Super thin no-halogen less-smoke fire proof organic-inorganic composite paint and its prepn process

A fire-resistant coating and inorganic composite technology, applied in fire-resistant coatings, polyester coatings, epoxy resin coatings, etc., can solve problems such as suffocation, failure to achieve the flame-retardant effect of halogen flame retardants, etc.

Inactive Publication Date: 2007-06-06
FUDAN UNIV
View PDF8 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the formula design of fire retardant coatings, flame retardants containing halogens are often added. This type of fire retardant coating has a relatively good flame retardant effect, but it will release a lot of smoke and hydrogen halide gas during the combustion process, which is easy to suffocate people. , a large number of fire analyzes have shown that the proportion of fatalities caused by toxic smoke is much higher than that caused by high-temperature burning
However, the flame retardant effect of the halogen flame retardant substitute products used in the current fireproof coatings, such as phosphorus flame retardants and nitrogen flame retardants, is not as good as that of halogen flame retardants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super thin no-halogen less-smoke fire proof organic-inorganic composite paint and its prepn process
  • Super thin no-halogen less-smoke fire proof organic-inorganic composite paint and its prepn process
  • Super thin no-halogen less-smoke fire proof organic-inorganic composite paint and its prepn process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0098] Organic-inorganic nano-hybrid resin formula 1

[0099] Composition Amount (g)

[0100] phosphoric acid 1

[0101] Citric acid 3

[0102] 3-Glycidyl ether methoxytrimethoxysilane 18

[0103] Propyltrimethoxysilane 37

[0104]Ethanol 10

[0105] Isopropanol 8

[0106] water 20

[0107] Ethyl silicate 3

[0108] In a reactor equipped with a stirrer, a thermometer, a condenser, and a dropping funnel, add 18 grams of 3-glycidyl ether methoxytrimethoxysilane, 37 grams of propyltrimethoxysilane, and 3 grams of ethyl silicate. Esters, 10 grams of ethanol, controlled temperature 20-40 ° C, 1000rpm stirring for 10 minutes, 8 grams of isopropanol, 22 grams of water, 1 gram of phosphoric acid, 3 grams of citric acid, mixed evenly and placed in the dropping funnel, at 200 At -400rpm, add dropwise at 20-40°C in 1-2 hours, and continue stirring at 50-70°C for 20 hours to obtain.

Embodiment 2

[0110] Organic-inorganic nano-hybrid resin formula 2

[0111] Composition Amount (g)

[0112] Oxalic acid 2

[0113] Phenylepoxydiethoxysilane 20

[0114] n-Hexadecyltriethoxysilane 34

[0115] Butyl acetate 40

[0116] water 3

[0117] Diisopropyl di(acetylacetonate)titanate 0.5

[0118] Aluminum acetylacetonate 0.5

[0119] The preparation method is the same as in Example 1.

Embodiment 3

[0121] Organic-inorganic nano-hybrid resin formula 3

[0122] Composition Amount (g)

[0123] Acetic acid 0.5

[0124] Phytic acid 7

[0125] Silmethoxy-terminated polydimethylsiloxane 18

[0126] γ-Piperazinylpropylmethyldimethoxysilane 15

[0127] Methyltrimethoxysilane 10

[0128] Methyl amyl ketone 19

[0129] Acetone 20

[0130] water 5

[0131] Propyl silicate 3.5

[0132] n-propoxyzirconate 2

[0133] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to one kind of super thin no-halogen less-smoke fireproof organic-inorganic composite paint and its preparation process. The composite paint is compounded with heat resistant organic and inorganic nanometer hybridized resin, organic resin, heat resistant pigment, heat resistant filler, carbon forming agent, foaming agent, catalyst, assistant, etc. In case of fire, the components of the paint synergy to swell, foam, isolate oxygen, delay heat transfer and inhibit fire spread. The fireproof paint may be used to form coating of controllable thickness in 0.2-2 mm, has fire resisting limit of 30-200 min, excellent heat resisting performance, excellent fire retarding performance, high fireproof performance, high anticorrosion performance and other advantages.

Description

technical field [0001] The invention relates to the fields of chemical industry, fire protection and anticorrosion, and relates to a halogen-free, low-smoke, ultra-thin organic-inorganic composite fireproof coating and a preparation method thereof. Background technique [0002] There are many types of fire-resistant coatings for steel structures, which can be divided into water-based, solvent-based and powder-based according to their material forms; organic-type, inorganic-type and organic-inorganic-type according to the type of resin; according to the fire prevention mechanism, they can be Divided into heat insulation type, expansion type and non-expansion type, according to the thickness of the coating, it is divided into thick type, thin type and ultra-thin type. The ultra-thin steel structure fireproof coating is mainly composed of base resin, char-forming agent, foaming agent, catalyst, etc. Isolate oxygen and have good heat insulation performance, which can delay the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D163/00C09D161/24C09D183/04C09D167/00C09D5/18
Inventor 武利民游波彭勃邢文涛马晓华杨海华
Owner FUDAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com