Compound environment-friendly paint suitable for high-chromium white cast iron and preparation method thereof

A technology of high-chromium white cast iron and environmentally friendly coatings, which is applied to casting molding equipment, casting molds, and casting mold components. It can solve the problems of high production costs and low prices, and achieve low cost, good effect, and high refractoriness. Effect

Active Publication Date: 2019-01-11
XIANGYANG WU ER WU PUMP IND
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problem that the production cost is too high due to the use of alcohol-based zircon powder coating when casting high-chromium white alloy slurry pumps in the traditional process, and to provide a high refractoriness, good sand-sticking resistance, and sintering peeling. Alcohol-based composite environmentally friendly refractory coating with good performance, low price and excellent comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound environment-friendly paint suitable for high-chromium white cast iron and preparation method thereof
  • Compound environment-friendly paint suitable for high-chromium white cast iron and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Start the reaction kettle with the high-speed disperser, drop into 200kg of ethanol first under stirring; then drop into 100kg of zircon powder (the components are: 70kg of ZrO 2 , 30 kg SiO 2 , the particle size is 325 mesh), 200 kg of aluminum silicate powder (the components are: 165 kg of AL 2 o 3 , 35 kg SiO 2 , the particle size is 200 mesh), 360 kg of high-purity alumina powder (the component is: 359 kg of AL 2 o 3 , 1 kg of SiO 2 , particle size is 270 orders), 50 kilograms of sepiolite powder, 18 kilograms of first-grade wood rosin, 35 kilograms of white carbon black, 1 kilogram of cationic surfactant, open high-speed disperser and stir for half an hour; Add 50 kilograms of ethanol at last, After the Baume degree is adjusted to be greater than 90Be, the coating preparation is completed.

Embodiment 2

[0031] Start the reaction kettle with the high-speed disperser, and drop into 190kg of ethanol under stirring; then drop into 135kg of zircon powder (the components are: 90kg of ZrO 2 , 45 kg SiO 2 , the particle size is 325 mesh), 170 kg of aluminum silicate powder (the components are: 140 kg of AL 2 o 3 , 60 kg SiO 2 , particle size is 200 mesh), 375 kg of high-purity alumina powder (component: 373.5 kg AL 2 o 3 , 1.5 kg SiO2 2 , particle size is 270 orders), 45 kilograms of sepiolite powder, 18 kilograms of first-grade wood rosin, 35 kilograms of white carbon black, 1 kilogram of cationic surfactant, open high-speed disperser and stir for half an hour; Add 50 kilograms of ethanol at last, After the Baume degree is adjusted to be greater than 90Be, the coating preparation is completed.

Embodiment 3

[0033] Start the reaction kettle with the high-speed disperser, drop into 200kg of ethanol first under stirring; 2 , 40 kg SiO 2 , the particle size is 325 mesh), 180 kg of aluminum silicate powder (the components are: 145 kg of AL 2 o 3 , 35 kg SiO 2 , the particle size is 200 mesh), 370 kg of high-purity alumina powder (the component is: 369 kg of AL 2 o 3 , 1 kg of SiO 2 , particle size is 270 orders), 42 kilograms of sepiolite powder, 19 kilograms of first-grade wood rosin, 38 kilograms of white carbon black, 1 kilogram of cationic surfactant, open high-speed disperser and stir for half an hour; Add 50 kilograms of ethanol at last, After the Baume degree is adjusted to be greater than 90Be, the coating preparation is completed.

[0034] The coating that each embodiment obtains is tested, obtains data as following table.

[0035]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invdention relates to a compound environment-friendly paint suitable for high-chromium white cast iron and a preparation method thereof and belongs to the field of casting. The paint comprises, bymass, 10-20% of zircon powder, 10-25% of aluminum silicate powder, 25-35% of high-purity aluminum oxide, 3-8% of a suspending agent, 2-6% of a binder, 4-10% of a modifying agent, 0.1-0.5% of a surface active agent and 20-30% of solvent. The preparation method of the paint comprises the steps that burdening is carried out according to the above mixing ratio, 80% of the total mass of the solvent isadded to a reaction kettle firstly under the condition of stirring; then the rest of components, except for the solvent, are all added, and the new mixture is stirred for over half an hour by a high-speed dispersion machine; and finally, the baume degree of the rest of the solvent is adjusted till being greater than 90 Be, and accordingly the paint is obtained. The paint has high refractoriness and coating strength, and the casting cost of paint production is effectively reduced.

Description

technical field [0001] The invention relates to a compound environment-friendly coating suitable for high-chromium white cast iron and a preparation method thereof, belonging to the field of casting. Background technique [0002] High chromium white alloy slurry pump series products, because of Cr ≥ 30%, poor thermal conductivity, casting temperature, long residence time in high temperature zone after casting, have high requirements for refractory casting refractory coatings, such as refractoriness and stripping. Alcohol-based zircon powder coatings are currently used, and the content of zircon powder is relatively high, but the resources of zircon powder are scarce, the price is too high, and the production cost of castings increases due to dependence on imports. Contents of the invention [0003] The purpose of the present invention is to solve the problem that the production cost is too high due to the use of alcohol-based zircon powder coating when casting high-chromiu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
CPCB22C3/00
Inventor 邓家祥李鹏飞刘云易智华
Owner XIANGYANG WU ER WU PUMP IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com