Method of preparing aerogels/nonwoven composites fireproof and heat-insulating materials

一种复合材料、气凝胶的技术,应用在气凝胶制备、非织造布、装饰用纺织品等方向,能够解决易破碎、气凝胶龟裂、影响气凝胶工业应用等问题,达到改善结合能力弱的效果

Active Publication Date: 2019-03-01
KUN SHAN UNIVERSITY
View PDF15 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this preparation method cannot be industrialized, and the airgel prepared by it will obviously have cracks and be easily broken, which will affect the overall industrial application of airgel, so there is still considerable room for improvement in the preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of preparing aerogels/nonwoven composites fireproof and heat-insulating materials
  • Method of preparing aerogels/nonwoven composites fireproof and heat-insulating materials
  • Method of preparing aerogels/nonwoven composites fireproof and heat-insulating materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0066] The present invention will be further described below in conjunction with specific embodiments and accompanying drawings, and the advantages and characteristics of the present invention will become clearer along with the description. However, these embodiments are only exemplary and do not constitute any limitation to the scope of the present invention. Those skilled in the art should understand that the details and forms of the technical solutions of the present invention can be modified or replaced without departing from the spirit and scope of the present invention, but these modifications and replacements all fall within the protection scope of the present invention.

[0067] First, see figure 1 as shown, figure 1 It is a flow chart of the preparation method of the airgel / non-woven composite material of the present invention. The invention provides a method for preparing hydrophilic and hydrophobic airgel / non-fabric composite materials respectively, comprising the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method of preparing aerogels / nonwoven composites fireproof and heat-insulating materials with a hydrophobic or hydrophilic surfaces and includes steps as follows. A mixture solution in which alkoxysilane, silicones and silane coupling agents are mixed and stirred is instilled by acidic catalysts for a hydrolysis reaction during which a silane coupling agent solution is added for continuous stirring; a hydrous alkali catalytic (anhydrous alkali catalytic) organic solution is added in the mixture solution for a condensation reaction and development of a 'silicones-silica aerogels-silane coupling agents' aerogel mixture solution; a non-woven felt is impregnated with the mixture solution for development of soft hydrophobic (hydrophilic) aerogels / nonwoven composites fireproof and heat-insulating materials after curing and natural drying. The aerogels / nonwoven composites materials with softness and surface hydrophobicity / hydrophilicity available in mass production are applicable to thermal-insulating materials for high-temp industrial facilities or indoor heat-insulating and fireproof panels of a building structure.

Description

technical field [0001] The invention relates to a preparation method and product of an airgel / non-fabric composite fire-proof and heat-insulating material with different surface hydrophilic and hydrophobic properties and flexibility, and particularly relates to a combination of silicon alkoxide compounds, silica gel compounds and The silica gel-silicon aerogel-silane coupling agent three-mix airgel sol solution system of silane coupling agent compound; soak a non-fabric in this three-mix airgel sol solution, so that the aforementioned airgel sol solution is evenly interspersed in the In this non-woven fabric, go through a drying process again to obtain an airgel / non-woven composite material that can have different hydrophilic and hydrophobic surface properties and has softness. This material can be applied to heat insulation materials for high-temperature equipment or building structures. Indoor insulation and fireproof board materials. Background technique [0002] Press, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/79D06M15/643D06M13/50D06M101/20D06M101/32D06M101/34D06M101/40
CPCD06M11/79D06M13/50D06M15/643D06M2101/20D06M2101/32D06M2101/34D06M2101/40B01J13/0091C08G77/18C08J9/28C08J9/40C08J2201/0502C08J2205/026C08J2383/04C08K5/5415C08K5/5425C09D183/06D04H1/587D04H1/64D06M13/507D06M13/513D06M2200/30D06M2400/02Y02B80/10Y02A30/24C08L83/06B05D1/02C08G77/38C08J9/228C08G2110/0091D04H13/00D06M23/00D10B2401/04D10B2403/0242
Inventor 陈建宏陈秀秀张智舜李劲直
Owner KUN SHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products