Plant-derived polypropylene master batch and preparation method thereof

A plant-sourced polypropylene technology, applied in the manufacture of fire-resistant and flame-retardant filaments, single-component polyolefin artificial filaments, etc., can solve the problems of reduced flame-retardant performance, poor uniformity of polypropylene masterbatch, and large coefficient of variation of breaking strength. , to achieve excellent flame retardant performance and good anti-pilling and fuzzing performance

Inactive Publication Date: 2019-03-22
ZHONGKE TEXTILE RES INST QINGDAO CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (1) The uniformity of plant-source polypropylene masterbatch is poor, easy to connect grains, and the oxygen index is low;
[0009] (2) Fibers prepared from plant-derived masterbatches have poor mechanical properties, high defects, large coefficient of variation of breaking strength, and reduced flame retardancy;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plant-derived polypropylene master batch and preparation method thereof
  • Plant-derived polypropylene master batch and preparation method thereof
  • Plant-derived polypropylene master batch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Example 1 A preparation method of honeysuckle plant source polypropylene masterbatch

[0055] Step 1, preparation of modified honeysuckle powder

[0056] (1) Selection of raw materials

[0057] Honeysuckle powder is selected as the plant source raw material of this embodiment, and 100% of the honeysuckle powder passes through a 10,000 mesh sieve, the appearance powder is loose and has no agglomeration, and the color: has the inherent color of the product, and is uniform; the smell is uniform The content of active ingredients is ≥98%, the content of chlorogenic acid is 16.5%, the moisture content is ≤5%, the total number of colonies is less than 100cfu / g, Salmonella and Escherichia coli cannot be detected, and the shelf life is 18 months.

[0058] (2) Preparation of modified honeysuckle powder

[0059] Mix 50 parts of honeysuckle powder with 15 parts of chitin and 4 parts of starch, adjust the pH to 7.1 with sodium carbonate, add 50 parts of deionized water and heat to...

Embodiment 2

[0082] Embodiment 2 A kind of preparation method of honeysuckle plant source polypropylene fiber masterbatch

[0083] Step 1, preparation of modified honeysuckle powder

[0084] (1) Selection of raw materials

[0085] Honeysuckle powder is selected as the plant source raw material of this embodiment, and 100% of the honeysuckle powder passes through a 10,000 mesh sieve, the appearance powder is loose and has no agglomeration, and the color: has the inherent color of the product, and is uniform; the smell is uniform The content of active ingredients is ≥98%, the content of chlorogenic acid is 16.5%, the moisture content is ≤5%, the total number of colonies is less than 100cfu / g, Salmonella and Escherichia coli cannot be detected, and the shelf life is 18 months.

[0086] (2) Preparation of modified honeysuckle powder

[0087] Mix 50 parts of honeysuckle powder with 16 parts of chitin and 5 parts of starch, adjust the pH to 7.5 with sodium carbonate, add 60 parts of deionized ...

Embodiment 3

[0110] Embodiment 3 A kind of preparation method of honeysuckle plant source polypropylene fiber masterbatch

[0111] Step 1, preparation of modified honeysuckle powder

[0112] (1) Selection of raw materials

[0113] Honeysuckle powder is selected as the plant source raw material of this embodiment, and 100% of the honeysuckle powder passes through a 10,000 mesh sieve, the appearance powder is loose and has no agglomeration, and the color: has the inherent color of the product, and is uniform; the smell is uniform The content of active ingredients is ≥98%, the content of chlorogenic acid is 16.5%, the moisture content is ≤5%, the total number of colonies is less than 100cfu / g, Salmonella and Escherichia coli cannot be detected, and the shelf life is 18 months.

[0114] (2) Preparation of modified honeysuckle powder

[0115] Mix 50 parts of honeysuckle powder with 20 parts of chitin and 6 parts of starch, adjust the pH to 8 with sodium carbonate, add 70 parts of deionized wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
acid valueaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a plant-derived polypropylene master batch. The plant-derived polypropylene master batch is prepared by mixing and melting polypropylene master batch and modified honeysuckle flower powder according to a mass ratio of 85:15. The invention also provides a preparation method of cellulose fiber. The prepared plant-derived polypropylene master batch has the advantages that the shape is regular, the connecting of particles is avoided, the crushed chips are avoided, the uniformity of particle size is 95.8 to 99.1%, and the OI (oxygen index) is 29 to 30. The prepared cellulosefiber has the advantages that the deviation rate of linear density is 0.7 to 1.2%, the deviation rate of length is 0.01 to 0.06%, the break strength is 7.9 to 8.3cN / dtex, the elongation rate at breakis 25.8 to 30.4%, the defect is 2.7 to 2.8mg / 100g, the combustion time of flame-retardant property is 9.4 to 8.5s, and the combustion class is V-1; after washing for multiple times, the flame-retardant effect is lasting and stable.

Description

technical field [0001] The invention relates to a plant-source polypropylene fiber masterbatch and a preparation method thereof, belonging to the field of fiber masterbatch preparation. Background technique [0002] Polypropylene masterbatch refers to the basic pellets for the manufacture of polypropylene fibers, which have certain physical and chemical properties such as shape and particle size. Polypropylene fiber is an important variety of synthetic fibers. It is the trade name of polyester fiber in my country. Polypropylene fiber has the advantages of low density, non-toxicity, corrosion resistance, good mechanical balance, and low price. It is a material with a wide range of applications. However, due to the poor flame retardancy of polypropylene itself, its application in motors, flexible circuit boards, electrical appliances and other fields is limited. [0003] Plants in nature, such as wormwood, Folium Folium, mint, honeysuckle, etc., are widely welcomed by technic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L5/08C08K5/521C08K5/14C08K9/04C08K5/00C08K13/06C08K3/02C08K3/22D01F6/46D01F1/07
CPCC08L23/12C08K2003/026C08L2201/02C08L2203/12D01F1/07D01F6/46C08L5/08C08K5/521C08K5/14C08K9/04C08K5/00C08K13/06C08K3/02C08K3/2279
Inventor 刘洁刘宇黄效龙黄效谦
Owner ZHONGKE TEXTILE RES INST QINGDAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap