Modified meta-aramid, preparation method thereof and hollow fiber membrane

A fiber membrane and aramid fiber technology, which is applied to the modified meta-aramid hollow fiber membrane and the preparation of the hollow fiber membrane, modified meta-aramid fiber and its preparation field, which can solve the problem of high intrinsic viscosity and difficult membrane filaments Dry storage, restricted application and other issues

Active Publication Date: 2019-03-12
OCHEMATE MATERIAL TECH CO LTD
View PDF19 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some aspects of the performance of the existing meta-aramid fiber can no longer meet the needs of the water treatment field. Although the existing meta-aramid fiber has a zigzag orderly arrangement of its main chain, it has a good cost performance. Compared with the mainstream ultrafiltration membrane materials in the market, its cost is lower, but the existing meta-aramid fibers have poor chlorine resistance, high intrinsic viscosity ([η] > 4.5), and membrane filaments are not Disadvantages such as easy dry storage restrict its application in the field of water treatment (membrane field)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Add 54.131 mL of DMAc solvent, 0.077 mol of m-phenylenediamine, 0.0385 mol of APBIA and 0.0385 mol of 4-fluoro-1,3-phenylenediamine into a four-neck flask, stir to dissolve. Adjust the reaction temperature to -25°C, add 0.1155mol of isophthaloyl chloride under stirring, control the reaction temperature of the reaction system to be lower than 0°C, and continue to add 0.0262mol of isophthaloyl chloride until the viscosity of the system is stable. After reacting until the viscosity of the system is stable, add 0.0123mol of isophthaloyl chloride at the end, and control the reaction temperature below 60°C until the reaction is complete. After adding 0.154mol of calcium hydroxide, continue stirring until complete neutralization (pH value = 7). At this time, the content of the modified meta-aramid polymer in the solution was 17.54 wt%. Take out a small part of the solution and dilute it with deionized water to obtain the modified meta-aramid polymer, and continue to wash it th...

Embodiment 2

[0057] Under nitrogen protection, add 80.383mL of DMAc solvent, 0.077mol of m-phenylenediamine, 0.0616mol of APBIA and 0.0154mol of 4-fluoro-1,3-phenylenediamine into a 1L four-necked flask equipped with mechanical stirring and a thermometer. Stir under nitrogen protection until the solute is completely dissolved. Use a freezing bath to adjust the reaction temperature to -15°C, add 0.1155mol of isophthaloyl chloride under stirring, control the reaction temperature of the reaction system below 0°C, and continue to add 0.0262mol of isophthaloyl dimethanol after reacting until the viscosity of the system is stable Acyl chloride, after the reaction until the viscosity of the system is stable, add 0.0123mol of isophthaloyl chloride at the end, the solution starts to thicken, the temperature rises, adjust the stirring speed to control the reaction temperature below 60°C until the reaction is complete, after adding 0.154mol of calcium hydroxide Continue stirring until neutralization ...

Embodiment 3

[0059] Under nitrogen protection, add 57.257mL DMAc solvent, 0.1386mol m-phenylenediamine, 0.0077mol APBIA and 0.0077mol 4-fluoro-1,3-phenylenediamine into a 1L four-necked flask equipped with mechanical stirring and a thermometer. Stir under nitrogen protection until the solute is completely dissolved. Use a freezing bath to adjust the reaction temperature to -25°C, add 0.1309mol of isophthaloyl chloride under stirring, control the reaction temperature of the reaction system below 0°C, and continue to add 0.0107mol of isophthaloyl dimethanol after the reaction reaches a stable viscosity Acyl chloride, after the reaction until the viscosity of the system is stable, add 0.0123mol of isophthaloyl chloride at the end, the solution starts to thicken, the temperature rises, adjust the stirring speed to control the reaction temperature below 60°C until the reaction is complete, after adding 0.154mol of calcium hydroxide Continue stirring until neutralization is complete. At this ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The inside diameter ofaaaaaaaaaa
Outer diameteraaaaaaaaaa
Average pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified meta-aramid polymer and a preparation method thereof. Metaphenylene diamine, 2-(4-aminophenyl)-5-aminobenzimidazole and various diamine monomers such as halogenateddiamine monomers are poly-condensed with isophthalic chloride by a low-temperature solution polycondensation method to form the modified meta-aramid polymer, wherein the isophthalic chloride is repeatedly added into reaction solution. The invention further discloses a preparation method for preparing a hollow fiber membrane by the prepared meta-aramid polymer. The prepared modified meta-aramid polymer keeps original excellent performances, further has low intrinsic viscosity and good chlorine resistance and is more applicable to spinning of the hollow fiber membrane, the prepared membrane is more easily preserved in a dry state, and the preparation method is simple, easy to operate and suitable for industrial production and has an excellent market application prospect.

Description

technical field [0001] The invention relates to the technical field of aramid fibers and membranes, in particular to a modified meta-aramid fiber and a preparation method thereof, a modified meta-aramid hollow fiber membrane and a process for preparing the hollow fiber membrane. Background technique [0002] Meta-aramid is obtained by polycondensation of isophthaloyl chloride and m-phenylenediamine. There are two commonly used preparation methods: the first is the interfacial polycondensation method, which is to dissolve m-phenylenediamine and a small amount of acid absorbent together. Prepare an aqueous phase in water, then dissolve isophthaloyl dichloride in an organic solvent and add it to the stirred aqueous phase, the reaction occurs at the interface between the aqueous phase and the organic phase, and the polymer is separated and dried to obtain a solid product; the second One is the low-temperature solution polycondensation method, which is to dissolve m-phenylenediam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G69/32B01D71/56B01D69/08B01D69/02
CPCB01D69/02B01D69/08B01D71/56B01D2325/30C08G69/32
Inventor 袁新兵李彬雷冰
Owner OCHEMATE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com