin: GPPS-500NT 48 48 48 48 thermoplastic styrene butadiene rubber 20 20 20 20 Toughener CPE 235C 3 3.75 7.5 10 Flame retardant FR-245 12 12 12 12 Flame Retardant Synergist 4 4 4 4 Inorganic filler 12 11.25 7.5 5 anti-dripping agent 0.2 0.2 0.2 0.2 Auxiliary 0.8 0.8 0.8 0.8

Embodiment 10～12

[0037] The only difference between the ABS composite material formulations of Examples 10-12 and Example 4 is the type of toughening agent. The ABS composite material formulations of Examples 10-12 are shown in Table 3.

[0038] The HIPS composite material formula of table 3 embodiment 10~12

[0039]

[0040]

[0041] "-" means do not add.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
diameteraaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high flame-retardant grade HIPS composite material, which comprises the following components in parts by weight: 40-60 parts of PS resin, 10-27 parts of thermoplastic styrene-butadiene rubber, 3-10 parts of toughening agent, and 10 parts of flame retardant ~18 parts, 2.5~6 parts of flame retardant synergist, 5~20 parts of inorganic filler, 0.1~0.5 parts of anti-dripping agent and 0~2 parts of auxiliary agent; the weight average molecular weight of the PS resin is greater than or equal to 15* 10 4 g / mol, the melt flow rate MFR is 3~6g / 10min. The high flame retardant grade HIPS composite material of the present invention: 1. High flame retardant grade, the highest can reach 2.0mm 5VA grade; 2. Good comprehensive performance, balanced strength and notch impact performance; 3. Low cost, can replace high Flame retardant grade ABS; 4. Good appearance and wide processing window.

Description

technical field [0001] The invention relates to the technical field of engineering plastics, in particular to a high flame-retardant grade HIPS composite material. Background technique [0002] Polystyrene (PS) includes ordinary polystyrene, expanded polystyrene (EPS), high-impact polystyrene (HIPS) and syndiotactic polystyrene (SPS). BASF began commercial production in Germany in 1930 polystyrene. As one of the five general-purpose plastics, it has the advantages of excellent formability, hard quality, transparency, rigidity, electrical insulation, low hygroscopicity, easy dyeing and low price. [0003] High-impact polystyrene (HIPS) is produced by adding a small amount of elastomer to PS, which overcomes the brittleness of polystyrene, so it is widely used in internal and external components of household appliances and office automation equipment. Such as monitors, video recorders, copiers, fax machines, printers, air conditioners, refrigerators, etc. Styrenic polymers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L9/06C08L23/28C08L27/18C08L23/08C08K13/02C08K3/22C08K3/34C08K5/3492
CPCC08K2201/003C08K2201/016C08L25/06C08L2201/02C08L2205/025C08L2205/035C08L2205/06C08L9/06C08L23/286C08L27/18C08K13/02C08K3/2279C08K3/34C08K5/3492C08L23/0815
Inventor 王亮叶南飚邹声文秦旺平付锦锋杜荣华刘凯杨霄云
Owner 江苏金发再生资源有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap