Stain and fade resistant wallpaper

A technology of anti-fading and wallpaper, which is applied in the direction of special paper, anti-aging agent added to paper, paper, etc. It can solve the problems of affecting the quality of decoration, fading, and non-dirty wallpaper, and achieves improved corrosion resistance, antibacterial properties, and sound insulation. good sex effect

Inactive Publication Date: 2018-12-18
BENGBU WEIGUANG PLASTIC PRODS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current research on wallpapers is mainly focused on the decorative effects of wallpapers, such as the patterns and colors of wallpapers, without too much consideration for improving the performance of wallpapers. Nowadays, many wallpapers are not resistant to dirt, and they will fade after long-term use, seriously affecting the entire environment. Quality of decoration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A preparation method for stain-resistant and anti-fading wallpaper, which is made of the following substances in parts by weight:

[0023] 92 parts of pulp, 20 parts of modified glass fiber, 8 parts of modified nano zinc oxide, 3 parts of rosin, 2 parts of amber, 4 parts of wood fiber, 6 parts of bleaching powder, 3 parts of linoleic acid, 2 parts of sheep oil, 4 parts of corn oil Parts, 5 parts of tributyl phosphate.

[0024] Further, the preparation method of the modified glass fiber comprises the following steps:

[0025] (1) Soak the glass fibers in a hydrochloric acid solution with a molar concentration of 2mol / L for 14 minutes. After completion, take out the glass fibers and rinse them with deionized water for later use;

[0026] (2) Place the glass fibers soaked in step (1) and modified liquid A together in ultra-high pressure equipment, and use high hydrostatic pressure for treatment. The pressure in the ultra-high pressure equipment is controlled at 500 MPa, a...

Embodiment 2

[0034] A preparation method for stain-resistant and anti-fading wallpaper, which is made of the following substances in parts by weight:

[0035] 94 parts of pulp, 22 parts of modified glass fiber, 10 parts of modified nano zinc oxide, 4 parts of rosin, 3 parts of amber, 6 parts of wood fiber, 8 parts of bleaching powder, 4 parts of linoleic acid, 3 parts of sheep oil, 5 parts of corn oil Parts, 5.5 parts of tributyl phosphate.

[0036] Further, the preparation method of the modified glass fiber comprises the following steps:

[0037] (1) Soak the glass fibers in a hydrochloric acid solution with a molar concentration of 3mol / L for 16 minutes. After completion, take out the glass fibers and rinse them with deionized water for later use;

[0038] (2) Place the glass fibers soaked in step (1) and modified liquid A together in ultra-high pressure equipment, and use high hydrostatic pressure for treatment. The pressure in the ultra-high pressure equipment is controlled at 550MPa,...

Embodiment 3

[0046] A preparation method for stain-resistant and anti-fading wallpaper, which is made of the following substances in parts by weight:

[0047]96 parts of pulp, 24 parts of modified glass fiber, 12 parts of modified nano zinc oxide, 5 parts of rosin, 4 parts of amber, 8 parts of wood fiber, 10 parts of bleaching powder, 5 parts of linoleic acid, 4 parts of sheep oil, 6 parts of corn oil Parts, 6 parts of tributyl phosphate.

[0048] Further, the preparation method of the modified glass fiber comprises the following steps:

[0049] (1) Soak the glass fiber in a hydrochloric acid solution with a molar concentration of 4mol / L for 18 minutes. After completion, take out the glass fiber and rinse it with deionized water for later use;

[0050] (2) Place the glass fibers soaked in step (1) and modified liquid A together in ultra-high pressure equipment, and use high hydrostatic pressure for treatment. The pressure in the ultra-high pressure equipment is controlled at 600MPa, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stain and fade resistant wallpaper. The wallpaper is produced from paper pulp, modified glass fibers, modified nanometer zinc oxide, rosin, amber, wood fibers, bleaching powder, linoleic acid, lanolin, corn oil and tributyl phosphate. Various raw material components are reasonably matched, so the finally obtained wallpaper has the advantages of effectively improved quality, improved flexibility, enhanced resistance to stain, aging and fading, prolonged service and great promotion and use values.

Description

technical field [0001] The invention belongs to the technical field of wallpaper, in particular to a stain-resistant and fade-resistant wallpaper. Background technique [0002] Wallpaper, also known as wallpaper, is an interior decoration material used to paste walls, and is widely used in interior decoration of houses, offices, hotels, hotels, etc. The material is not limited to paper, but also includes other materials. Because of its incomparable characteristics such as various colors, rich patterns, luxurious style, safety and environmental protection, convenient construction, and reasonable price, it has been popularized in developed countries and regions such as Europe, America, and Japan. The current research on wallpapers is mainly focused on the decorative effects of wallpapers, such as the patterns and colors of wallpapers, without too much consideration for improving the performance of wallpapers. Nowadays, many wallpapers are not resistant to dirt, and they will ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/20D21H21/38D21H21/36D21H21/16D21H21/14D21H17/67D21H17/62D21H17/10D21H17/04D21H13/40
CPCD21H13/40D21H17/04D21H17/10D21H17/62D21H17/675D21H21/143D21H21/16D21H21/36D21H21/38D21H27/20
Inventor 李维光杨永志
Owner BENGBU WEIGUANG PLASTIC PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com