Preparation method of antibacterial polypropylene fiber non-woven fabric for wiping paper

A polypropylene non-woven fabric, wiping paper technology, applied in textiles and papermaking, biochemical fiber treatment, fiber type, etc., can solve the problems of high crystallinity, no antibacterial properties, poor hydrophilicity and antibacterial properties, etc.

Inactive Publication Date: 2018-12-18
HEFEI JIENUO MEDICAL PROD CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the macromolecular structure of polypropylene does not contain hydrophilic groups, and its crystallinity is very high. It has no antibacterial properties, resulting in poor hydrophilicity and antibacterial properties of polypropylene non-woven fabrics. Sex and antibacterial properties are not very good defects, which limit its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of preparation method of antibacterial polypropylene fiber nonwoven fabric for wiping paper proposed by the present invention comprises the following steps:

[0023] S1. Add graphene oxide to dimethylacetamide after freeze-drying, add mercaptosuccinic acid and anhydrous triethylamine after ultrasonic dispersion, stir and react at 45°C for 5 hours, and obtain material A by dialysis, washing and drying; Add material A into dimethylacetamide, add curcumin and p-toluenesulfonic acid after ultrasonic dispersion, stir and react at 65°C for 4 hours, and obtain modified graphene oxide through dialysis, cleaning and drying;

[0024] S2. Mix sodium dodecylbenzenesulfonate, sodium lauryl sulfate, sodium phosphate, modified graphene oxide, carbon nanotubes, nano silver, and aloe extract with water to obtain an impregnating solution; The cloth is soaked in the impregnating solution for 100 minutes, and the impregnated non-woven fabric is obtained after drying;

[0025] S3. A...

Embodiment 2

[0029] A kind of preparation method of antibacterial polypropylene fiber nonwoven fabric for wiping paper proposed by the present invention comprises the following steps:

[0030] S1. Add graphene oxide to dimethylacetamide after freeze-drying, add mercaptosuccinic acid and anhydrous triethylamine after ultrasonic dispersion, stir and react at 35°C for 15 hours, and obtain material A through dialysis, washing and drying; Add material A into dimethylacetamide, add curcumin and p-toluenesulfonic acid after ultrasonic dispersion, stir and react at 55°C for 10 hours, and obtain modified graphene oxide through dialysis, cleaning and drying;

[0031] S2. Mix sodium dodecylbenzenesulfonate, sodium lauryl sulfate, sodium phosphate, modified graphene oxide, carbon nanotubes, nano silver, and aloe extract with water to obtain an impregnating solution; Add the cloth into the impregnating solution and impregnate for 60 minutes, and obtain the impregnated non-woven fabric after drying;

...

Embodiment 3

[0036] A kind of preparation method of antibacterial polypropylene fiber nonwoven fabric for wiping paper proposed by the present invention comprises the following steps:

[0037] S1. Add graphene oxide to dimethylacetamide after freeze-drying, add mercaptosuccinic acid and anhydrous triethylamine after ultrasonic dispersion, stir and react at 43°C for 7 hours, and obtain material A through dialysis, washing and drying; Add material A into dimethylacetamide, add curcumin and p-toluenesulfonic acid after ultrasonic dispersion, stir and react at 63°C for 5 hours, and obtain modified graphene oxide through dialysis, cleaning and drying;

[0038] S2. Mix sodium dodecylbenzenesulfonate, sodium lauryl sulfate, sodium phosphate, modified graphene oxide, carbon nanotubes, nano silver, and aloe extract with water to obtain an impregnating solution; Add the cloth into the impregnating solution and impregnate for 85 minutes, and obtain the impregnated non-woven fabric after drying;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an antibacterial polypropylene fiber non-woven fabric for a wiping paper. The preparation method comprises: dispersing graphene oxide in dimethylacetamide, adding mercapto-succinic acid and anhydrous triethylamine into the solution for a reaction, carrying out aftertreatment to obtain a material A, dispersing the material A in dimethylacetamide, adding curcumin and p-toluenesulfonic acid into the solution for a reaction, carrying out aftertreatment to obtain modified graphene oxide, uniformly mixing sodium dodecylbenzenesulfonate, sodium lauryl sulfate, sodium phosphate, modified graphene oxide, carbon nanotubes, nano-silver, aloe extract and water to obtain an immersion liquid, immersing a polypropylene fiber non-woven fabric in the immersion liquid, carrying out drying to obtain the immersed non-woven fabric, adding 5, 5-dimethyl hydantoin into the aqueous sodium hydroxide solution, adding methanol and allyl bromide into the solution for a reaction to obtain a hydantoin derivative, uniformly mixing acrylic resin, hydroxyethyl acrylate, octadecyl acrylate, hydantoin derivative, a light initiator and ethyl acetate, immersing the immersed non-woven fabric into the mixed solution, and carrying out drying, curing, chlorination, washing and drying.

Description

technical field [0001] The invention relates to the technical field of nonwoven fabrics, in particular to a method for preparing antibacterial polypropylene nonwoven fabrics for wiping paper. Background technique [0002] Non-woven fabric is a kind of non-woven fabric, which is formed by directly using polymer chips, short fibers or filaments to form fibers through airflow or mechanically, and then strengthened by hydroentanglement, needle punching or hot rolling, and finally finished. The non-woven fabric is a new type of fiber product with soft, breathable and planar structure. The materials of non-woven fabrics are polyester, polypropylene, nylon, spandex, and acrylic. Polypropylene non-woven fabrics are easy to handle, have good mechanical properties, good chemical stability, non-toxic, good air permeability, strong tensile strength, bending resistance, and wear resistance. And the advantages such as lower price, have been widely used at present. However, the macromole...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M14/28D06M11/74D06M11/83D06M11/71D06M13/00D06M101/20
CPCD06M11/71D06M11/74D06M11/83D06M13/00D06M14/28D06M16/00D06M2101/20
Inventor 张德满
Owner HEFEI JIENUO MEDICAL PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com