High-strength bearing processing frosting wheel

A bearing processing and grinding wheel technology, applied in the grinding wheel field, can solve the problems of the grinding wheel waste and other problems, and achieve the effects of high machining accuracy, improving work efficiency and prolonging life.

Inactive Publication Date: 2019-01-08
扬中市飞宇磨具有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is generally composed of abrasives, binders and pores. These three parts are often called the three elements of bonded abrasives. Grinding wheels are the most widely used abrasive tools. They rotate at high speeds and can be used on metals or the outer circle, inner circle, plane and various profiles of non-metallic workpieces, etc., for rough grinding, semi-finishing and fine grinding, as well as slotting and cutting; the grinding wheel in the prior art can be used for long-term grinding. The waste is serious and the replacement frequency is high. In order to prolong the service time and service life of the grinding wheel, reduce the scrap rate and production cost, the invention proposes a high-strength bearing processing grinding wheel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment provides a high-strength bearing processing grinding wheel, including a grinding wheel substrate and an abrasive layer, the abrasive layer includes a bond and a mixed abrasive; the bond is a vitrified bond; the mixed abrasive layer includes the following components in parts by mass Parts: graphite: 12 parts, diamond: 22 parts, pigments and fillers: 30 parts, silicon dioxide: 10 parts, black silicon carbide: 14 parts, auxiliary abrasive: 8 parts;

[0026] Wherein, the pigment and filler are a mixture of titanium dioxide and zinc chloride, wherein the mass ratio of titanium dioxide and zinc chloride is 2:1; the auxiliary abrasive is white corundum;

[0027] The grinding wheel substrate is made of high-strength alloy, and its weight percentage composition is: Zr: 1.23%, Re: 0.02%, Bi: 0.58%, Cs: 0.05%, Pb: 0.78%, Al: 0.02%, Ru: 2.45%, Zn: 1.19%, rare earth: 20%, the balance is Fe and trace impurities;

[0028] Among the rare earths, the following component...

Embodiment 2

[0031] This embodiment provides a high-strength bearing processing grinding wheel, including a grinding wheel substrate and an abrasive layer, the abrasive layer includes a bonding agent and a mixed abrasive; the bonding agent is a vitrified bond; the mixed abrasive layer includes the following components in parts by mass: Graphite: 16 parts, diamond: 26 parts, pigments and fillers: 33 parts, silicon dioxide: 14 parts, black silicon carbide: 18 parts, auxiliary abrasive: 14 parts;

[0032] Wherein, the pigment and filler are a mixture of titanium dioxide and zinc chloride, wherein the mass ratio of titanium dioxide and zinc chloride is 2:1; the auxiliary abrasive is white corundum;

[0033] The grinding wheel substrate is made of high-strength alloy, and its weight percentage composition is: Zr: 1.78%, Re: 0.09%, Bi: 1.14%, Cs: 0.13%, Pb: 1.45%, Al: 0.06%, Ru: 3.15%, Zn: 1.25%, rare earth: 28%, the balance is Fe and trace impurities;

[0034] Among the rare earths, the follow...

Embodiment 3

[0037] This embodiment provides a high-strength bearing processing grinding wheel, including a grinding wheel substrate and an abrasive layer, the abrasive layer includes a bonding agent and a mixed abrasive; the bonding agent is a vitrified bond; the mixed abrasive layer includes the following components in parts by mass: Graphite: 14 parts, diamond: 23 parts, pigments and fillers: 31 parts, silicon dioxide: 12 parts, black silicon carbide: 16 parts, auxiliary abrasive: 12 parts;

[0038] Among them, the pigment and filler are a mixture of titanium dioxide and zinc chloride, wherein the mass ratio of titanium dioxide and zinc chloride is 2:1; the auxiliary abrasive is white corundum;

[0039] The grinding wheel substrate is made of high-strength alloy, and its weight percentage composition is: Zr: 1.56%, Re: 0.05%, Bi: 1.07%, Cs: 0.09%, Pb: 1.12%, Al: 0.04%, Ru: 3.08%, Zn: 1.21%, rare earth: 25%, the balance is Fe and trace impurities;

[0040]Among the rare earths, the foll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength bearing processing frosting wheel comprising a frosting wheel base body and an abrasive layer. The abrasive layer comprises a bonding agent and a mixed abrasive; the bonding agent is a ceramic bonding agent; a mixed abrasive layer comprises the following components including, by mass, 12-16 parts of graphite, 22-26 parts of diamond, 30-33 parts of pigment filler, 10-14 parts of silicon dioxide, 14-18 parts of black silicon carbide and 8-14 parts of an auxiliary abrasive; the pigment filler is a mixture of titanium dioxide and zinc chloride, the mass ratio of the titanium dioxide to the zinc chloride is 2:1; the auxiliary abrasive is white corundum; and the frosting wheel base body is made of a high-strength alloy material and comprises components including, by weight, 1.23%-1.78% of Zr, 0.02%-0.09% of Re, 0.58%-1.14% of Bi, 0.05%-0.13% of Cs, 0.78%-1.45% of Pb, 0.02%-0.06% of Al, 2.45%- 3.15% of Ru, 1.19%-1.25% of Zn, 20%- 28% of rare earth and the balance Fe and trace impurities.

Description

technical field [0001] The invention relates to the technical field of grinding wheels, in particular to a high-strength bearing processing grinding wheel. Background technique [0002] Grinding wheel, also known as bonded abrasive, is a bonded abrasive that consolidates ordinary abrasives into a certain shape (mostly round, with a through hole in the center) with a certain strength. It is generally composed of abrasives, binders and pores. These three parts are often called the three elements of bonded abrasives. Grinding wheels are the most widely used abrasive tools. They rotate at high speeds and can be used on metals or the outer circle, inner circle, plane and various profiles of non-metallic workpieces, etc., for rough grinding, semi-finishing and fine grinding, as well as slotting and cutting; the grinding wheel in the prior art can be used for long-term grinding. The waste is serious and the replacement frequency is high. In order to prolong the service time and se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24D3/00B24D3/14B24D3/34
CPCB24D3/00B24D3/001B24D3/14B24D3/346
Inventor 孙留保
Owner 扬中市飞宇磨具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com